intergranular 中文意思是什麼
intergranular
解釋
間粒狀；粒間的-
Review on the intergranular corrosion and exfoliation corrosion of aluminum alloys
幾種時效工藝下1420鋁鋰合金性能研究 -
Intergranular and exfoliation corrosion behavior of sc - containing al - cu - li - zr alloy
合金的抗晶間腐蝕和剝落腐蝕性能 -
Study on intergranular corrosion and exfoliation corrosion behaviors of 2195 al - li alloy
鋰合金晶間腐蝕及剝蝕行為研究 -
Original porosity is typified by the intergranular porosity of sandstones and the intercrystalline and oolitic porosity of some limestones
原生孔隙度以砂巖粒問孔隙度和某些石灰石的晶體粒間和鮞狀孔隙度為代表。 -
The result is that this gas pool has simple structure, only forms a little nose - like structure at the district of fenghuangshan ; this pool belongs to delta front sub - facies sedimentary model, the underwater distributary channel and mouth bar is the better sedimentary microfacies ; the physical property of the reservoir is poor, the type of pore of the reservoir rock mostly are intergranular pore, intergranular solution hole and little are intercrystalline micropore ; the influential factors of pore structure and physical property are lithofacies, lithologic character and diagenesis ; the off - take potentia of all the testing well are deadly shortness, the wells have the worth of industrial recovery only under the condition of going through sand fracturing, and in the early of binging into production, the oil and sheath pressure drop rapidly, the production of the well drop rapidly
研究認為該氣藏構造簡單，只在鳳凰山形成了一個小型的鼻狀構造；屬於三角洲前緣亞相沉積模式，水下分流河道和河口壩是有利的沉積微相；儲層物性差，儲層巖石的孔隙類型主要有粒間孔、粒間（內）溶孔及少量晶間微孔；影響蓬萊鎮組氣藏儲層孔隙結構及儲集性的因素有巖相、巖性條件及成巖作用；所有測試井自然產能都極低，必須經加砂壓裂后才有工業開采價值，且投產初期，油套壓下降較快，氣井產量下降迅速。 -
Excellent intergranular corrosion resistant properties, suitable to manufacture the equipment which resist to sulphuric acids. phosphonic acide. formic acids andacetic acids
用於抗鹽酸、磷酸、甲酸、乙酸的設備，有良好的耐晶間腐蝕性。 -
Based on these experiments, it may be claimed that there is segregation of sn to grain boundaries in 0. 15 % c steel during cooling from a high solution treatment temperature. this segregation reduces grain boundary cohesion, which results in low hot ductility and intergranular fracture
通過試驗和計算得出: sn在0 . 1swt . % c鋼中發生非平衡晶界偏聚的臨界時間為1245左右，臨界冷卻速率大約為8 / s ，與試驗結果基本一致。 -
It is found that the electric, field improves elongations in 2090 and 2090 + ce alloys markedly, especially in 2090 alloy, but has little effect on strengths. at the same time, the electric field lessenes percentages of intergranular delamination and increases transgranular fracture and microscopic plastic deformation. besides, the electric field makes both average particle size and its distributing range of 8 " phase smaller, and reduces the half width of pfz in aged alloys
研究表明：固溶電場可顯著提高2090合金及2090 + ce合金的延伸率，尤其是對2090合金，但對強度則無明顯的影響；同時，固溶電場減少合金的沿晶分層斷裂比例，並增加穿晶斷裂及微區塑性變形；固溶電場還使合金時效后相顆粒的平均尺寸減小、尺寸分佈范圍減小，並使pfz的寬度減小。 -
The electric field strengthens the laminate boundary of 2090 alloy. the laminate strengthening mechanism translates into boundary strengthening and grain inner toughening with more ductility fracture and less intergranular fracture. the ductility property is enhanced with no change of intensity
對鋁理合金sem實驗發現，電場固溶和時效強化了晶界，和晶內塑性的改善，斷裂特徵出現由分層沿晶斷裂向塑性斷裂轉變，斷麵塑性變形特徵增加。 -
Corrosion of metals and alloys - determination of resistance to intergranular corrosion of solution heat - treatable aluminium alloys
金屬與合金的腐蝕.溶解熱處理鋁合金的耐晶間腐蝕性的測定 -
Burial dissolution mainly developed inside the primary micropores, the partly filled intergranular porosities and the intercrystal porosities, which furthermore formed lots of enlarged pores, intergranular pores, oolimolds
埋藏溶解作用主要在粒間半充填剩餘縫隙、交代白雲石的晶間孔內進行，這進一步溶蝕造就了大量超大孔隙、粒間溶孔、粒內孔、鑄模孔等。 -
Intergranular segregation dilution induced by ap plied stress
低作用應力引起的溶質在晶界非平衡偏聚或貧化 -
Review on the development and research of single layer intergranular semiconductor ceramic
單層片式晶界層半導體陶瓷材料研究進展 -
The fatigue cracks initiate in a intergranular manner and propagate in a transgranular manner, which stages are separated by secondary cracks
實驗結果表明疲勞載荷下的橡膠裂紋首先沿片晶結合面萌生，然後穿晶擴展破壞，且存在次生裂紋。 -
With carbon content increasing, the carbide network on the fertile grain boundary sprouting and propagating. the fracture mode has been changed from cleavage to along boundary and the intergranular corrosion induced by solution chromium decreasing
隨碳含量提高，晶界上碳化物萌發、擴展呈網狀，鑄件脆斷由解理斷裂發展為沿晶斷裂，同時鐵素體不銹鋼晶間腐蝕傾向增大。 -
The microwave magnetic sintering can not only lower the sintering temperature and shorten the sintering time, but also decrease the micro - grain size of magnets and make intergranular phase and grain boundary of main phase distributed well. the abnormal grain growth was found in conventional sintered ndfeb magnets, which may be due to the greater particle size and uneven distribution of powder, and higher sintering temperature and longer sintering time. of course, the abnormal grain growth would deteriorate the magnetic properties
微波磁場燒結的不但降低燒結溫度，縮短燒結時間，而且使磁體整體加熱，受熱更均勻，因而磁體晶粒更細小，並且主相晶粒邊界趨于規則化，晶間相的分佈更均勻；在常規燒結的磁體中則出現了晶粒異常長大現象，造成這一現象的原因，一方面可能是燒結溫度過高或燒結時間過長，另一方面可能是磨製的粉體均勻性較差，存在的大顆粒被許多細小顆粒包圍，在燒結過程中，大顆粒不斷吞併小顆粒，逐漸長大，而異常長大的晶粒自然會導致磁體性能的惡化。 -
The results show that the fracture surface is characterized by a combination of most intergranular brittle regions and a few cleavage regions, and there are finer precipitations on grainboundaries
結果表明，成型模裂紋斷口形態呈沿晶特徵，沿晶面上有細小析出物，為脆性斷裂。 -
All of these reservoirs have bad physical property with lower porosity and lower permeability. mainly reservoir paces is cracks ( structure crack, diagenetic crack ), the following is primary intergranular pores, primary intragranular pores, intergranular solution pores, intergranular solution pores, intercrystaline pores and so on. this layer was in later diagenetic a stage
這些儲集體的物性都很差，為低孔、低滲儲層，其儲集空間主要為裂縫（構造縫、成巖縫等） ，其次為原生粒間孔、溶蝕粒間孔、原生粒內孔、溶蝕粒內孔和晶間孔等。 -
The boundary of ferrite has been clarified and fined by adding re into crsomo. the intergranular corrosion induced by solution chromium decreasing can be restrained for nb, v, ti combing carbon in the steel. the wear resistance of stainless steel can be increased for the precipitation of microalloyed carbides
其中，稀土能夠凈化鐵索體晶界，並起到變質劑的作用，細化鐵素體晶粒，改善不銹鋼的韌性；鈮、釩、鈦能夠與鋼中的碳結合，減少固溶鉻的損失，從而避免晶間腐蝕，同時細小微合金碳化物的沉澱析出可提高不銹鋼的耐磨性。 -
By the analyses of corrosive medium and manufacturing process quality, the cracks of glycol evaporators in dushanzi petrochemical company have been confirmed to be intergranular corrosion cracks
摘要通過裂紋宏微觀形貌分析、腐蝕介質分析、對蒸發塔製造過程質量分析等，證實了獨山子石化乙二醇蒸發塔的裂紋屬晶間型應力腐蝕裂紋。