Some main results of testing research were as fellows : i. in the course of testing of leaching zinc dross, leaching zinc dross by sulfuric acid was researched and the effects on the leaching rate of the zinc dross were analyzed by author, the optimum conditions of leaching testing of zinc dross were determined as fellows : liquid - solid ratio 6 : 1, stirring ratio 250r / min, granularity 120 mesh, the soaking time 5h, the concentration of sulfuric acid of 30 %, and under these conditions, the rate of leaching zinc is above 92. 0 %. ii. in the course of testing of purification, on the basis of comprehending and comparing all present methods of the manganese - removal and iron - removal, the oxidizing method of manganese - removal in zinc sulfate solution using ammonium persulfate was put forward and the oxidizing method of iron - removal in zinc sulfate solution using the goethite process and oxidation - hydrolysis process was adopted
研究的主要結果具體如下： 1 、研究了硫酸浸出鋅浮渣並分析了影響浸出率的各種因素，確定了浸出鋅浮渣的最佳條件為：液固比為6 ： 1 ，攪拌速度為250r min ，粒度為- 120目，酸浸時間為5 . 0h ，硫酸濃度30 ，鋅浮渣的浸出率大於92 . 0 ； 2 、在綜合和比較了目前除錳和除鐵的各種方法基礎上，提出了過硫酸銨氧化除錳方法和選擇了針鐵礦-氧化水解聯合法除鐵方法，並分析和討論了影響除錳率和除鐵率等各種因素，確定了除錳的條件為：溫度90 ， ph值5 . 4 ，反應時間3h ，過硫酸銨達到理論值的1 . 2倍，除錳率超過99 . 86 ；聯合法除鐵的條件為：氧化反應時間1 . 5小時、溫度控制在90 92 、 ph值5 . 2 5 -
A lot of experiments have been done in the process of exploiture soft packaging li - ion battery about how to choice the rational arts and crafts. the content include : how to deal with the collector, add how much pvdf in the material, how long the material need to stirring and the right viscidity, how much condubtivity agent the electrode need, what theckness is best, choice different collectors, the degree of dryness of the electrode, theckness of pressed model, how much electrolyte will be added, placement how long after added the electrolyte, system of formation how to influnce the battery, in formation the battery need or not need preesure from outside, how to vacuumize and the optimize matching positive pole and negative pole. with these practice make sure the parameter of the positive pole should less than 90 m ; according to different vacuumize order the conduc - tivity agent in anode will be 5mass % and 9mass %, respectively, and in cathode the data is 2mass % ; every 100mah added to 0. 4 ml electrolyte ; before formation the battery should be placement 8 hours and the system of formation must be less than 0. 01c before the voltage reach to 3. 0v ; should press in outside when battery in formation ; to these batteries which capacity more than 350mah the vacuum time not excess 15s ; the optimize matching positive pole and negative pole between 2. 10 : 1 and 2. 15 : 1. finally make out the battery which cycling performance and security are all very well
液態軟包裝鋰離子電池的研究主要是對關鍵工藝進行了優化設計，具體包括:集流體的處理、 pvdf的加入量、漿料攪拌時間和粘度、導電劑的加入量、電極膜的厚度、不同集流體的選擇、電極膜的乾燥程度、壓型的厚度、電解液的加入量、注入電解液后靜置時間的長短、化成制度的影響、化成時電池所具有的壓力影響、抽真空的處理、正負極活性物質的匹配。最後確定出液態軟包裝鋰離子電池最佳工藝參數:正極膜的厚度小於90 m ;根據化成時不同抽真空順序，確定正極膜中的導電劑的加入量分別為5mass %和9mass % ;負極膜中導電劑的加入量為2mass % ;電解液的加入量為每100mah添加0 . 4ml ;化成前電池的靜置時間應當大於8h ;電池在3 . 0v之前採用小於0 . 01c的化成制度;在化成過程中應當施加一定的外部壓力;對於350mah的電池抽真空的延時不應大於15s ;而正負極活性物質的質量比應當在2 . 1 : 1 2 . 15 : 1之間。 -
The technique of producing metal matrix composite include powder metallurgy, casting ( including stirring casting process, in situ contact reaction process, liquid - phase metal infiltration process, co - spray deposition forming process ), reaction mechanic alloying process
制備金屬基復合材料的工藝分為粉末冶金法、鑄造法（鑄造法細分為攪拌鑄造法、原位接觸反應法、液相浸滲法、共噴射沉積法） 、反應機械合金化技術。 -
Every once in a while he would clinch his fingers and tap his foot - signs of the stirring mental process he was undergoing
他不時地捏緊拳頭，用一隻腳敲著地-這是他心情激動不安的跡象。 -
Both tidal mixing and wind stirring can weaken the vertical stratification induced by freshwater buoyancy, but different mechanisms dominate such a process : tidal mixing is accomplished through the upward dissipation of turbulent kinetic energy whereas wind stirring is in the opposite direction
盡管潮汐混合和風的攪動作用均能削弱河流沖淡水浮力引起的垂直層化現象，但是其控制機制有所不同：潮汐混合是通過湍流動能自下向上的耗散來完成的，風攪動的方向恰好相反。 -
Study on the basis of co operation by making a research on the two theories, then put forwards a teaching mode combining the above two. according to the characteristics of high school students, the author conducted a biology - teaching experiment among the second - grade students in high school. in the process, the mode succeeded in stirring the students " interest and cultivating their enthusiasm, initiative and creativity by adopting several methods such as questionnaire, observation, statistics analysis
根據高中學生心理特點，深入鉆研教材，挖掘適合自主?合作學習的內容，操作過程中運用了問卷調查、等組實驗、觀察和統計分析等方法，對高二生物教學中開展自主-合作學習進行實踐研究和探討，通過創設自主課堂、營造合作的課堂氛圍，激發學生的學習興趣，深入挖掘學生學習的積極性、主動性、創造性，努力實現由「要我學」到「我要學」的轉變，最後達到「我會學」的目標。 -
In the process of wollastonite fining, we can forge and then cool it to protect its crystal structure which is short acicular fiber. mechanochemical modification by jet mill is super to speedily mixed modification by stirring mix
硅灰石微粉碎過程中，為保護硅灰石的短纖維針狀結構，可在粉碎前對硅灰石進行煅燒空冷處理。 -
The characteristic of stirring equipment is used a shaking sieve to disperse the adding pure fe or fe203 powder and used a combined stirrer instead of a common paddle stirrer to improve the shear effect to mixing melts. the particularity of fabricating process is the step of holding stirring at a constant high temperature. both of which can improve the even distributing degree of reinforcement phase in pure al matrix
攪拌設備的特殊之處在於使用了振蕩篩分散加入粉末和更換組合式攪拌器來提高對混合熔體的剪切效果，工藝的特別之處在於一定溫度下的保溫攪拌過程，這二者均能提高強化相在純al基體中的均勻分佈。 -
Based on the analytical result of stirring kinetics, the maximal affecting factors to the size and distribution homogeneous degree of intermetallic al3fe reinforcement phase in al matrix during the stage of heat preservation stirring are studied, and some important parameters of stirring equipment and stirring process are ascertained, and the stirring processing is optimized
根據攪拌動力學分析的結果，研究了攪拌過程中對金屬間化合物al _ 3fe強化相尺寸大小和分佈均勻度的影響的因素，確定了攪拌設備和攪拌過程的幾個重要參數，並對攪拌工藝進行了優化設計。