  1. The expansion agents can only make up the shrinkage to some extent, and the compensation effects would be reduced when the retardener and fly - ash are used. the expansion agents are not panaceas to avoid the shrinkage cracking as expansion can also reduce the concrete soundness. under bad curing condition, the polypropylene fibrillated film fiber can improve concrete ' s anti - crarking property, while the nominal steels have very unobvious effects. to reduce the concrete shrinkage thus avoid the cracking, the former factors must all be taken into account in concrete proportion design to develop sound concrete

    研究結果表明，水泥的品種和用量是影響混凝土收縮值的主要因素之一，當混凝土中水泥用量超過470kg / m ~ 3時，混凝土的收縮值超過400 10 ~ （ - 6 ） ，在約束狀態下存在高開裂風險；採用細砂使混凝土單位用水量顯著提高，收縮值也大幅增加；優質粉煤灰總體上能抑制混凝土的收縮，以超量方式摻入其抑制作用更加明顯，但粉煤灰混凝土早期的粘聚性較差，應注意養護，以免失水產生龜裂；早強減水劑和緩凝減水劑都會使混凝土收縮值增加；膨脹劑只能補償混凝土部分收縮，同時受緩凝劑和粉煤灰的抑制，而且膨脹使混凝土的體積安定性增加了不確定因素，膨脹劑不是解決混凝土收縮裂縫的良方。
  2. The effects of mineral additive such as fly ash, slag, and dura fiber on concrete expansive property are studied, the results show that these mineral admixture reduce shrinkage in common concrete and also reduce expansive value in shrinkage - compensating concrete

    本文討論了粉煤灰、礦渣、杜拉纖維對混凝土膨脹性能的影響，在補償收縮混凝土中，摻合料使其膨脹率減低，杜拉纖維可以提高混凝土的體積穩定性，顯著提高劈拉強度。
  3. It shows that fly ash added may restrain expansion of wecam and improved its soundness. 6. as for wecam, its soundness should be tested appropriately with concrete specimens autoclaved at 200 for 6h, its limit expansion should be determined from 0. 1 % to 0. 2 %

    5 .在其它條件不變的情況下，外摻氧化鎂混凝土的壓蒸膨脹率隨著粉煤灰摻量的增加而減小，表明粉煤灰的加入具有抑制外摻氧化鎂混凝土的膨脹作用，提高了混凝土的安定性。
  4. The shrinkage characteristics of hsc and normal concrete at short term and long term are researched. based on the above research, high performance expansive c50 - c80 concrete, which posses good expansive properties, excellent flow ability, low slump loss and hydration heat. in order to improve the anti - cracking of some important projects, such as cutting wall, the workability and bulk stability of fiber - reinforced micro expensive concrete are researched

    針對高強混凝土的收縮特性以及性能特點，本文提出將膨脹劑引入高強混凝土內進行補償收縮，研究了粉煤灰、礦渣、硅灰等摻和料對混凝土工作、力學耐久性能的影響和c50 c80高強微膨脹補償收縮混凝土的力學與工作性能，配製出具有很好的可泵性能和耐久性能的混凝土。
  5. In this paper, the influences on concrete shrinkage and splitting tensile strength by the varieties and contents of the raw materials, such as cement, sand, fly ash, water - reducer and expansion agents, are studied. the possibility of the prevention of the concrete cracking by proper concrete proportion design is discussed

    本文著重研究了水泥、砂、粉煤灰、減水劑、膨脹劑等材料的品種、用量對混凝土收縮性能及混凝土劈裂抗拉強度的影響，探討了通過合理的配合比設計達到減少混凝土收縮、提高混凝土劈裂抗拉強度進而降低混凝土開裂風險的可能性。