Effect of the carbon black on the electrical performance of gas diffusion electrode of zinc - air battery
炭黑對鋅空氣電池空氣擴散電極電性能的影響 -
The optimum conditions for air electrode preparation were shown as follow : 20 % ptfe and 20 % mno2 in active layer, thickness of active layer 0. 15 - 0. 25mm and the ratio of active carbon to ethine black 4 : 1 ; 60 % ptfe in the gas diffusion and waterproof layer, employing na2so4 as pore - making agents, thickness 0. 35 - 0. 45mm, colding forming and layer sequence catlytic layer / gas diffusion and waterproof layer / current collector layout ; employing 40 meshed nickel screen as current collector and thermal treatment temperature over 200
確定了制備空氣電極的優化工藝條件，催化層中ptfe含量約20 ， mno _ 2的最佳含量約為20 ，催化層中活性炭和乙炔黑的比例為4 ： 1 （質量比） ，厚度在0 . 15 - 0 . 25mm之間。防水透氣層中ptfe的含量約為60 ，以無水硫酸鈉作為造孔劑，厚度一般為0 . 35 - 0 . 45mm 。電極各層採用催化層/防水透氣層/集流體的排布方式，冷壓成型，熱處理對空氣電極的性能影響較大，熱處理溫度不低於200 。 -
The calculation results show that the radius of the gas channels in the reaction layer and the porosity and average pore radius of the gas - diffusion layer seem to be less important for the performance of the electrode
模型結果表明對于電極性能而言，氣體擴散層的孔隙率與平均孔徑以及反應層氣體通道的半徑，相對其他參數來說顯得不太重要。 -
Air electrode, in which nh _ 4hco _ 3 is as pore former, is mainly studied in this paper. the manufacturing process of air electrode, the composition of waterproof and gas diffusion layer, the composition of catalysis layer, and two kinds of catalyst were studied by numbers
本文針對以碳酸氫銨為造孔劑的空氣電極進行研究，分別對電極製作工藝、防水透氣層組成、催化層組成以及兩類催化劑進行了初步系統的探索和研究。 -
The thin - film and flooded - agglomerate ( tffa ) model assumes that the oxygen diffusion electrode made of a gas - diffusion layer and a reaction layer possesses a double - scales of porous structure in the reaction layer
薄膜浸漬聚集體（ tffa ）模型假定由氣體擴散層和反應層構成的氧氣擴散電極在反應層中是一種二次構造形式的多孔結構。 -
In the experiments, two series of catalysts were synthesized by co - deposition and sol - gel methods each. the composition of both waterproof and gas diffusion layer and catalysis layer were optimized by the orthogonal test. meanwhile, quasi - steady cathode polarization curves, x - ray diffraction ( xrd ), scanning electronic microscope ( sem ) were used to analyst the relationship between the microstructure and the performance of air electrode
實驗採用共沉澱法和溶膠凝膠法合成了兩類催化劑;對防水透氣層和催化層進行了正交試驗優化;同時，還採用測準穩態極化曲線， x射線衍射（ xrd ） 、掃描電子顯微鏡（ sem ）等分析測試手段，對空氣擴散電極催化材料、空氣擴散電極界面結構與性能的關系等作了較深入的研究。