Bismuth ruthenate and silver were selected as conductor phases and the mixture of calcium oxide - alumina - silicon dioxide ( cao - al _ 2o _ 3 - sio _ 2 ) glass and lead oxide - boron oxide - silicon dioxide ( pbo - b _ 2o _ 3 - sio _ 2 ) glass was selected as inorganic binder phases. it was found that, with the increasing of volume fraction of silver and conductor phase, sheet resistivities descend and there are critical thresholds
實驗發現,隨著功能相百分含量的增加,電阻膜層的方阻值逐漸減小,存在兩個臨界閾值,電阻溫度系數偏向正值;功能相中銀百分含量增加,膜層的方阻值逐漸減小,有一個臨界閾值,電阻溫度系數偏向正值。 -
On the base of the development of thick film pastes technology, ru - based thick film resistor pastes have been studied due to select conductive phase and inorganic binder. state - of - the - art techniques such as rolling, screen printing and sintering were used for sample preparation. effects of ingredients, printing parameters and sintering parameters, microstructure on the properties of thick film resistor ( trf ) have been analyzed with xrd, sem, dsc and electrical tests
本文在跟蹤國內外厚膜漿料技術發展的基礎上,以釕酸鉍/銀系厚膜電阻漿料為研究對象,通過選用合適的功能相和無機粘結相成分,以三輥軋制、絲網印刷和高溫燒結等制備工藝為技術特徵,採用xrd 、 sem 、 dsc等分析方法和電性能測試手段,系統的研究了漿料中各相的成分配比、制備工藝參數,以及膜層微觀結構對厚膜電阻性能的影響規律。 -
In the study, a new kind inorganic anchoring material was developed, which consisted of special binder and aggregate, the former is made from clinker, blast furnace slag and compound admixture, and the later is superfine sand. effects of the factors such as clinker / slag, binder / sand, solution / binder and constituent of solution on the strength, set - time and contraction of the matrix made from the anchoring material were studied
上述分析研究得出以下結論:新型無機錨固材料具有早強、快硬、高強特點, 10h .抗壓強度可達26 . 5mpa , 365天強度可達144 . 0mpa ;初凝時間在40min . 3h .之間,且初終凝時間差在15分鐘以內;在保濕條件下具有微膨脹性,膨脹率在0 . 5 %以內。 -
Secondly, appropriate refiring change ratio is gained by designing compound inorganic binder. effects of additional inorganic constituents on properties of trf were studied
從提出復合無機粘結相的概念,實現了對重燒變化率的可控調整。 -
The study shows that when 1 % ~ 2 % of a binder is added and sintering is done at 900, macroporous inorganic membrane is obtained
研究表明,當粘結劑加入量為1 % ~ 2 % 、燒結溫度在900時,可以獲得較大孔徑的無機膜。