熱疲勞 的英文怎麼說
中文拼音 [rèpíláo]
熱疲勞
英文
heat fatigue; thermal fatigue熱疲勞斷裂 thermal fatigue fracture-
For the manifold of sedan engine, the hest thermal fatigue properties can be obtained by keeping the percent of vermicular graphite at about 50 %, therefore it shouldn ' t he considered that the lowest e. g. percent limit of 50 % specified in chinese vermicular iron standard is too lower, and it is also not proper to take the v. g. percent as the basis for judging the level of production technology
摘要對轎車發動機排氣歧管而言,蠕化率控制在50 %左右可以獲得最佳的抗熱疲勞性能,因此不能認為我國的蠕鐵標準中規定的蠕化率高於50 %的要求偏低了,也不能把蠕化率的高低作為衡量工藝水平的依據。Thermal fatigue behavior of niobium microalloyed h13 steel
13鋼的熱疲勞行為The thermal properties of medium silicon - molybdenum vermicular iron are about three times of that of normal vermicular iron, so it is an ideal material for producing manifold
中硅鉬蠕鐵的抗熱疲勞性能為普通蠕鐵的3倍,因而是製造排氣歧管的理想材料。Flame tube in aircraft engine undergoes high temperature and high speed airflow washing. a hypothesis was suggested, which takes the transient heat transferring as the main reason to the cracking and damage on flame tube. finite element method was adopted to simulate the thermal fatigue and the hypothesis was reproduced
發動機火焰筒的熱疲勞損傷是導致火焰筒失效的主要原因,本文提出了一種火焰筒熱疲勞損傷假設,認為火焰筒熱疲勞損傷不是由於發動機的運行和停車時冷熱溫度循環造成的,而是發動機啟動時瞬態溫度傳導過程中材料循環塑性變形的結果,利用該假設結合有限元計算模擬了火焰筒產生疲勞損傷的原因。Thermal fatigue testing method for hot die steel
熱作模具鋼熱疲勞試驗方法Method of thermal fatigue testing for metallic materials
金屬材料的熱疲勞試驗方法Effect of plasma nitrided compound layer on thermal fatigue behavior of h13 steel
13鋼熱疲勞性能的影響Ergonomics - evaluation of thermal strain by physiological measurements
人類工程學.熱疲勞的生理學測量評價A testing study on thermal fatigue property of building up casting pipe model
堆焊鑄管模熱疲勞性能試驗研究Study on structure and property and thermal fatigue behavior of sdh13 steel
13鋼的組織性能及熱疲勞行為研究Thermal fatigue testing machine
熱疲勞試驗機Acted a pulse current to prevent the thermal fatigue crack subcritical extending
脈沖放電截止熱疲勞裂紋的亞臨界擴展The study of thermal fatigue resistance of spheroidal graphite cast iron and cast steel
球鐵與鑄鋼的抗熱疲勞性能的比較Thermal fatigue fracture
熱疲勞斷裂( 2 ) it is found that distilled water as lubricant can markedly reduce the accumulation of friction heat and temperature rise on the frictional surfaces of polymer. so the heat fatigue and adhesive wear decrease. moreover, a lubricating film forms on the interface between the counterpart and polymer when distilled water acts as polar lubricant
( 2 )潤滑劑水的存在,可大幅度降低聚合物磨損表面的摩擦熱積累及溫升,從而減少了基體的熱疲勞磨損和粘著磨損,同時,水作為一種極性潤滑劑,在摩擦界面上能形成一層潤滑膜,對摩擦表面起了一定的隔離作用。Abstract : in the light of two common failure modes in use, i. e. thermal wear and hot fatigue crack, this paper analyzes the reasons and puts forward the measures to be taken for improving the life of forging die
文摘:針對鍛模在使用過程中常見的兩種失效形式,即熱磨損和熱疲勞裂紋,分析了其產生的原因,並提出了為提高鍛模壽命而應採取的措施。7 the investigation of the thermoeconomic performance of an existing facility used for thermal fatigue experiments of aircraft canopy reveals the possibility and practicability of taking measures to improve it significantly. a piping system with alternative variation of flow temperature exists in this facility
對一現行的飛機座艙蓋熱疲勞試驗系統? ?即流體溫度升降交替變化的管路系統,進行了熱經濟行為的研究,揭示出它具有潛在與可行的重大改進方向和途徑。The results indicated that the microstructure, mechanical properties, oxidation resistance, growth resistance and thermal fatigue resistance were improved obviously
結果表明,顯微組織、抗氧化、抗生長及熱疲勞抗力等性能,均有顯著的改善和提高。Heat fatigue cracking
熱疲勞裂痕Abstract : the process of thermal fatigue crack propagation on the surface of steel bonded carbide gjw35 under the action of thermal stress has been observed
文摘:觀察了在熱應力作用下gjw35鋼結硬質合金表面熱疲勞裂紋擴展過程。分享友人