大坍落度混凝土-
The results of research on the workability of hbc concrete show that hbc concrete, when compared with opc concrete, has excellent compatibility with superplasticizer, in terms of better initial fluidity, less slump loss, definite saturation point and less dosage at saturation point. in addition, good mineral admixture such as i class fly ash can obviously improve the workability of hbc concrete. moreover, hbc concrete exhibits more excellent workability under the condition of low w / c ratio, which indicates hbc is more suitable for making super high strength concrete whose w / c ratio is very low
對高貝利特水泥高性能混凝土工作性能的研究結果表明，高貝利特水泥與高效減水劑具有良好的適應性，表現為初始流動度較大，經時損失較小，具有明顯的飽和點且飽和點摻量較小；此外，優質的礦物摻和料如一級粉煤灰能明顯改善hbc混凝土的工作性能；更為突出的是hbc混凝土在低水膠比的情況下表現出更為優異的工作性，這一特性預示著高貝利特水泥更適宜配製水膠比很低的超高強混凝土。 -
The new high effective water - reducing agent act - fdn has characteristic of reactivity, it ca n ' t dissolve in water but do in alklia. in the concrete, it decompounds slowly and gives out sulfonate group which has dispersity, this can make the high effective water - reducing agent available for a long time, therefore it can reduce slump loss
研製的新型高效減水劑act - fdn ，具有反應性的特點，不溶於水但溶於堿，在混凝土這樣的堿性環境下可以緩慢分解釋放出具有分散性能的陰離子磺酸基，使高效減水劑能夠持久發揮作用，從而達到了降低坍落度損失的目的。 -
But some problems with self - compacting concrete such as high slump loss and the difficulty of harmonizing the cohesiveness and the flowability should be solved. the theory of concrete mix design should also be perfected. in accordance with these problems, this thesis carry out such research works as follows to deal with them
然而，免振搗混凝土特別是高強超高強免振搗混凝土坍落度損失大，粘聚性和流動性難以統一以及易產生收縮裂紋的問題亟待解決；免振搗混凝土的配比設計理論也需要進一步地加以完善。 -
Mineral admixtures have unsuperseded advantages in improving the workability and durability of self - compacting concrete. the reasons of tendency of cracking in self - compacting concrete and the influence factors have been studied, and the new type of mineral admixture has been used in high performance self - compacting concrete, and its defects such as high slump - losing and shrinking or cracking is successfully prevented
分析了免振搗混凝土容易產生收縮開裂的原因及其影響因素，將研製的新型礦物添加劑應用於免振搗高性能混凝土之中，解決了免振搗混凝土坍落度經時損失大、易產生收縮開裂等技術難題，配製出免振搗微膨脹高性能混凝土。 -
Polycarboxylate series high range water - reducing agents, which can provide concrete high fluidity, good retarding performance and low slump loss, have become more popular recently
聚羧酸鹽系高效減水劑既具有較好的初始流動性，又具有較好的保坍性，日益成為混凝土外加劑領域研究的熱點。 -
According to many years experience of dealing with client quality complains, the author introduced in brief its principle and content, and laid emphsis on the common quality complains of cement enterprise, such as concrete strength is lack, the concrete setting time is unnormal, the concrete slump constant is a little small and the loss is high, compatibility between cement and admixture is bad, cement color changes, concrete surface rise sand and cement agglomerate
作者結合自己多年處理顧客質量投訴的經驗，簡單介紹了處理顧客質量投訴的調查原則和內容；重點對水泥廠最常見的質量投訴內容包括混凝土強度不足，凝結時間異常；混凝土坍落度偏小，經時損失大；水泥與外加劑相容性不好；水泥顏色變化、混凝土地面起砂及水泥結塊等等投訴，分別進行了現象描述，原因分析和調查方法介紹。 -
The result of experiment states hpc which initial slump is more than 230mm, after 120min is still above 190mm ; the 7d and 28d hydration, the compression strength of concrete is more than vompa and 90mpa can be made from the ground high - ti bfs instead of 10 - 30 percent of equal p. o. 525r, with the aid of superplasticizer and additive on the water cement ratio is 0. 26
利用磨細的高鈦礦渣等量取代10 - 30的硅酸鹽水泥，並摻入高效減水劑b和外加劑ua ，在水灰比為0 . 26時，可以配置出初始塌落度大於230mm ， 120min后，塌落度仍大於190mm ， 7天強度大於70mpa ， 28天強度大於80mpa的高性能混凝土。 -
As commercial concrete is arisen, people pay much attention to make concrete fluidized ; and it ' s to say the concrete must keep a high slump after long - playing transportation and halt
隨著商品混凝土的興起，混凝土正向流態化的方向發展，要求混凝土拌和物在經過較長時間的運輸和停放后仍能維持較高的坍落度。 -
To obtain high fluid structural lightweight aggregate concrete with good uniformity, it is necessary to limit the max grain size of lightweight aggregate to 20mm, cement content to 500kg / m ~ 3 and slump of concrete mixture to 260mm
要獲得均勻穩定的大流動性結構輕集料混凝土，陶粒的最大粒徑不宜超過20mm ，水泥用量不宜超過500kg / m ~ 3 ，拌和物坍落度宜小於260mm 。 -
In addition, vibration has great effects on uniformity of high fluid structural lightweight aggregate concrete. there is obvious separation of lightweight aggregate from mortar in mixture of high fluid structural lightweight aggregate concrete with slump of 220mm when vibrated for 10 minutes
此外，振動對大流動性輕集料混凝土的勻質性十分不利，對坍落度220mm左右的輕集料混凝土拌和物，振動時間超過10秒，就會出現明顯的分層現象。 -
Under the direction of such theories, the influence of the composition of the concrete to the workability, mechanical property and durability of hplc is analyzed systematically ; the key technology of the preparation of hplc was grasped. the theory of strength improvement of subsidiary bonder is detected, special additive - fdl for hplc is made, lc40 - lc60 hplc with the slump over 18cm, the slump flow over 50cm, segregation degree below 5 %, small drying shrinkage, high tension strength and long durability is prepared. the concept and experimental method of the segregation degree of the mixture is put out and the analytical system of high performance hplc is built
以設計理念和設計理論為指導，系統研究了輕集料、輔助膠凝材料等組分及其配比參數對輕集料混凝土工作性能、力學性能和耐久性能的影響規律，探明了輔助膠凝材料對于輕集料混凝土的增強機理，研製出能夠有效控制輕集料混凝土拌和物分層離析度和降低坍落度經時損失的專用外加劑fdl ，掌握了制備高性能輕集料混凝土的關鍵技術，制備出坍落度大於18cm 、擴展度大於50cm 、分層度小於5 、低干縮、高韌性、高耐久的lc40 lc60高性能輕集料混凝土。 -
The shrinkage characteristics of hsc and normal concrete at short term and long term are researched. based on the above research, high performance expansive c50 - c80 concrete, which posses good expansive properties, excellent flow ability, low slump loss and hydration heat. in order to improve the anti - cracking of some important projects, such as cutting wall, the workability and bulk stability of fiber - reinforced micro expensive concrete are researched
針對高強混凝土的收縮特性以及性能特點，本文提出將膨脹劑引入高強混凝土內進行補償收縮，研究了粉煤灰、礦渣、硅灰等摻和料對混凝土工作、力學耐久性能的影響和c50 c80高強微膨脹補償收縮混凝土的力學與工作性能，配製出具有很好的可泵性能和耐久性能的混凝土。 -
Measures for further developing concrete mix design were presented based on above work. for example, adopts pfca as an index in designing durability of concrete, uses mortar slump flow test to select cements and water - reducers and to measure saturation dosage of water - reducer in mortar and then determine optimum dosage of it in concrete, uses bar - slump test to determine stability and fluidity of fresh concrete, and consequently, the workability of high fluidity and high stability concrete such as pumped or self - compacting concrete can be designed by adopting proper cfvm determined in terms of rheological properties of designed mortar measured with cone - based rheometer
如採用粗集料破碎率作為耐久性設計的一個指標；採用砂漿坍落擴展度試驗選擇水泥和減水劑，確定砂漿中減水劑的飽和摻量，並通過上述數學模計算混凝土中減水劑的飽和摻量，以此為參照確定最佳摻量；採用障礙坍落度試驗確混凝土的穩定性和流動性，結合由漏斗式砂漿流變儀測定的砂漿流變性能確定合理的砂漿填充系數，從而實現對高流動性高穩定性要求的混凝土（如泵送和免振自密實等）的工作性設計。 -
In this paper, the confecting technique on many ingredients " hpc was studied, and the optimum ratio of many ingredients in hpc was confirmed by regression method in spss and optimizing method in matlib, considering mechanics performance of high performance concrete and collapsing slump of hpc mixture. c : bf : fa : sf : uea = 3 : 1 : 1 : 0. 2 : 0. 02. we confected out hpc with the ratio
用這一比例關系我們配製出塌落度達130mm 、早期強度高、後期強度增長幅度大的高性能混凝土，其7d 、 28d和56d的抗壓強度分別為47 . 55mpa 、 71 . 05mpa和88 . 8mpa ，後期強度增長率可達到25 。