  1. Laser marking is a kind of technique using heat effect of laser to ablate meterials on object surface so as to leave over permanent press

    激光打標是利用激光的熱效應燒蝕掉物體表面材料從而留下永久標記的技術。
  2. The charter i introduced the schematics of the experimental setup, the model of pulsed laser ablating solid target ( s - n model ) and the subplantation model for film growing proposed by y. lifshitz

    第一章簡要介紹了實驗裝置、激光燒蝕固體靶的s - n模型和y . lifshitz提出的次表面生長模式。
  3. At last, the effect on the outer ballistic trajectory characteristic after the ablation of hypersonic projectile wing has been analyzed

    最後，初步分析了高超聲速彈翼表面發生燒蝕后對其外彈道特性的影響。
  4. Therefore, the surface roughening and smoothing can be adjusted by controlling the hipib irradiation parameters

    通過優化輻照參數可控制hipib輻照純金屬ti燒蝕表面的粗糙化和光滑化。
  5. Experience shows that the positive electrode always burns away more rapidly than the negative.

    經驗表明，正電極比負電極燒蝕得快得多。
  6. The interior temperature distribution and ablation model of projectile wing is established from general transmitting heat differential equation ; at the same time, the heat flow density and pressure distribution model of projectile wing is also established

    從一般形式的導熱微分方程出發，逐步建立了彈翼內部溫度分佈和燒蝕的數學計算模型；與此同時，建立了彈翼表面的熱流密度和壓力分佈的數學模型。
  7. The special system is able to inspect and analyse the state of ablation, disfigurement of machine, bug of material and the degree of abrasion on the inner surface, which is an important instrument for make certain on remain life and shooting security of artillery body

    該專用系統可對火炮身管膛內表面的燒蝕狀況、機械損傷、材質缺陷及磨損程度等疵病進行檢測與分析，是確定身管剩餘壽命及評價射擊安全性的重要手段。
  8. The conclusion obtained from experimental result showed that particle concentration is an important factor on inhibitor ablation

    試驗結果表明：粒子聚集濃度是絕熱層燒蝕的重要影響因素。
  9. The antiablation of silicone rubber liner can be improved both by changing the structure of unvulcanized rubber and adding antiablative fillers, and the bond strength between propellant charge and the liner would be increased largely by coating the primer liquid on the charge surface

    硅橡膠包覆層中填料的粒徑對硅橡膠的補強效果十分重要；可從改變生膠結構、添加耐燒蝕填料兩方面來改善硅橡膠包覆層的耐燒蝕性；在推進劑藥柱表面上塗覆底塗液可以大幅提高硅橡膠包覆層與推進劑的粘接強度。
  10. The expressive model of the characteristic value of the gun bore erosion and wear

    火炮身管內膛燒蝕磨損特徵量表述模型
  11. The new requirements for applications in material surface engineering urge a new type of hipib apparatus, for instance, the generation of medium - power - density ion beam, high - stability ion beams and long - lifetime ion source etc. therefore, characterization of high power ion diode - magnetically insulated ion diode ( mid ), the key issue for the technique development, is considered in this dissertation. the investigations of hipib generation and its mechanisms have been carried out in a temp - 6 hipib apparatus, in order to optimize the configuration of ion diode and its ion beam parameters for materials surface treatments

    針對強流脈沖離子束（ hipib ）技術研發的關鍵環節?高功率離子二極體（磁絕緣離子二極體）的工作特性，在temp - 6型hipib裝置上開展了hipib產生及其形成機理的實驗研究，確定了優化的離子二極體結構和輻照工藝參數；通過hipib輻照金屬材料燒蝕行為的系統研究，揭示了燒蝕表面形貌的形成規律，為徹底弄清hipib與材料相互作用機理提供了實驗依據。
  12. The scar on the surface of steel part of the projectile shows that different reaction violence have happened, though the impact velocities of projectile are almost the same in these tests

    從數發試驗回收的鋼托的表面燒蝕痕跡，可判斷相近撞擊速度下反應的烈度不盡相同。
  13. The results of static firing test shows that the thermal erosion properties, mechanical properties, tand thermal shock resistance of the c / sic composites can meet a demand for thermal - structure application in the area of aerospace such as liquid rocket thruster

    試驗發動機地面熱試車結果表明，該c / sic復合材料的力學性能、燒蝕性能和熱震性能優良，可滿足宇航工程中諸如液體火箭發動機推力室等對熱結構材料的使用性能要求。
  14. The simulations results show that the spoiler is available to make the fuel and the oxidizer coming from the former to stay in the cavity for a long time, to let the fuel and oxidizer mix and burn completely. since there is a high temperature zone forming by vortex in the middle of the motor, it required a restricted thermal protection. the plate with holes decreased the vortex function in the cavity, which could not promote the combustion efficiency, but to decrease temperature in the cavity and be benefit to thermal protection of the wall

    計算結果分析表明:擾流板可以使燃料和氧化劑在擾流腔內的滯留時間加長，促進燃料與氧化劑的摻混燃燒，提高燃燒效率，但由於渦流在發動機的中間部位形成了高溫燃燒區域，致使局部燃料和絕熱層燒蝕速率增大，加大了熱防護的難度;孔板結構減弱了擾流腔內迴流區的漩流作用，不能增加推進劑燃燒效率，但可以使擾流腔內的溫度降低，給壁面熱防護帶來好處。
  15. The system can scan stereoscopicly the internal tube of the measured object, the aim is to test the internal flaws of the inspected object, such as crazing, rust - eaten and dropping of electroplated coating

    該系統對被檢測物體內表面進行立體掃描，可獲得被檢測物體內壁疵病信息，包括燒蝕面積，裂紋深度及電鍍層脫落面積等。
  16. The missile with its radome is at high temperature during the entrance. due to aerodynamics heating process, the high temperature cause air ionization and ablation of the radome, so the radome is at unsymmetrical heat environment, its electrical properties vary with different parts of the radome

    導彈在再入過程中，由於空氣動力加熱效應，引起空氣電離和天線罩表面被燒蝕，因此，天線罩處于不對稱熱環境中，它各部分的介電性能不同。
  17. By observing the macrocosmic and microcosmic state of the test specimens, the ablation pattern of inhibitor was put forward and ablation mechanism was analyzed. the critical average particle diameter that influenced inhibitor ablation was obtained. the time - dependent ablation expression associated particle concentration and angle was achieved through analyzing their variation alone with the change of specimen figure

    （ 4 ）通過對試驗后絕熱材料試件的表觀和微觀狀態分析，提出了過載條件下絕熱層的燒蝕模式，並分析了其燒蝕機理，獲得了試驗條件下影響絕熱層燒蝕的平均顆粒直徑。
  18. It is found that the ablated surface morphologies for both the ti samples of different roughness have a similar change trend from roughening to smoothing with increasing the shot number, where the surface roughening is relatively weaker at lower ion current density

    通過輻照不同原始粗糙度的純金屬ti發現，隨著輻照次數的增加，燒蝕表面形貌均發生表面粗糙化向光滑化的轉變。離子束流密度較低時，輻照表面的粗糙化程度較弱。
  19. The experimental results show that dlc film could be deposited on silicon substrate rapidly and uniformly in a large area by means of ablated plasma jet generating on the target surface during hipib irradiation, the instantaneous deposition rate is as high as imm / s and the uniform deposition area covered 40 - 50 cm2

    實驗結果表明，利用hipib燒蝕等離子體在si基體上可以實現快速、大面積、均勻地沉積類金剛石薄膜，薄膜的瞬時沉積速率達到1mm s ，均勻薄膜的面積達到40 ? 50cm ~ 2 。
  20. Adopting the short circuit electric current of to formate the test prove that this contact turn on and cut off performance. according to ablation situation of contact surface after testing, have analysed that coil type double - pole amf influences electric arc

    採用短路電流合成試驗驗證了這種觸頭的開斷性能，根據實驗后觸頭表面的燒蝕情況，分析了線圈式兩極縱向磁場在大電流時對電弧特性的影響。