高爐熔劑 的英文怎麼說
中文拼音 [gāolúróngjì]
高爐熔劑
英文
blast furnace flux-
Rapid repairing mass for converter ismade of electro baked magnesite and high - quality synthetic sandand manufactured by adding high fluidity recarburizer ( beveloped by ourselves ) as addition agent withspecial technique. lt has the characteristics of well fluidity, well rapid fluidityand rpid sintering etc. it is applied to hot patching of large area before or after the converter as rapping hole patching and other parts for converter
轉爐快速補爐料是以電熔鎂砂和優質合成砂為主要原料，配以自行研製的高流動性的增碳劑為添加劑，以特殊工藝生產製成，具有流動性好、快速燒結等特點，適合於轉爐的前後大面的熱修補及出鋼口等部位的修補The results showed that the melting ratio of silica flux decreases and the complete melting time prolongs with the size of silica flux and matte grade increasing, and the effect of the blowing air and oxygen enrichment is not remarkable in the high grade copper matte converting process
對于高品位冰銅轉爐吹煉，鼓入氣體流量和氧濃度對石英熔劑熔化率影響不顯著；熔劑粒度和冰銅品位對熔化率影響顯著，並隨著熔劑粒度和冰銅品位的增加，熔劑熔化率降低，完全熔化時間延長。They have excellent corrosion, thermal shock resistance and spalling resistance. they wide applications and can be used in key locations of thermal processing equipment such as bof, eaf, lf and so on. 2 alumina - magnesia - carbon brick made from high - purity bauxite or fused alumina and fused magnesia grain or high purity magnesia by pressing, resin - bond for thermal shock resistance
1 ，鎂碳磚是不燒的耐火材料，經過摩擦壓磚機的成型以及乾燥處理后而成，它的主要原料是電熔鎂，高純鎂砂和高純石墨，結合劑為樹脂，鎂碳磚有良好的耐侵蝕性，熱震穩定性和抗剝落性，它已經被廣泛地用在鋼廠的轉爐電爐鋼包精煉鋼包等關鍵部位。Additions of carbon for improved slag resistance. spinel formation improves hot strength, slag resistance and brick joint erosion. 3 repairing material for bof uses fused magnesia or sintered magnesia as the main raw material and after modifid pitch and special additives are added, it has the following characteristcs than other conventional converter pitch temperature, shorter sintering time, longer service life and less pollution. it is mainly used for repairing converter working face, also for tapping side, tapping hole and bottom
3 ，轉爐大面補料是採用電熔鎂砂或燒結鎂砂為主要原料，通過加入改性瀝青和特種添加劑使它和傳統瀝青補爐料相比具有高溫附著性好燒結時間短流動性好使用壽命長污染小等特點，主要用於修補轉爐迎鋼面通常稱「大面」也可以用於修補出鋼側，出鋼口及爐底等部位。Abstract : melting behavior of silica flux in the converting process of high grade copper matte was investigated
文摘:研究了高品位銅冰銅轉爐吹煉石英熔劑熔化行為。It is made of fused magnesite and high purity flake graphite by adding metal composite antioxidant and phenolic resin as binder. it has the excellent properties of corrosion resistance, spalling resistance, resistance to oxidation and better thermal shock resistance. it can be used in all kinds of converters, eaf, refining ladles and common ladles. upon request, multiple lining - up designs of reasonable materials can be provided according to the working conditions of above mentioned furnaces
採用電熔鎂砂、高純鱗片石墨為主要原料，添加金屬復合抗氧化劑，以酚醛樹脂為結合劑製成的製品具有優良的抗浸蝕性、抗剝落性、抗氧化性和良好的抗熱震性，適用於各種容量的轉爐、電爐、精煉鋼包及普通鋼包，本公司可根據用戶要求，針對上述4種熱工窯爐的具體使用條件提出爐襯的材質綜合砌築方案。分享友人