When the alumina fiber accounted for 10 %, the density of the composites was chiefly high and the fiber evulsion effect was reinforced ; when the alumina fiber accounted for 30 %, the fiber evulsion effect, fracture and bridge - connection effect were mainly strengthened, when the fiber proportion was 50 %, at the temperature of 1500 c, the bending strength reached 26. 11 mpa while the compressive strength was 79. 30 mpa
氧化鋁纖維含量為10和30的試樣增強機理不同,含量為10時,復合材料以基質密實度高、纖維拔出效應增強為主;氧化鋁纖維含量為30時,復合材料以纖維拔出、斷裂、橋聯效應增強為主。當纖維含量為50時,在1500下燒成,其抗折強度達到26 . 11mpa ,耐壓強度達到79 . 30mpa ,該復合材料可用作輕質保溫材料。 -
By using the high pure alumina micro - powder ( > 99. 0 % ) and the polymorphous alumina fiber as materials, by adding alumina sulfate as the binder or polypropylene - amide as the disperser respectively, through mixing, dispersing, and compression molding, at different temperatures of 1200 c, 1350 c, 1400 c, 1500 c, and 1550 c with no pressure, the alumina fiber - alumina composites were made
本試驗採用高純氧化鋁微粉( 99 . 0 )和多晶氧化鋁纖維為原料,分別加入硫酸鋁和聚丙烯酰胺作結合劑和分散劑,經混合、分散、壓力成型及在1200 、 1350 、 1400 、 1500 、 1550下無壓燒成制得氧化鋁纖維? ?氧化鋁復合材料。 -
In the 2lth century, there is more opportunities for the alumina oxide fibers, but the process of continuous high performance alumina oxide fiber is still a great challenge
對含鋁氧化物陶瓷纖維的發展前景和發展方向進行了較為深刻的探討。