It focuses on the theory of the mineral functional materials " improving the anti - chloride permeability and the chloride binding. the main achievements of this article include : 1 ) use the technology of xrd, sem, bet, laser particle size distributor etc to test the component, the construction, particle size distributor, specific surface etc of micro - silica, ultra - fined slag, high quality fly ash, meta - kaolin clay, four types of the mineral functional material, theoretically analysis the functions which the four mineral functional minerals act on cement concrete, namely pozzolanicity effect, filling effect, micro - aggregate effect, surface adsorption effect and so bring into play the affect of plastification, lowing of temperature, reinforcement, improvement of durability. base on this analysis we can conclude that the proper diameter of the mineral functional material is 5 m - 15 m, that is blain fineness 4500cm2 / g - 7500cm2 / g
本論文的主要成果包括以下幾個方面： （ 1 ）採用xrd 、 sem 、 bet 、激光粒度分析儀等多種測試手段，探明了以硅灰，超細磨粒化高爐礦渣，優質粉煤灰及偏高嶺土超細粉等4種超細礦物功能材料的組成、結構、粒度分佈、比表面積等基本性質；從理論上分析了礦物功能材料在混凝土中的4種效應，即火山灰效應、填充密實效應、微集料效應、表面吸附效應，並由此發揮出增塑、溫峰削減（降熱） ，增強及耐久性改善等作用；通過相關理論分析，推導出礦物功能材料的合理粒徑范圍在5 m 15 m ，即勃氏比表面積為4500cm ~ 2 g 7500cm ~ 2 g 。 -
There is correspondence in evaluating sulfate resistance of cement paste by three test methods such as rapid boiling, gypsum mixing and wet - dry test. high strength grade cement can meliorate property of sulfate resistance
外摻石膏法、干濕交替法以及快速沸煮法三種實驗方法對評價水泥砂漿的抗硫酸鹽侵蝕性能有較好的一致性；高標號水泥品種對抗硫酸鹽侵蝕性能有很好的改善作用。 -
In this article, the steel fibre is a kind of industrial wastes - stainless steel fibre dregs. the use of it is helpful in comprehensive utilization of resource and environment protection. the author of this article used orthogonal test design, arranged the test scheme scientifically, selected material, at last yield a high strength concret, whose strength exceeded c60, mainly by using 42. 5 ordinary portland cement, silica fume, superplasticizers, stainless steel fibre dregs and so on
本文所用的鋼釬維是一種工業廢料?不銹鋼纖維渣，它的應用有利於資源的綜合利用和生態環境的保護本文在廣泛閱讀國內外有關資料的基礎上，採用正交設計，科學地安排試驗方案，精心選擇材料，用42 . 5普通硅酸鹽水泥、硅灰、高效減水劑、不銹鋼纖維渣等材料，採用常規工藝配製出了強度達到c60的高強混凝土，並且通過對試驗數據的分析，給出了最優配比方案。 -
Through searching on the technical property of such pile, taking two foundation treatments as project background which are soft foundation treatment of wuhan dongxihu segment of the jingzhu freeway in hubei province and bridge foot protection at hebi xingfu eservoir in henan province, this paper carries out test study on active mechanism of crushed stone pile filled with cement slurry and its application in dealing with high earth filled soft ground and bridge foot protection
通過對無砂混凝土小樁技術特點的探討，以湖北京珠高速公路武漢東西湖段軟基處理和河南省鶴壁市幸福水庫公路橋梁基礎加固為工程背景，就無砂混凝土小樁的作用機理及其處理高填方軟基和橋梁基礎加固等方面展開試驗研究。 -
Aminobenzenesulfonic acid super - plasticizer is selected though cement paste test, which be provided with high water - reducing property, low slump loss and good compatibility with cement. according to the request of super high early strength, admixture rf is obtained though tests to compare performances of different accelerators and admixtures. experimental research and analysis are carried out on coarse aggregate ' s grain - size effect and composite aggregate ' s bulk - density to take sensitivity of coarse aggregate into account
通過水泥凈漿試驗比較選擇了減水率高、坍落度損失小、與水泥適應性好的氨基苯磺酸鹽高效減水劑；針對超早強的性能要求，試驗比較了不同早強劑及早強性摻合料的性能表現，研製了早強性能顯著、與高效減水劑和水泥相容性較好的rf摻合料；考慮到修補混凝土對粗集料粒徑的敏感性，對粗集料粒徑效應及混合集料堆積密度進行試驗研究與分析；並對修補混凝土的抗折、抗壓、新老界面粘結強度以及抗凍性等進行了試驗研究。 -
Test results show that the carbon fiber with high elastic modulus can not only improve strength performance but also improve toughness of cement mortar, and that the polypropylene fiber with low elastic modulus can only toughen cement mortar
試驗結果表明，高彈性模量的碳纖維對水泥砂漿既能增強，又可顯著增韌；低彈性模量的聚丙烯纖維對水泥砂漿只能增韌。 -
6. the durability of concrete structures resisting chloride diffusion in different water cement ratio and different contents of fly ash and silica was analyzed and durable life was predicted based on the results of the test, which will be helpful to preparation of high performance concrete ( hpc ) as well as durability design and assessment of concrete structures
系統地研究了低水膠比及摻加粉煤灰、硅灰的高性能混凝土的電滲透性和氯離子擴散系數，分析了水膠比以及粉煤灰和硅灰等活性集料對混凝土結構抵抗氯離子侵蝕的耐久性能的影響，並對高性能混凝土結構抗氯離子侵蝕的耐久壽命進行了預測，為氯鹽污染環境下高性能混凝土的配製以及混凝土結構耐久性評估與設計提供參考。 -
The essay researched the compressive strength, bending strength, impact resistance and abrasion resistance of high strength polypropylene fibermesh concrete the mechanism of enhancing the properties of high strengh poloypropylence fibemesh road concrete composite was discussed and analyzed the regression on tensile strengh with portland cement mixed with fiber was derived using experiment the tensile strength of fiber soil stablization with porland cement was increased with dosage and length of fiber while the former was more effective than the latter test and analysis results indicate that polypropylene fiber can not only reinforce the strength of concrete, but also obviously promote the flexural fatigue life by the great stress the application of polypropylence fiber reinforced concrete in pavement construcion are also introduced
文章研究了不同摻量有機纖維混凝土的抗壓、抗折強度、抗沖及性能、疲勞性能及耐磨性等各種路用性能，綜合論述了有機纖維對水泥混凝土路用性能的影響。通過試驗闡述了纖維水泥混凝土各種路用性能與纖維摻量、長度間的關系。分析表明纖維水泥混凝土隨著纖維摻量和長度增加而增加，且纖維摻量對纖維混凝土抗拉強度的影響比纖維長度的影響更大。 -
The author of this article used orthogonal test design, arranged the test scheme scientifically, selected material carefully, at last yielded an high strength lightweight aggregate concrete material ( hslacm ), whose compressive strength exceeded 50 mpa and quality under 1950kg / m3, mainly by using 42. 5 ordinary portland cement, expanded fly ash aggregate, silica fume, superplasticizers and so on
本文是在廣泛閱讀國內外有關資料的基礎上，採用正交設計，科學地安排試驗，精心選材，用42 . 5普通硅酸鹽水泥、粉煤灰陶粒、硅灰、高效減水劑等材料，採用一般工藝配製出了一種抗壓強度超過50mpa 、質量低於1950kg m ~ 3的高強輕骨料混凝土材料。 -
Test method for analysis of high alumina cement
高鋁水泥化學分析方法 -
Orthogonal test of sintering conditions of q phase - ca - c12a7 high alumina cement
7高鋁水泥燒成的正交試驗研究