斷口金相研究 的英文怎麼說

中文拼音 [duànkǒujīnxiāngyánjiū]
斷口金相研究 英文
fractographic investigation
  • 斷 : Ⅰ動詞1 （分成段） break; snap 2 （斷絕;隔斷） break off; cut off; stop 3 （戒除） give up; abstai...
  • 口 : Ⅰ名詞1 （人或動物進飲食的器官; 嘴） mouth 2 （容器通外面的地方） mouth; rim 3 （出入通過的地方） ...
  • 金 : Ⅰ名詞1 （金屬） metals 2 （錢） money 3 （古時金屬制的打擊樂器） ancient metal percussion instrum...
  • 相 : 相Ⅰ名詞1 （相貌; 外貌） looks; appearance 2 （坐、立等的姿態） bearing; posture 3 [物理學] （相位...
  • 研 : 研同 「硯」
  • 究 : Ⅰ動詞（仔細推求; 追查） study carefully; go into; investigate Ⅱ副詞[書面語] （到底; 究竟） actually; really; after all
  • 金相 : metallographic金相分析 metallurgical analysis; 金相技術 metallographic technology; 金相檢驗 metal...
  • 研究 : 1. （探求） study; research 2. （考慮或商討） consider; discuss; deliberate
  1. Abstract : by means of metallographical examination and sem, the microstructure characteristics, macro - and microfractographs of the brittle broken wheel hull bolt of bj212 automobile have been studied. the results show that the thin - headed screw, with excessively deep carbonitriding layer and hardening layer, has less resistance to brittle fracture in the thin area of its head. at the root of the head connecting the stem, a tensile stress may emerge owing to the non - even quenching stress. those are the two reasons for low torque fracture of bolt

    文摘:藉助金相、掃描電鏡等手段對低扭矩脆斷的bj212汽車輪殼螺栓的金相組織特徵，宏觀和微觀斷口形貌等進行了研究，結果表明：這種頭部薄的螺栓，滲層和淬透層過深，使頭部薄區脆斷抗力降低，在頭部與桿的根部，由於淬火應力不均勻導致根部產生拉應力，均是導致螺栓低扭矩斷裂的原因。
  2. The mechanical parameters at high temperatures - reduction in area ( ra % ) and tensile strength ( o b ) are measured by means of gleeble - 2000 thermal simulating machine. fracture surfaces are analyzed by scanning electron microscopy and optical microscopy. the segregation of sn is also examined by auger electron spectroscopy

    通過測定試驗鋼種的高溫力學參數（斷面收縮率ra和抗拉強度_ b ） ，觀察金相顯微組織，分析掃描斷口形貌，測試第二相析出物和俄歇能譜試驗等方法，研究了殘留元素sn及冷卻速率對高溫力學性能的影響。
  3. The fractorgraphy analysis show that in the layer rich in w and mo, the feature of fracture is brittle fracture which follow the bordline of crystal. in sections rich in the felt metal, the feature of fracture is ductile fracture. in w - mo layer, the feature of fracture are brittle fracture and some ductile fracture

    斷口形貌特徵研究表明，富w區、富mo區主要為沿粒界脆性斷裂；粘結金屬發生韌性斷裂； w - mo混合區為顆粒的沿粒界脆性斷裂和粘結相的韌性斷裂的混合型斷裂；富ti區為典型的穿晶解理斷裂； mo - ti混合區以穿晶解理斷裂為主，顆粒邊界表現出準解理斷裂特徵。
  4. This paper sets about studying room - temperature fracture mechanisms of tial - based alloys of fully lamellar and duplex microstructures through the measurements of mechanical properties, in - situ observations of fracture surfaces and finite element method ( fem ) calculations, the measurement of macro - parameters, the observations of fracture surface and fem calculations on notch specimens ( 4pb ) and pre - crack specimens ( 3pb ), detailed observations of configuration changes at pre - crack tips in metallographic cross sections of specimens unloaded at various applied loads and fem calculation

    本文通過光滑試件機械性能的測定，原位拉伸試件的表面觀察、相應的斷口觀察及有限元計算；缺口彎曲宏觀參數的測定、斷口觀察及其有限元計算；裂紋彎曲參數的測定、裂紋卸載試樣剖面的觀察及其有限元模擬與計算研究了tial基合金全層組織和雙態組織的室溫斷裂機理。
  5. The paper have studied development law of paper and paperboard for global and some regions. the paper have studied the law of output, consumption, throughput changing with population gross and gdp of each country, regressing corresponding mathematics models, analyzing composing law of market request for several main series produces. the result indicates that paper industry requires much fund and technology and possesses characteristic of scale economy, competition makes industry concentrate more and more and paper industry is still traditional " rising sun industry "

    本文對全球及部分地區紙及紙板的發展變化規律進行了研究分析；研究了紙及紙板的生產量、消費量、生產能力與各國的人口總量和gdp變化而變化的規律；回歸出了相應的數學模型；分析了資金、技術密集型的造紙業產業，具有規模經濟性，競爭使工業集中度不斷提高；分析了幾大類主要產品系列的市場需求份額構成規律。
  6. Taking ti alloy tc11 electron beam welded work - piece as research object, which is the conventional material of aero engine compressor blisc, the fatigue damage evolution law of fatigue damage action in the area of welded joint based on damage mechanics theory is analysed, and fatigue damage model, which macro - parameter and micro - damage characteristics are related, with fractal geometry - a new conception of modern mathematics is set up in this paper. it tries to research the measuring method of fatigue fracture fractal dimension and the relationship of fractal damage variable with fatigue life. it also sets up the welded joint fatigue damage fractal evolution equation

    本課題以航空發動機壓氣機葉盤常用材料鈦合金（ tc11 ）電子束焊構件為研究對象，對焊接接頭的疲勞破壞行為，基於損傷力學理論分析其疲勞損傷演化規律，應用現代數學的新概念? ?分形幾何學理論，建立宏觀參量與細觀損傷特徵相聯系的疲勞損傷模型，研究疲勞斷口分維數測量方法以及分形損傷變量與疲勞壽命之間的關系，建立焊接接頭疲勞損傷分形演化方程。