灰漿配比 的英文怎麼說
中文拼音 [huījiāngpèibǐ]
灰漿配比
英文
mortar mix ratio-
Through experiment on the influence factor of calcic - mortar ' s performance, we find out the best cement contrast minute stone for compounding, strength of cement, configuation craft, maintenance system and minute stone cement intensity grading
摘要通過對鈣性黏結砂漿性能影響因素的試驗研究，找出了配製鈣性黏結砂漿的最佳灰砂比、水泥強度等級、配製工藝、養護制度為和沙子級配。Anti penetration of hardened mortar can reach 10 - 7cm / s. adopting sulfate - aluminum cement, phosphorus slag, flying ash, yellow slag and ect raw materials, the optimized mixture program of dmm is a3b3c2 ( cement 480 m2 / kg, phosphorus slag352 m2 / kg, activated agent 3 % ), 28 strength is low, due to cement alkality, resulting in activity of phosphorus slag and flying ash small
採用硫鋁酸鹽水泥，磷渣、粉煤灰、黃砂等原武漢理工大學碩士學位論文料配製抗滲干拌砂漿最優配料方案為: a3b3c2 （水泥比表面積4som ， / kg ，磷渣比表面積352mz / kg ，激發劑3 % ） 。For accumulating heat from piping and making as even the temperatures in various spaces betwiin pipes an possible, gravel foundation is first laid, mortar is mixed fully by mixing ratio of 1 : 2, the floor is finished level and then perfect curig in damp condition is carried out
為保證管路間蓄熱和溫度均勻應鋪下砂礫層后進行配比為1 ： 2的灰漿完成處理，不僅要保證地板水平，還要在濕潤狀態下自然乾燥，使得到徹底的養護，人為的養護會導致地板雛裂，應予以注意。In the paper the effects of the made parameters, the main materials and environmental conditions on plastic shrinkage cracking were investigated. it can be concluded as following : 1 ) there was a critical w / c ratio of maximum plastic shrinkage cracking between lower and higher w / c ratio of concrete mixtures made with the same cement content per cubic meter, concretes with lower or higher w / c ratio being less prone to plastic shrinkage cracking and the w / c critical ratio critical of maximum plastic shrinkage cracking being about 0. 5
本文研究了配製參數、主要原材料以及環境條件對新拌混凝土塑性收縮裂縫的影響，結果表明： 1 ）單方混凝土水泥用量一定時，較低水灰比和較高水灰比對應的混凝土拌合物不易開裂，而中間某一臨界水灰比對應的混凝土拌合物開裂較嚴重，這一臨界水灰比為0 . 5 ；單方混凝土水用量或水泥漿量一定時，混凝土拌合物的塑性開裂趨勢與上述情況相似，但臨界水灰比分別為0 . 45 - 0 . 4和0 . 4 。The proportions and performances of plastic concrete of some cut - off walls at home and abroad, the proportion of self - congealing slurry used in the cut - off wall of third stage cofferdam of three gorges project, mechanics properties of expansive soil slurry and harden clay mortar, and proportions of hardened slurry are introduced
列舉了國內外部分防滲墻工程塑性混凝土基本配合比及性能參數；國內自主研發的自凝灰漿墻體材料及應用於三峽工程三期圍堰防滲墻的配合比；固化灰粘土漿、膨潤土漿的物理力學性能及固化灰漿採用不同制攪方法時的配合比。The grouting liquid with this stability agent has many advantages such as the good volume stability, low dialysis ratio, high strength of cement rock less dry - shrink and convenient construction etc. when the water - cement ratio is 0. 6 or 0. 8, the 28d strength of cement - rock is 210 % and 179 % of the bentonite cement - rock under standard maintain
該穩定劑配製的水泥漿具有體積穩定性好、不析水、結石強度高、不幹縮、施工方便等優點。如水灰比0 . 6 、 0 . 8時，標準養護條件下28d強度分別較膨潤土水泥漿結石提高100和80以上， 20水中養護28d強度則提高30左右。By using wind - blown soil, fly ash, clay, a small amount of cement and addition agent as raw materials in this paper, the optimum dispensation formula and spreading theory about filling and pre - grouting of composite filling material were studied to have important practical significance to large filling and pre - grouting project
本文利用風積土、粉煤灰、粘土、少量水泥和其它外加劑為原材料，研究復合充填注漿材料的最佳配比及其擴散充填注漿理論，對于大型充填注漿工程具有重要的現實意義。Based on analyzing and determining basic characteristics of every raw material, the dispensation tests had been performed about clay - cement paste, fly ash - cement paste, fly ash - clay - cement paste and wind - blown soil - clay - cement paste, and their performance figures were tested systematically and obtained perfectly so that a reasonable dispensation formula was get to be used in filling project
在分析測試各種原材料基本性能的基礎上，按正交試驗設計方法，完成了粘土?水泥漿、粉煤灰?水泥漿、粉煤灰?粘土?水泥漿和風積土?粘土?水泥漿的配比試驗，並對其各項性能指標進行了系統的測試和分析，得到了可供工程應用的合理配方。分享友人