退火脆性 的英文怎麼說

中文拼音 [tuìhuǒcuìxìng]
退火脆性 英文
annealing brittleness
  • 退 : 動詞1 （向後移動） retreat; draw back; move back 2 （使向後移動） cause to move back; remove; wit...
  • 火 : fire
  • 脆 : 形容詞1 （容易折斷破碎） fragile; brittle 2 （較硬的食物容易弄碎弄裂） crisp 3 （聲音清脆） （of ...
  • 性 : Ⅰ名詞1 （性格） nature; character; disposition 2 （性能; 性質） property; quality 3 （性別） sex ...
  • 退火 : [冶金學] anneal; annealing; back-out
  1. The accidental quenching, occurring in the sintering process, will make the steel back of a powder alloy brake lining brittle and useless. in this paper, an annealing process has been adopted to regain the plastic property of the steel back while the other properties of cg03 brake linings are still remained

    粉末合金剎車片在燒結後有時會意外淬火，造成剎車片鋼背脆化而報廢.採用一種退火工藝，在保持剎車片其它性能的同時，使剎車片鋼背恢復塑性
  2. The maximal power outputs of 37. 0 mw / cm2 and 30. 0 mw / cm2 for the p - and n - type laminated materials respectively at the temperature difference 490 have been experimentally obtained, which are about 2. 5 and 3. 0 times those of - fesi2. chemical analyses show that the interface failure between the bridge alloy and the semiconductor bi2te3 results mainly from the eutectic mixtures with low melting point and brittle compounds formed during welding and long time annealing at 190. it is found that the electrical properties of a laminated structure are mainly controlled by the wettability of the bridge alloy on the semiconductor surface

    發現： 1 ）疊層材料具有明顯優于均質材料的熱電性能，在490溫差下， p -型和n -型疊層材料的最大輸出功率分別達到37 . 0和30 . 0 （ mw / cm ~ 2 ） ，是同類型均質- fesi _ 2的2 . 5和3倍； 2 ）在焊接過程和190長時間退火處理過程中，焊接過渡層合金和基體半導體（特別是bi _ 2te _ 3 ）之間存在明顯的元素相互擴散，從而在過渡層中形成一些低熔點共晶體和脆性化合物，這是導致疊層材料破壞的主要原因； 3 ）焊接過渡層合金與半導體基體之間的潤濕性是影響界面層電性能的主要因素。
  3. Karst ecosystem is a kind of vulnerable ecosystem, its vulnerability including mainly : 1 environment capacity is small, vegetation is difficult to recover after having been destructed, hydrologic movement is rapid and floods and droughts often occur ; 2 vegetation growth depends on the conditions of eco - environment overly, which are affected by environment obviously ; 3the positive evolve of eco - environment relies on the recover of vegetation, 4the methods of water resource use and land use lack of rationality. these vulnerabilities are be magnified by climate changes

    巖溶生態系統是一種脆弱的生態系統，它的脆弱性主要表現在：環境容量小，植被遭破壞后很長時間才能恢復，以及水文過程變化迅速，旱澇時常發生；植被生長過度依賴于生境條件，但生境條件受到環境影響明顯；生態環境的良性演化依賴植被的恢復；水資源利用與土地利用方式間缺乏合理性，如刀耕火種、過渡開墾造成生態環境中種子庫嚴重丟失，物種多樣性受到影響，植被演化趨于單一或種群退化。
  4. Anneal means make harden steel soft and remove brittleness

    退火就是使淬火鋼變軟並消除其脆性。