The co - effect of silane coupling agent, shrinkage reducing admixtureand fly ash on new - to - old concrete interfacial layer were primarily studied through a contradistinctive experimental study in this paper
摘要通過對比試驗研究，初步探討偶聯劑、減縮劑和粉煤灰共同作用對新老混凝土界面層劈拉強度的影響。 -
At last, in order to improve the interfacial bond strength, durafiber pretreated by variable silane coupling agents were mixed into furan polymer mortar, then make its mechanic properties testing
最後，為改善杜拉纖維與呋喃樹脂砂漿的界面粘結性能，採用杜拉纖維用不同的硅烷偶聯劑處理后再加入到呋喃樹脂砂漿中，測試其力學性能。 -
The results show that the tensile strength and rupture strength of furan polymer concrete were improved when the durafiber was used ; and durafiber pretreated by wd - 60 silane coupling agent can enhance the strengths ( the tensile strength, rupture strength and impact toughness ) greatly,
結果表明：在呋喃樹脂混凝土（砂漿）中加入杜拉纖維，可提高其抗拉強度、抗折強度和沖擊韌性；經硅烷偶聯劑wd - 60處理后的杜拉纖維對其抗拉強度、抗折強度有大幅度提高。 -
Silane coupling agents are also used in many commercial sand-epoxy-type composites.
硅烷偶聯劑亦用於許多通用的砂子環氧型復合材料中。 -
Silane coupling agents are compatible with almost every type of organic polymer.
硅烷偶聯劑幾乎對每一種類型的有機聚合物都是合適的。 -
Organic silicon : silicon oil ( silicon grease, silicon suckling liquid, silicon surfactants ), silane coupling agent ( organic silicon chemistry reagent ), high temperature sulfur rubber, liquid silicon rubber, organic silicon polymer, silicon resin, organic silicon singles, compound etc., organic silicon produce and the related raw material, aid chemical preparation, technique
有機硅：硅油（硅脂、硅乳液、硅表面活性劑） ，硅烷偶聯劑（有機硅化學試劑）高溫硫化橡膠、液體硅橡膠、有機硅聚合物、硅樹脂、有機硅單體、復合物等，有機硅生產相關原料、助劑、技術。 -
Single - walled carbon nanotubes ( swnts ) were opened and oxidized in the concentrated h2so4 / hno3 mixture ( volume ratio : 3 : 1 ), hydroxyl groups could be brought into the swnts after oxidation modification treatment, and the long - chain silane coupling agent was grafted onto swnts via hydroxyl - silanol route
摘要採用混酸體系（濃硫酸濃硝酸體積比為3 / 1 ）對單壁碳納米管進行了氧化處理，並通過氧化處理后在單壁碳納米管表面生成的羥基官能團與長鏈硅烷偶聯劑進行反應，制備了表面有機修飾的單壁碳納米管。 -
Polyurethane composites contained different content of alumina and silicon dioxide particles were prepared, and the alumina particle was processed with two kind of silane coupling agent which models were kh550 and kh560
論文分別制備了al _ 2o _ 3顆粒及白碳黑增強的聚氨酯復合材料，考查了填料種類、填料體積分數、偶聯劑種類對聚氨酯復合材料力學性能及沖蝕磨損性能的影響。 -
Silane coupling agent series
硅烷偶聯劑系列 -
Silane coupling agent
硅烷偶聯劑 -
Effects of silane coupling on interface between asphalt and granite or cement mortar
硅烷偶聯劑對瀝青與石料及水泥膠砂界面的作用 -
The mixture of bis triethoxysilpropyl tetrasulfide and white carbon black silane coupling agent
雙-丙基三乙氧基硅烷-四硫化物與白炭黑的混合物硅烷偶聯劑 -
The mixture of bis triethoxysilpropyl tetrasulfide and carbon black n330 silane coupling agent
雙-丙基三乙氧基硅烷-四硫化物與n - 330炭黑的混合物硅烷偶聯劑 -
Preparation and properties of antibacterial and anticorrosive film made of silane coupling agent solution adding ag on stainless steel surface
不銹鋼表面含銀有機硅烷偶聯劑抗菌耐蝕薄膜制備和性能 -
This thesis is researching the surface antibacterial application in stainless steel. preparing two antibacterial films that have different properties in the surface of stainless steel, silver doped tio2 or sio2 films and silver doped sca ( silane coupling agents ) film
本課題研究不銹鋼的表面抗菌化，在不銹鋼表面制備兩種性質不同的抗菌膜層，即摻銀tio _ 2 、 sio _ 2無機抗菌薄膜和摻銀有機硅烷抗菌薄膜。 -
Silane coupling agent ( kh - 560 ) with active groups was used for the treatment on silica particles in this article. the surface of silica which was treated in the way of chemical bonds was changed from hydrophilication to amhydrophilication
本文採用具有活性基團的硅烷偶聯劑（ kh - 560 ）對二氧化硅粒子進行了表面改性，使二氧化硅顆粒表面由親水性變為親油性。 -
Surface modification of nano - zinc oxide by silane coupling agents
通過雙螺桿擠出機制備了尼龍 -
The study on the core - shell particles shows, one extrenity of silane coupling agents at the surface of the composite particles after adding aps are connected with the fe particles. and the other extrenity outside can polymerize with the active silica. the slick and compact surface of the composite particles shows the obvious core - shell structure. the surface of the composite particles are composed of the combined apex of the element si, o, c, h. the element o is superfluous to the element si
對納米復合鐵粒子研究表明，在aps改性的鐵納米粒子表面硅烷偶聯劑氨基一端連接鐵粒子，另一端對鐵粒子外面，能與活性硅聚合。鐵納米復合粒子顆粒表面光滑緻密。核殼復合粒子表面主要由si ， o組成，伴隨著微量的c ， h元素的峰，核殼復合粒子表面氧對硅有富餘。 -
Manufactures pharmaceutical and dye intermediates in china. products include a wide range of brominated organics, as well as esters, quaternary ammonium compounds, and silane coupling agents
-生產2 ， 2 -甲氧基丙烷2 -甲氧基丙烯2 -甲氧基丙烷亞硫酸二甲酯等中間體產品。 -
The results showed that compressive strength of sand mixture was markedly raised by using the silane coupling agent which can improve the surface contact state between sand and the binder
試驗結果表明，硅烷偶聯劑可以改善黏結劑與砂粒表面的接觸狀態，極大地提高堿酚醛樹脂砂的黏結強度。