  1. Some main results of testing research were as fellows : i. in the course of testing of leaching zinc dross, leaching zinc dross by sulfuric acid was researched and the effects on the leaching rate of the zinc dross were analyzed by author, the optimum conditions of leaching testing of zinc dross were determined as fellows : liquid - solid ratio 6 : 1, stirring ratio 250r / min, granularity 120 mesh, the soaking time 5h, the concentration of sulfuric acid of 30 %, and under these conditions, the rate of leaching zinc is above 92. 0 %. ii. in the course of testing of purification, on the basis of comprehending and comparing all present methods of the manganese - removal and iron - removal, the oxidizing method of manganese - removal in zinc sulfate solution using ammonium persulfate was put forward and the oxidizing method of iron - removal in zinc sulfate solution using the goethite process and oxidation - hydrolysis process was adopted

    研究的主要結果具體如下： 1 、研究了硫酸浸出鋅浮渣並分析了影響浸出率的各種因素，確定了浸出鋅浮渣的最佳條件為：液固比為6 ： 1 ，攪拌速度為250r min ，粒度為- 120目，酸浸時間為5 . 0h ，硫酸濃度30 ，鋅浮渣的浸出率大於92 . 0 ； 2 、在綜合和比較了目前除錳和除鐵的各種方法基礎上，提出了過硫酸銨氧化除錳方法和選擇了針鐵礦-氧化水解聯合法除鐵方法，並分析和討論了影響除錳率和除鐵率等各種因素，確定了除錳的條件為：溫度90 ， ph值5 . 4 ，反應時間3h ，過硫酸銨達到理論值的1 . 2倍，除錳率超過99 . 86 ；聯合法除鐵的條件為：氧化反應時間1 . 5小時、溫度控制在90 92 、 ph值5 . 2 5
  2. Yellow - brown powder. it is insoluble in water. it is soluble in sodium sulfide solution with a yellow - orange colour, slightly soluble in concentrated sulfuric acid

    黃棕色均勻粉末，不溶於水，溶於硫化鈉溶液中呈黃光橙色，微溶於濃硫酸。
  3. The test solution is placed in a test tube, and a small amount of alpha - naphthol added ; concentrated sulfuric acid is then trickled slowly down the side of the tube

    在試管中放入待檢測的溶液，加入少量的萘酚，接著把濃硫酸沿著試管壁緩緩滴入試管。
  4. Standard test method for weight loss mass loss of sheet steel during immersion in sulfuric acid solution

    薄鋼板在硫酸溶液浸漬過程中重量損失
  5. In this paper, concentrated sulfuric acid and titanium dioxide are used to prepare the tios04 solution that test later required under long time heat. the influences of reaction time and reaction temperature to yield of tioso4 are discussed. in the experiment of preparing tio2 powder, reaction temperature, ph values, material ratio, operation way, velocity of feed, calcining heat and time are researched by the principle of nucleation and growth in thermodynamics and kinetics

    在制備tio _ 2粉體實驗中，根據成核生長的熱力學和動力學原理，深入分析了沉澱反應時環境的溫度、 ph值、反應物配比、操作方式、加料速度等因素對ti （ oh ） _ 4粒度的影響，以及焙燒溫度和保溫時間等因素對制得的納米tio _ 2粉體性能的影響，得出了制備銳鈦型納米tio _ 2粉體的優化工藝條件。
  6. Corrosion behaviour of new pb - ca alloy in sulfuric acid solution

    新型鉛鈣合金在硫酸介質中的耐腐蝕性能研究
  7. Nanometer pore arrays alumina films were prepared by anodizing of highly pure aluminum foils in sulfuric and oxalic acid solution. the porous alumina layers were detached from the al substrate by using step - down voltage or solution method

    在草酸和硫酸溶液中，通過陽極氧化高純鋁片的方法制備了納米氧化鋁膜孔陣列，用階梯降壓法或溶解法將氧化鋁膜層和鋁基底分離。
  8. In view of process technology of potassium sulfate by neutralizing potassium hydrogen sulfate with ammonia, the effects of mole ratio of potassium chloride to sulfuric acid, reaction temperature and reaction time on preparation of middle product potassium hydrogen sulfate have been studied in aqueous solution

    針對硫酸氫鉀用氨中和制備硫酸鉀的生產工藝，研究了水溶液中氯化鉀和硫酸反應的原料配比、反應溫度、反應時間等因素對制得的中間產品硫酸氫鉀影響。
  9. Amino - group doping ci - c : h film showed good response to h ~ ion in strong sulfuric acid solution

    研究表明摻胺碳膜在濃強酸條件下對氫離于具有良好的選擇性響應。
  10. The effects of superfine powder on composite anodizing process of aluminum in sulfuric acid solution

    超細粉體對鋁在硫酸溶液中陽極氧化的影響
  11. Comparison of electrochemical property between ta amp; ta - 2. 5w alloy in sulfuric acid solution

    在硫酸溶液中的電化學性能比較
  12. Corrosion inhibion of amino acids for cold rolling steel in sulfuric acid solution

    氨基酸類有機物在硫酸介質中對鋼的緩蝕作用
  13. In o. 5 - ~ - 3mol / l sulfuric acid solution, the sensitivity exhibited linear response with slope of 66mviph

    在05 3mo卜l濃度的硫酸溶液中具有線性響應，其響應靈敏度為66my ph 。
  14. The process of leaching serpentine by waste sulfuric acid discharged from titanium dioxide industry and making products from the leaching solution

    鈦白廢酸浸出蛇紋石礦粉及產品制備研究