  1. In general, smaller grain size and greater angularity tend to increase the porosity while an increase in range of particle size tends to decrease porosity

    通常，顆粒越小曲率越大孔隙度越大，而當顆粒尺寸增大時孔隙度會減小。
  2. Because of the interaction of urushiol chains and cus, the transformation temperature tg of hybrid - epu / cus was higher than that of epu. heat stability and solvent resistance were also improved. the interaction and network of urushiol chains were efficiency to inhibit the dimension of cus nanoparticles

    漆酚鏈段與cus之間的作用，以及漆酚交聯網路的存在可有效阻止cus顆粒尺寸的增大，但漆酚交聯網路產生的空間位阻也在一定程度上降低了sz 」的擴散。
  3. The results indicate that the fracture toughness is influenced markedly by the different base structure of vermicular east iron and by the form of graphite ; unlike steel, the fracture toughness of vermicular cast iron increases with the yielding strength, while drops drastically with the increase of ratio of graphite grain length to thickness

    試驗結果表明，蠕墨鑄鐵的斷裂韌度受不同基體組織的影響比較明顯；受不同石墨形態的影響顯著，與結構鋼不同，蠕墨鑄鐵的斷裂韌度隨材料的屈服強度增大而增大，隨石墨顆粒的長厚比增加會急劇下降。
  4. Uptake of folate - bsanp by cancer cells was gadually increased with the extension of incubation time or the increase of folate - bsanp concentration, and the uptake could be competitively inhibited by excess free folate

    葉酸偶聯白蛋白納米粒的腫瘤細胞攝取量隨納米粒濃度增大、培養時間延長而增加，腫瘤細胞對葉酸偶聯白蛋白納米粒的攝取可被過量的外源性游離葉酸所抑制。
  5. And vibration function make supplies viscidity and interior frictional force of particle reduce greatly, make the sport tempo of the particle of the supplies increase, has increased the number of times of colliding effectively, accelerate cement particle surface hyrate to speed that liquid phase spread, is it fully go on to mix and stir at micro competence to guarantee

    而振動作用使物料顆粒間的粘性和內摩擦力大大減小，使物料顆粒的運動速度增大，增加了有效碰撞次數，加快了水泥顆粒表面水化物向液相擴散的速度，從而保證了拌和在微觀水平上的充分進行。
  6. The research results show that aggregate gradation and the nominal maximum aggregate size evidently influence the shear resistance of asphalt mixture ; aggregate flakiness content influences the shear resistance of asphalt mixture, and with the increase of aggregate flakiness content the shear resistance of asphalt mixture decreases ; asphalt binder properties, especially penetration, softening point and viscosity influence the shear resistance of asphalt mixture, and the latter increases with the decrease of penetration and the increase of softening point and viscosity ; asphalt content influences shear resistance of asphalt mixture, and with the increase of binder / aggregate ratio the shear resistance of asphalt mixture decreases ; air void influences shear resistance of asphalt mixture, and usually with the increase of air void the shear resistance of asphalt mixture decreases ; homogeneity does not have a direct and obvious relationship with absolute value of shear resistance of asphalt mixture, but does with variation of shear resistance of asphalt mixture

    研究結果表明：集料級配和公稱最大集料粒徑對瀝青混合料抗剪強度有顯著的影響；瀝青混合料抗剪強度受其集料中針片狀含量的影響較大，集料中針片狀含量增大，瀝青混合料抗剪強度減小；結合料的性質，特別是針入度、軟化點和粘度對瀝青混合料抗剪強度有較大的影響，隨著針入度減小，軟化點和粘度增大，瀝青混合料抗剪強度增大；含油量對瀝青混合料抗剪強度有較大影響，隨著油石比的增大，瀝青混合料抗剪強度減小；瀝青混合料抗剪強度受其空隙率的影響較大，一般隨著空隙率的增大，其抗剪強度減小；瀝青混合料均勻性與瀝青混合料抗剪強度絕對數值間沒有明顯的關聯，而與數值間的變異性有著很好的相關性。
  7. At the first stage of ball milling, the granularity of powders increases with prolonging the time. but if ball milling continues, the granularity will minish. when minishing to a certain extent, the granularity of powders don " t change greatly along with prolonging the time of ball milling

    在初始階段隨球磨時間的增加，粉末粒度變大，繼續球磨，粉末粒度變小，細化到一定程度后粉末粒度不再隨球磨時間的延長顯著變化。
  8. ( 3 ) in multi - particle simulation, if the particles are not too dense, the reconstruction images of particles are clear. when the particles density reaches some degree, the definition of the reconstruction images will decrease along with the particles density growing

    （ 3 ）在對多個粒子的模擬記錄和再現過程中，通過改變粒子的密度，發現粒子密度較小時，記錄和再現效果都很好，而當粒子密度增大一定程度時，粒子再現像的清晰度會下降。
  9. As the ratio of alcohol to water descends, both of them rise. as the solution concentration of nitrates descends, the crystalline size firstly descends and then rises. the nozzle pressure brings forth little affluence on the crystalline size of the powder, but the elevated pressure can enlarge the quantity and the size of the agglomeration

    隨酒精和水的比值的減小，粒徑和顆粒粒徑都增加；粒徑隨溶液濃度的減小，先減小后增加；一次粒徑隨壓力的變化，變化很小，但隨壓力和流量的增加，團聚體增多、團聚粒徑增大。
  10. The xrd showed that the crystalline of samples prepared in various o _ ( 2 ) partial pressure and various sputtering power was amorphous, the anatase crystalline formed when heat treatment temperature was above 450, and heat treatment temperature was higher, the crystalline was better. sem showed that the crystal grams formed on the surface of films when the o _ ( 2 ) partial pressure was high ; the obvious and big grains appeared hi the surface with improvement of heat treatment temperature

    Xrd分析表明，不同氧氣分壓下制備的樣品基本是無定型結構，不同濺射功率下制備的樣品基本也是無定型結構，當熱處理溫度高於450時，試樣出現了晶面趨向為（ 101 ）的銳鈦礦相，隨著熱處理溫度的升高，結晶程度增大； sem分析表明：隨著氧氣分壓的升高，試樣表面出現微小結晶顆粒；隨著熱處理溫度的升高，試樣表面出現了相當明顯的結晶顆粒，試樣的比表面積增大。
  11. Particle ratios embody the chemical equilibrium driven by inelastic interaction during rapid expansion when the temperature decreases in the colliding system, the measured hadron ratios provide the chemical composition of the fireball at the chemical freeze - out point and access the baryon transporter stopping ) for the initial conditions at early stage of the collisions. in this paper, we study the anti - proton to proton ratio from ig7au + 197 au collisions, analyzing p / p ratio as functions of rapidity, transverse momentum and centrality at ^ / saw = 200gev and the dependence on the center of mass energy of p / p ratio, compared with the experimental results. it shows that the p / p ratio has n ' t obvious dependence on rapidity for mid - rapidity, but shows a slight increase trend with pt increasing in the range of pt < 1gev / c for mini - bias or central collisions, and rqmd shows a more remarkable correlation between p / p ratio and centrality than experiments do at snn = 200gev

    研究表明：對廠在中心快度區沒有明顯的快度依賴性，在越靠近邊緣快度區， p p呈下降趨勢；在對心碰撞或者最小無偏事件中， p p在低橫動量區域隨著橫動量的升高而增大； p隨著碰撞對心度的比實驗結果表現出稍強的隨對心度增大而減小的趨勢，尤其是有再散射ujrqmd模型；在中心快度區， p p隨著碰撞的質心能量的提高而快速的增大，與實驗結果一致；在低能，有末態粒子再散射的d較好的預言了的：但是在mc能量下，有末態粒子在散射的d所預言的p p值比實驗值要小。
  12. After heat treatments, the granularity of powders increases and ultraf ine grains decreases. cracks appear on the surface of powders. so the rigidity of powders descends

    熱處理后粉末的粒度增大，微細顆粒的比例減小，表面出現裂紋，降低了粉末的硬度，同時粉末團聚作用減弱。
  13. With the optimum parameter, the obtained composite particle have many changes compared with uncoated graphite, such as the increase of coating ratio, particle size and decrease of specific surface area, et al

    在最佳包覆工藝條件下，所得復合粉體相對未處理石墨氧化物含量（包覆率）增加、粒度增大與表面積減小。
  14. The appropriate calcinations temperature is about 700, and the tetragonal sno2 phase crystal structure of the particles remained unchanged when sb was doped to it. as the calcinations temperature increasing and the calcinations time prolong, the size of particles grows and the crystallization tend to be complete. study on the electrical properties of ato powders prepared by hydrothermal synthesis was performed in - depth, the most optimal electrical properties are obtained at doping ratio of 11 percent

    水熱法制備的ato納米粉體在熱處理溫度700左右較為適宜，銻的摻雜並未改變粉體的四方相金紅石結構，隨銻摻雜量的增加，粉體的粒度變小；隨熱處理溫度的升高和熱處理時間的延長， ato粉體的粒度增大，晶體結構趨于完整。
  15. Electrorheological ( er ) fluids are a kind of complex fluids that is a suspension of high dielectric constant particles dispersed in an insulating oil of low dielectric constant, which have reversible and adjustable rheological property under the applied electric field

    電流變液是一種復雜流體，通常是由高介電常數的固體顆粒分散在低介電常數的絕緣油中形成的懸浮液。在外加電場作用下，其粘度增大，可由液態轉變為類固態，且該過程是瞬時的、可逆的、可調控的。
  16. The results indicate that, the viscosity of the slurry is increased and the dispersion of the slurry is decreased along with the superfine particle diameter decreasing ; the viscosity and dispersion of the slurry are obviously influenced by the variety of particles ; the viscosity of the slurry is increased and the dispersion of the slurry is decreased along with the superfine particle content in the slurry decreasing

    研究表明：隨著粒子粒徑的減小，粒子在漿料中分散難度增加，漿料的粘度增大；粉體的含量增加，粒子的分散效果也下降，漿料粘度也上升；粉體種類的不同對漿料的粘度影響很大，同時也較大程度的影響了粒子的分散性。
  17. For the soft rock, the shrink of material and reconstruction of particle is dominant, and density of rock is large

    至於孔隙率較高且連通性較高的軟砂巖則以顆粒重組和收縮佔主導地位，巖石密度增大。
  18. On the basis of the analysis of the test data, the additional force linearly increased with variation of water pressure in the aquifer, and increased with the increase of the depth and with the content of coarse soil particle in the overburden layer

    試驗結果表明：豎直附加力隨含水層降壓量的增大而線性增加，隨深度增大而增大，隨土層中粗顆粒含量增多而增大。
  19. Blend in molten state make hdpe crystals small, crystallinity large, quantity of cb particle benefit to conductivity decreasing ; in solid state cb aggregate is sheltered with a insulate hdpe film, also cb structure will be broken down during blend ; all of these will make conductivity bad. but processing alds can lower this effect obviously. 3. the effect of crosslink is restricting the movement of molten polymer molecules

    為此筆者認為固相混合使hdpe晶粒尺寸變小，結晶度增大，使得異相成核的晶粒增多，參與導電的炭黑粒子數量減少：熔混卻使炭黑粒子表面被覆一層絕緣膜：這都將導致材料的導電性明顯變差，同時兩種混合還會造成炭黑結構的破壞，皆使得材料的導電性明顯變差。
  20. As the temperature and the soak time increasing, crystallite size, graphitic degree and average particle size of the graphite increase, while specific surface area decreases. the electrochemical performance of modified graphite is improved with the change in structure and surface characteristics

    結果表明，隨著熱處理溫度的升高和恆溫時間的延長，石墨材料的石墨化度、石墨微晶尺寸l _ c及l _ a逐漸增大，比表面積減小，平均粒徑增大，充放電性能得到改善。