過滲碳鋼 的英文怎麼說
中文拼音 [guòshèntàngāng]
過滲碳鋼
英文
perished steel-
After forming, they receive adequate surface hardness through heat treatment. such hardening is made possible by carburizing. these case - hardening steels are an important group of materials for mold cavities
成形后,鋼經過熱處理得到足夠的表面硬度,這種硬化常通過滲碳的方式進行,這種表面硬化鋼是一種很重要的模具型腔製作材料Abstract : the paper analyzes the wear resistance and anti - adhesion of 20 and 45 steel formed in austenitic ion - nitrocarburising and comparisons to the general ion - nitrocarburising. the experiment shows that austenitization - nitrocarburising can be carried out at 590 700, its wear resistance and anti - adhesion is the best at 630 , the worst at 660 and anti - adhesion is the best at 630 , the worst at 660 and the mediate at 570 600. with the help of raising processing temperature properly and speeding up the process the wear behavior can be improved
文摘:研究20鋼、 45鋼經奧氏體離子氮碳共滲后的耐磨性和抗咬合性,並與普通離子氮碳共滲后的作了比較,試驗表明:在570 700范圍內進行離子氮碳共滲后,其耐磨性和抗咬合性以630處理時為最佳, 660處理時最差,而570 600處理時則介於兩者之間,通過適當提高共滲溫度,再提高滲速,從而縮短共滲時間的同時,可以提高耐磨損性能。It shows the nanometer particles have automation to make the friction surface in a comparatively even state. 4 ) through tribology chemistry function, the nanometer cacoj and cao particles form a deposited film on the wear scar ' s surface or strengthen the surface through a small amount of metal ca ' s diffusion to improve the friction surface ' s a
( 4 )納米碳酸鈣和納米氧化鈣粒子通過摩擦過程中的摩擦化學作用在磨斑表面上形成了沉積膜,少量金屬鈣通過擴散作用滲透到鋼基體表面,形成表面強化層,提高了表面的耐磨性。Abstract : the average diffusion coefficient of carbon in surface layer of steel 20 rare ea rth carburized at 880 and 900 for 8 h was calculated by substituting the mea sured layer depths into the diffusion equation
文摘:通過對20鋼常規氣體滲碳和稀土滲碳層深的測定,計算出稀土滲碳時碳在奧氏體中的平均擴散系數。分享友人