Equal channel angular processing of the pearlitic steel ( 0. 65 wt. % c ) was successfully carried out at 650 with route c in this study, obtaining a total equivalent true strain ~ 5. the microstructure evolution of pearlitic steel in ecap was investigated by means of transmission electron microscope and scanning electron microscope. the main results are as the following : 1
本研究成功地實現了c方式650珠光
體鋼65mnecap變形,累積等效真應變達到5 。並用透射電鏡、掃描電鏡研究了珠光
體組織的演變特點和
滲碳體的變形。主要結果如下: 1
-
Study on gas carburizing technique of instillation with kerosene - carbinol
甲醇滴注式氣
體滲碳工藝的研究
-
New process of drop feed gas carburizing with high rate
滴注式快速氣
體滲碳新技術
-
Gear pre - oxidation gas carburizing at low temperatrue
齒輪預氧化低溫氣
體滲碳
-
Study and application of pulse gas carburizing technology
脈沖式氣
體滲碳技術研究和應用
-
Cementite graphitization in fe - 2. 3 si - 3. 7c alloy
合金中
滲碳體的石墨化
-
Study on cementite graphitization in cast iron at high temperature
鑄鐵中
滲碳體高溫石墨化研究
-
The results indicated that low graphite spheroidization rate and free cementite were the main causes of poor mechanical property
試驗結果表明,控制
碳當量和球化劑加入量,採用瞬時孕育等可提高球化率;採用預熱砂型等可減少
滲碳體。
-
Excessive imperfections even sub - grained boundaries may be introduced in cementite. this makes the accelerating dissolution and spheroidization of cementite easy. 5
由於
滲碳體的強烈塑性變形,在其內部導入了大量的晶
體缺陷甚至亞晶界。
-
The main causes which lead to tensile abnormal fracture of swrh82b steel rods are the network cementite sod the big brittle inclusion
摘要通過對swrh82b盤條的拉伸斷口進行分析,認為網狀
滲碳體和大顆粒脆性夾雜物等缺陷是引起斷口異常的主要原因。
-
3. on the present deformation condition, the cementite in pearlitic steel has more severe plastic deformation capability t - he max shear strain up to 1. 9. 4
C方式ecap變形條件使珠光
體鋼65mn中的
滲碳體可以表現出很強的塑性變形能力? ?觀察到的最大切變形達到1 . 9的等效真應變。
-
It is known that a pearlitic material is composed of numerous pearlitic colonies with randomly distributed orientations, and in each colony there are many parallel ferrite and cementite laminas arranged alternatively
珠光
體材料為兩相材料,它由大量隨機取向的珠光
體團組成,每一珠光
體團由包含大量鐵素
體片和
滲碳體片交互疊合而成。
-
The strength of extension of low carbon ductile cast iron can reach 750mpa in casting state, the impact ductility can reach 20j / cm2. the diameter of graphite nodule is 5 - 20 ( am, the base body is consisted of pearlite -
低
碳球鐵在鑄態下的抗拉強度可達750mpa ,沖擊韌性可達20j cm ~ 2 ,其中石墨球直徑在5 20 m ,基
體以珠光
體為主,有少量的鐵素
體與
滲碳體。
-
In ecap route c, in order to accommodate the severe shear deformation the deformation form of lamellae cementite in pearlitic steel include periodical bending, periodical shearing and shearing fracture etc
在c方式ecap變形中,珠光
體鋼65mn中的
滲碳體以周期性的彎曲變形,周期性的剪切變形,剪切斷裂等形式協調ecap的強烈塑性變形。
-
The microstructure of lamellae pearlite has evolved ultrafine cementite particles throughout the ferrite matrix uniformly after five passes. the ferrite matrix is homogeneous grains, average grain size is - 0. 3 m. 2
變形五道次后,片層狀的珠光
體組織演變成了超細的
滲碳體顆粒均勻分佈於鐵素
體基
體的組織,鐵素
體基
體為均勻的等軸晶,平均晶粒大小為0 . 3 m 。
-
The main results are as the following : ( 1 ) the microstructure of lamellae pearlite has evolved ultrafine cementite particles throughout the ferrite matrix uniformly after four passes. the ferrite matrix is homogeneous grains, and average grain size is - 0. 3um
主要結果如下: ( 1 ) ecap變形四道次后,片層狀的珠光
體組織演變為了超細的
滲碳體顆粒均勻分佈於亞微晶鐵素
體基
體的組織。
-
The fracture and spheroidization of cementite shows obvious anisotropy. there are two possible mechanism about spheroidization of cementite : the fracture cementite lamellae grows up non - uniformly and the fine spherical cementite particles grows up as the core
滲碳體的破碎和球化表現出明顯的各向異性。
滲碳體的球化可能以兩種機制進行:破碎
滲碳體片的非均勻長大和細小球狀
滲碳體顆粒的形核長大。
-
In order to avoid eutectic carbide, improve nodularity, increase nodule count and increase mechanical properties, three times of inoculations were adopted in the centrifugally cast nodular iron pipes production : a ) inoculation in ladle ; 2 ) pouring stream inoculation ; 3 ) in - mold inoculation
摘要在離心鑄造球墨鑄鐵管生產中,為防止共晶
滲碳體析出,改善球化,增加石墨球數,提高力學性能,採用了三次孕育: ( 1 )包內孕育; ( 2 )澆注時隨流孕育; ( 3 )型內孕育。
-
On the surface of annealed 45 steel, as the pearlite in it contains cementite phase and has high crystal boundary density, the nucleation and growth of deposits prefer to occur at the pearlite at the beginning during depositioa the coating exists in form of nano - polycrystal layers composed by gathering of nano - sized crystals
在退火態45鋼表面,由於珠光
體組織中含有
滲碳體相且具有比較高的晶界密度,因而在沉積初期鍍層優先在此處形核和生長;鍍層在基
體表面是以納米尺度的晶粒聚集在一起形成的聚晶
體形式存在的。
-
( 4 ) which deformation behavior of cementite lamellae in pearlite colonies is closely related to the stress state of cementite which significantly depends on cementite thickness and orientation, especially on cementite thickness. ( 5 ) the lamellar cementite undergoes partial dissolution on the present deformation. the thermodynamical destability of cementite is attributed to a large number of defect in cementite introduced by severe plastic deformation providing evidence for cementite dissolution
而滲碳體的應力狀態主要是與滲碳體的片層厚度和取向密切相關的,其中滲碳體的厚度起決定性作用; ( 5 )本實驗變形條件下,滲碳體出現了部分溶解的現象,這是由於強烈塑性變形而在滲碳體中引入大量的缺陷導致其處于高能不穩定狀態從而促使了滲碳體溶解。