凝固梯度- solidification : n. 團結；凝固；【化學】固體化（作用）。
- gradient : adj. 1. 傾斜的。2. 【動物；動物學】步行的，能步行的。n. 1. 〈英國〉（道路的）傾斜度，坡度，坡路。2. 【物理學】梯度，陡度，（溫度、氣壓等的）變化率，梯度變化曲線。
-
Microstructure and its scales of cu - 70 sn peritectic alloy under high - temperature gradient directional solidification
包晶合金高溫度梯度定向凝固的組織及其尺度 -
It was found that the interface morphology of ni, cr, al - tac eutectic in - situ composite evolved from plan to cell and then to dendrite with the increase of solidification rate, if the gradient retained constant. in the same time, the eutectic microstructure also evolved from rod to cell and then to dendrite
本工作發現，在溫度梯度基本保持不變的條件下，隨著凝固速率的增大， ni ， cr ， al - tac共晶自生復合材料的凝固界面由平界面向胞狀及枝狀界面逐漸轉化。 -
The coupled turbulent flow field and temperature field are simulated by finite element method ; the influence of casting speed on the turbulent flow field and temperature field in the melting bath and the interaction between those two field are analyzed ; the variation tendency of the heat flux intensity between the melting bath and casting roll and law of variation with changes of casting speed in the process of solidification are given ; a comparison between the simulation results and experimental results demonstrates their good agreement ; and the mechanism of the heat flux variation is identified by analysis on the temporature gradient and development of solidification within the melting bath and its influence on the variation of the heat flux intensity
採用有限元法模擬了雙輥鑄軋不銹鋼過程的流熱耦合問題;分析了鑄軋速度對熔池內流場、溫度場的影響以及流場與溫度場之間的相互影響;給出了凝固過程中熔池與鑄軋輥之間的熱流密度變化趨勢及隨鑄軋速度的變化規律，並把此模擬的結果與試驗的結果相比較，吻合較好;通過熔池內溫度場及溫度梯度分析了熔池內凝固的發展及其對熱流密度變化的影響。 -
In this paper, an ingot of niobium - niobium silicide based in - situ composites ( rmics ) was prepared by arc melting process, and nb - nb3si / nb5si3 in - situ composites with a uniformly orientated microstructure were produced in a high temperature gradient directional solidification apparatus named electron beam floating zone melting ( ebfzm ). the relationships between the processing parameters and the characteristics of the solidified microstructure have been investigated. the influence of the microstructure on the mechanical properties has been revealed and the rupture mechanism at room temperature has been discussed
本文採用真空電弧自耗熔煉法制備了鈮?硅基rmics材料的母合金錠，並採用電子束區熔（ ebfzm ）高溫度梯度定向凝固裝置制備了定向效果良好的nb - nb _ 3si nb _ 5si _ 3共晶自生復合材料，並對其定向凝固工藝參數和組織之間的對應規律、組織特性進行了研究，探討了凝固組織對室溫力學性能的影響及其斷裂機制。 -
In this paper, one high temperature gradient directional solidification apparatus with liquid metal cooling ( lmc ) was used. the technology parameter of preparation for ni, cr, al - tac eutectic in - situ composite was optimized
本文採用lmc高溫度梯度定向凝固裝置，對ni ， cr ， al - tac共晶自生復合材料進行了深入的研究，優化了該種自生復合材料的制備工藝。 -
The main subjects and conclusions are as follows : 1. a kind of directional solidification equipment of high temperature gradient and double - zone heating is self - made
主要內容和成果有： 1自行設計了一臺雙區加熱高梯度定向凝固裝置。