The design and machining technology process of its molding part including the front moulding plate 、 front mould kernel 、 back mould plate 、 back mould kernel 、 back mould set piece 、 incline guide pin 、 slide steatite etc, and the choice and calculation of technology parameters of the impotent part, the design process of extrusion outfit, inject system and other makeup are specified in detail ; test and product have been introduced
詳細地敘述了模具成型零件包括前模板、前模仁、后模板、后模仁、后模鑲件、斜導柱、滑塊等的設計與加工工藝過程,重要零件的工藝參數的選擇與計算,推出機構與澆注系統以及其它結構的設計過程,並對試模與產品缺陷作了介紹。It can typecast wet or dry shape sand, improve the cast quality. in a word, it is a fine quality cast sand adhesives, which has the character of dilatability, cohesiveness, floatability. and gel dispersivity, repeated use
可以澆注濕態和干態型砂,改善鑄件質量,並有良好的復用性,是一種優質的膨脹劑,黏合劑,懸浮性和膠體分散性的鑄造型砂粘結劑。The wax setting and casting process is complicate process with a series of procedures, including model creating, spruing and construction, rubber mold vulcanization and cutting, wax models injection, stone setting in wax model, wax tree creating, investing, investment mold burning - out, metal melting and pouring, casting cooling and divesting, etc
蠟鑲鑄造是一個多工序的復雜工藝過程,包括母版製作、開設水線、製作橡膠模、製作蠟模、寶石鑲嵌到蠟模、種蠟樹、製作石膏型、石膏型脫蠟焙燒、金屬熔煉澆注、飾件冷卻清理等。Compounds for use in cable accessories ; casting resinous compounds before cure and in the cured state vde specification
電纜附件用的化合物.在固化前和固化狀態時的澆注樹脂The calculation model about the runner system of the downsprue of metal - powder injection molding ( mim ) and the finite element analysis of injection parts molding have been established. the analogue analysis of the molding process of metal - powder injection molding has been made and draw some correlative conclusion
基於連續介質理論和有限元理論,建立了金屬粉末注射成形澆注系統的流道和注射件成形有限元分析計算模型,並對金屬粉末注射成形過程進行了模擬分析,得出了相關的結論。The experiments of high speed milling of titanium alloy were conducted under different cooling and lubricating modes, i. e. dry milling, flood coolant, oil mist with nitrogen gas, cryogenic nitrogen gas jet, and cryogenic nitrogen gas jet with minimal quantities of lubricant
在干銑削、澆注切削液、常溫氮氣油霧、低溫氮氣射流和低溫氮氣射流結合微量潤滑等冷卻潤滑條件下進行了鈦合金的高速銑削對比試驗。Low temperature flexible, easily pourable rtv silicone sealant / encapsulant, can be used with a wide variety of curing agents, thus varying pot life, cure time, mix ratios and cure conditions
低溫彈性,易澆注的rtv密封硅膠,可與多種固化劑使用,可改變灌膠時間、固化時間、混合比率以及固化條件。The research showed that basin is the more important feeding resource than runner in runner type gating system in lost wax casting. therefore, on the basis of the basin as feeding resource, runner and ingate as feeding channel, a new design method for runner type pouring and feeding system in investment casting was developed. the corresponding feeding mathematical pattern and allowable total weight listed for casting cluster with different basin were established after analyzing the practical feeding of basin and the calculating process for design was described in detail
在熔模鑄造橫澆道型澆注系統中,澆口杯是比橫澆道更為重要的補縮源,因此在立足於澆口杯為補縮源、橫澆道和內澆道為澆注補縮通道的基礎上,開發了適用於熔模鑄造橫澆道型澆注補縮系統設計的新設計方法,在詳細分析了澆口杯的實際補縮情況后,建立了相應的數學補縮模式和不同澆口杯的鑄件組許用鑄件總質量表,並具體介紹了設計計算過程。Used to concrete seam and arbitrarily shape seam in component. in the condition of the expanding being favorable limited, attain satisfied stop - water effect and manage the concrete interstitial leaking. at the same time, it can be also used to shipping and engine etcindustrial equipment
適用於現場澆注的混凝土施工縫和嵌入構件任意形狀的接縫內,在其膨脹受到良好限制的條件下達到滿意的止水效果,治理混凝土裂縫的漏水,同時也用於船舶、機車等工業設備的防水密封。Road safety barriers. cast in place concrete separators and walls. special steel accessories
道路安全隔欄.現場澆注混凝土隔離墩.專用鋼制附件Road safety barriers. in - situ concrete partition walls and low walls. implantation conditions
道路安全隔欄.現場澆注混凝土隔離墩和矮墻.安裝條件The effective cost dust content of molding sand should be determined according to time factors such as the quality of the coal dust, casting size and thickness, pouring temperature, lacing sand or unit sand, and so on
決定型砂中的有效煤粉含量應根據煤粉質量的優劣、鑄件大小和厚薄,澆注溫度、面砂或單一砂等因素。Based on the mechanism of hot cracking formation of castings, the cracking defects of furnace door frame castings was analyzed, and found that the main reasons causing cracking are as follows : construction of the casting was not reasonable, gating system was not proper, and pouring temperature was too high
摘要根據鑄件產生熱裂紋的機理,對爐門框裂紋缺陷進行分析,找到了裂紋產生的主要原因是鑄件結構和澆注系統不合理,以及澆注溫度過高。The composite material, which is used to make muller plow of sand mill, is prepared by the method of cast - infiltration and the technology parameters for making composite material is optimized. then the effects of the matrix component on composite layer also are disccused
通過試驗對利用鑄滲法在鑄件表面獲得一定厚度復合材料層的形成機理進行了理論分析,優選了利用鑄滲法在鑄件表面制備復合材料的工藝參數(澆注溫度、合金膏塊的厚度、澆注位置等) 。During the temperature fields, the results indicate that the processing parameters such as the extrusion velocity, casting temperature, perform preheating temperature, die preheating temperature and so on are important for the temperature fields besides the dwell time. they are must be in concordance each other to the deforming zone is in the quasi - solid state, and the stable semi - solid extrusion is implemented. during the deforming fields, the hyperbolic sine thermo - rigid - viscoplastic fem model is selected according to the forming feature of the process, and the variations of the stress - strain fields are studied
在溫度場的模擬中,模擬結果表明,保壓時間是影響製件成形質量的關鍵因素之一,擠壓速度、液態金屬澆注溫度、預制體預熱溫度和模具預熱溫度等工藝參數對溫度場的影響也很大,需進行參數之間的協調,只有當變形區內部始終維持準固態時,才能實現穩定的液-固擠壓成形過程;在變形場的模擬中,根據液態浸滲擠壓的成形特徵,選用了雙曲正弦剛-粘塑性有限元計算模型,研究了變形過程中應力應變場的變化規律,研究了模角對變形和金屬流動的影響及變形力的變化過程和其影響因素。Liquid - solid extrusion of composite material is a new kind of metal forming process, which has been developed in recent years with a promising practical application prospect for its simple working procedure, low cost and good workpiece performance. through a lot of experiments, the optimization and chosing method of key process parameters ( pouring temperature, mold warm - up temperature, impregnating pressure, impregnating time ) has been mastered. under the precondition of appropriate chosing these parameters, the effective control of extrusion velocity is the key of mading good workpiece. but the control of extrusion velocity remains a handwork, and it is heavily affected by such uncertainties as a handler ' s knowledge and skill about the process. in order to solve the problem, the automatic control of the extrusion velocity is studied, and a computer control system is also designed under existing condition
通過大量實驗,已掌握了關鍵工藝參數(熔液澆注溫度、擠壓模預熱溫度、浸漬時間、浸漬力)的優化選取方法。在合理選取關鍵工藝參數的前提下,擠壓速度的控制是成形出質量良好製件的關鍵。但是,目前對于擠壓速度的控制仍停留在手動控制階段,利用該工藝制備管、棒材製件的成功與否受操作者對該工藝及其設備的經驗及熟練程度等不確定因素影響很大。Uses : packing of high tension electrical equipment, expoxy pouring packing material, plastic pacing material, dry type transformer, high tension mutual inductance equipment, insulator
產品用途:高壓電器件的絕緣澆注料、環氧灌封料、塑封料、包封料、絕緣子、乾式變壓器、高壓互感器、填料等。Wear resistant layer of cylinder and double - layer liner in catalyst creaking apparatus ( without or with tortoiseshell net can be used ), inner liner of carbon monoxide exhaust - heat boiler, pouring at site for furnace roof with high temperature of heating furnace of steel rolling, different forging furnace, resistance furnace, the prefabricated parts can also be made
催化裂化裝置中的筒體耐磨層及雙層襯里, (無龜甲網和有龜甲網均可採用)及一氧化碳余熱鍋爐的內襯,也適用於軋鋼加熱爐、各種煅造爐、電阻爐的爐頂、爐墻、爐底高溫部位的現場澆注,可製成預制構件。Steel casting : 20 tons arc - furnace steelmaking, 40tlf refiner furnace ; the max elevating capacity 125t ; the max casting products 80t, dimension of casting products length, width, high 8. 54. 53m, spun casting min outer diameter, min wall thickness, max length 1000154000mm ; various specification steel strands
鑄鋼: 20t電弧煉鋼爐40tlf精煉爐最大起重能力125t最大鑄鋼件80t鑄鋼件最大尺寸長寬高8 . 54 . 53m離心澆注最大外徑最小壁厚最大長度1000154000mm各種規格連鑄坯。Abstract : introduced is the experience in replacing atmosperic riser with thermal - isolation riser and improving pouring system to eliminate shrinkages
文摘:介紹了用保溫冒口代替大氣壓力冒口,改進澆注系統解決鑄件縮孔問題的經驗。分享友人