Firstly, the mechanism of the preparation of superfine quartz powder with ball mill is studied in this article, based on nature of quartz material, griffith ' s strength theory and the crush theory of planetary ball mill. the problem of granulation during the process of the preparation of superfine quartz powder is studied minutely. and proposed increasing dispersant and disperser medium to restrain granulation, and dispersing use ultrasonic after milled
首先，本文結合石英材料的基本物性，以格里菲斯強度理論和行星式球磨機的粉碎原理為基礎，研究了球磨法制備超細石英粉體的機理，同時對粉石英制備過程中的團聚問題及其控製作了細致的研究，提出粉磨過程中增加分散劑和分散介質來抑制團聚，粉磨后採用超聲法進行分散，並確定了最佳分散劑、分散介質的用量和最佳超聲分散時間。Based on the experimental results and the correlative chemistry theory, the phases formed in the process and its influenceable factors were studied. the significant results were enumerated as follows : as for the mn - h2o system, 5g pure mn scraps ( 99. 5 %, - 200mesh ) and distilled water served as the starting materials were milled by high energy ball miller together with 200g steel balls as the milling medium. the experiments were conducted with the rotation speed of 380rpm. - mn3o4 nanopowders were fabricated after milling some time and would experienced phase transformations if continue to be milled. the reaction would be accelerated if a little of hcl or mnso4 was added while be decelerated if. a little of naoh was added. the - mn3o4 phase with particl size between 20 ~ 100 nanometer was obtained after milling 1. 5h when trace hcl was added. the oxygen added to the ball tin has little effect on the reaction
主要實驗結果如下: （ 1 ）對于mn - h2o系，通過高能行星式球磨機，在50ml蒸餾水中球磨5gmn粉末，球料比為40 : 1 ，轉速為380rpm ，球磨一定時間后獲得了納米級單相- mn3o4 。隨著球磨時間的延長，生成的- mn3o4會繼續被氧化或發生晶型轉變。加入微量hcl或mnso4會明顯加快mn的反應，加入hcl后，球磨1 . 5h后即獲得粒徑為20 100nm的單相- mn3o4粉末;加入微量的naoh會抑制mn反應生成- mn3o4 。
分享友人