fire retardant paint 中文意思是什麼
fire retardant paint
解釋
防火塗料-
The results showed that : there were five stages in the rising process of the internal temperature of untreated, fire - retardant solution soaked, and fire - proof paint coated wood during the fire ; the carbonization rate of wood decreased by 21. 1 % ~ 35. 6 % and the rising speed of internal temperature also declined greatly when wood was soaked in fire - retardant solution or coated with fireproof paint ; the carbonization rate of white pine was 8. 5 % ~ 17. 4 % higher than that of the northeast china ash ; for untreated wood, the carbonization rate in tangential direction was 5. 8 % ~ 10. 5 % higher than that in radial direction ; the internal temperature of wood varies with the developing direction of combustion
結果表明：火災發生過程中未處理木材、阻燃浸漬處理和塗刷防火徐料木材內部溫度上升過程出現5個階段；經過阻燃浸漬處理和塗刷防火塗料后，木材的燃燒炭化速度降低了21 . 1 % ~ 35 . 6 % ，內部溫度上升速度大幅度下降；白皮松木材的燃燒炭化速度比水曲柳木材的燃燒炭化速度快8 . 5 % ~ 17 . 4 % ；未處理木材沿弦向的燃燒炭化速度比徑向快5 . 8 % ~ 10 . 5 % ；木材內部的溫度變化沿燃燒推進方向不同而不同。 -
In order to make clear the regulation of the combustion and the heat - transport process of fire - retardant treated wood, the combustion of untreated, fire - retardant solution soaked, and fire - proof paint coated white pine ( pinus bungeana ) and northeast china ash ( fraxinus mandshurica ) wood as well as the rising process of temperature at different sites in wood were measured in this study, taking a multi - function fire - proof experiment oven to simulate the typical process of fire
摘要為了弄清楚阻燃處理木材的燃燒及其熱傳導規律，該研究採用多功能耐火實驗爐模擬典型火災的發生過程，測定了未處理、阻燃劑水溶液浸漬處理、塗刷防火塗料白皮松和水曲柳木材的燃燒及木材內不同位置的升溫過程。 -
Surface treatment of cold galvanizing, hot dip galvanized, plastic spraying, fire coatings, paint, and also produces aluminum alloy, stainless steel, glass steel, fire - retardant products such as cable tray
產品表面處理有冷鍍鋅、熱鍍鋅、噴塑、防火塗料、烤漆等，並且還生產鋁合金、不銹鋼、玻璃鋼、阻燃等電纜橋架產品。 -
A water - based fire retardant paint, after suitable surface preparation, this paint can be used on steel, aluminum, foam, wood and plastic materials as well as previously painted surfaces
這是水基性防水漆油，在適當的表面準備工序后，可塗上這漆油在鋼鐵、鋁料、泡沫膠、木材和塑膠原料上，甚至塗在油漆的表面上，用作防火之用。 -
Application as widely used all over the world, it is a good substitute for asbestos in construction industry, an ideal filling material for paint, dope, rubber and plastic, and its application goes as far as to manyother fields like electric welding, fire retardant, electronic products, oil well drilling and nacre dye
經加工成雲母粉還有較好地滑動性和較強的附著力。由於雲母和雲母粉本身的性能，主要有如下用途：日用化工原料雲母陶瓷原料油漆添料塑料和橡膠添料建築材料用於焊條藥皮的保護層用於鉆井泥漿填加劑等。 -
Finishing fire retardant paint
飾面型防火塗料 -
Our production of magnesium hydroxide modified surface treatment products, high purity, particle size uniform dispersion of good, strong affinity, are halogen - free, smoke - free, no drops, non - toxic, the safety of flame retardants, rubber, plastics, rubber, engineering, electrical appliances, wires, cable, cable sheathing, thermoplastic materials, insulators, surge arresters, synthetic textiles, fire retardant paint, ink, paper, conveyors, mine ventilation duct, electronic appliances equipment, tarpaulins, tents, military, aerospace, shipbuilding, automobiles, steel products, such as the glass industry ideal fuel filler - type resistance
我公司研發生產的改性表面處理氫氧化鎂系列產品，純度高、粒徑均勻、分散性好、親和力強，屬于無鹵、無煙、無滴、無毒性、安全性的阻燃劑，是橡膠、塑料、橡塑、工程塑料、電器、電線、電纜料、電纜護套、熱縮材料、絕緣子、避雷器、化纖紡織、防火塗料、油墨、造紙、運輸帶、煤礦風筒、電子電器器材、蓬布、帳篷、軍事、航空航天、造船、汽車、玻璃鋼製品等各行業理想的填料型阻燃料。 -
B. main use : as widely used all over the world, it is a good substitute for asbestos in construction industry, an ideal filling material for paint, dope, rubber and plastic, and its application goes as far as to many other fields like electric welding, fire retardant, electronic products, oil well drilling and nacre dye
天然雲母粉廣泛應用於絕緣絕熱油漆塑料橡膠陶瓷石油鉆井電焊條化妝品宇航等領域中，超細雲母粉作塑料塗料油漆橡膠等功能性填料，可提高其機械強度，增強韌性附著力抗老化及耐腐蝕型等。