anchoring material 中文意思是什麼
anchoring material
解釋
結合劑-
According to the anchoring material difference, post - installed bars may include organically post - installed bars and inorganically post - installed bars
植筋按照粘結材料的不同，可分為有機植筋和無機植筋兩類。 -
Inorganically post - installed bars although have the ideal durability and heat - resistance, its bonding strength is low. it is unable effectively to transmit the load, the anchor depth is too big. these restricted application of the inorganic anchoring material in the post - installed fastening project
無機植筋雖有較理想的耐久性能和耐高溫性，但其粘結強度較低，無法有效傳遞荷載應力，錨固深度太大，這制約了無機粘結材料在植筋工程中的應用。 -
The fastened end of bar was machined to multi cone - shaped heads. through the cone heads compress the inorganic anchoring material, the load was transmitted from bars to base material. it changes the transfer path of loads and takes advantage of high compress strength of inorganic material, thus enhanced the anchor intensity of inorganically post - installed bars
本文提出一種新型的植筋技術? ?帶錐頭無機植筋，它把鋼筋錨固端加工成多個錐頭，通過錐頭對無機錨固材料的擠壓，將荷載傳遞給基材，使基材與無機錨固材料的界面上產生剪壓復合應力狀態，改變傳統植筋的受力機理，利用了無機錨固材料抗壓強度高的特點，從而提高了無機植筋的錨固強度。 -
In practical projects, because of high bonding strength of the organic anchoring material, organically post - installed bar was widely applied. however, the durability and the heat - resistance of the organic anchoring material are relatively bad, the structure lied in hidden danger
在實際工程中，因為有機粘結材料的高粘結性能，有機植筋被廣泛應用，而有機粘結材料的耐久性能和耐高溫性能較差，給結構埋下了安全隱患。 -
Electro - optical curves for lc cells have been analyzed and it has been shown mat a large attenuation range and a shallow attenuation slope can be achieved simultaneously for a variable optical attenuator based on a parallel - aligned lc cell with an appropriate surface anchoring strength. as compared with the existing liquid crystal - based voa structure ( using two cascaded lc cells with a particular material ), the present structure is simple and has no special requirement for the lc materials
提出了基於弱錨定平行排列液晶盒的可變光衰減器（衰減范圍大、衰減曲線下降平緩以保證調節精度） ，與己有液晶型可變光衰減器結構（選用特定液晶材料、兩個液晶盒級聯結構）相比較，本論文提出的基於弱錨定平行排列液晶盒的可變光衰減器結構簡單，同時對于液晶材料無特殊要求。 -
Since the existed research has n ' t illuminated the failure form of post - embedded reinforcing steel bar bonding anchor and its mechanism, has n ' t systematic research on factors influencing the function of post - embedded reinforcing steel bar bonding anchor, and also failed to test on the long period validity of post - embedded reinforcing steel bar bonding anchor, it is very unfavorable for the spread and application of post - embedding technique. in the meantime, the fact that the present post - embedding anchoring material is of few kinds, high prices and still - to - be - improved performance has become the bottleneck of the post - embedding technique ' s development, which has restricted its further application and development. therefore, it is of great importance to develop a new type high - performance inorganic anchoring material with reasonable price and improved performance
由於已有研究對后植鋼筋粘結錨固的失效形式、破壞機理未作出明確回答，對后植鋼筋粘結錨固性能的影響因素未進行系統研究，對后植鋼筋粘結錨固的長期有效性未予以試驗證實，不利於植筋技術這種新型結構加固技術的推廣應用，同時現有植筋錨固材料存在品種少、價格高、性能需要進一步改進和提高等局限性，已成為植筋技術發展的瓶頸，制約了植筋技術的進一步應用和發展，因此開發價格合理、性能優良的新型高性能無機質類錨固材料就顯得尤為重要和迫切。 -
In the study, a new kind inorganic anchoring material was developed, which consisted of special binder and aggregate, the former is made from clinker, blast furnace slag and compound admixture, and the later is superfine sand. effects of the factors such as clinker / slag, binder / sand, solution / binder and constituent of solution on the strength, set - time and contraction of the matrix made from the anchoring material were studied
上述分析研究得出以下結論：新型無機錨固材料具有早強、快硬、高強特點， 10h .抗壓強度可達26 . 5mpa ， 365天強度可達144 . 0mpa ；初凝時間在40min . 3h .之間，且初終凝時間差在15分鐘以內；在保濕條件下具有微膨脹性，膨脹率在0 . 5 %以內。 -
Durability ' s of the material such as permeability, heat - resistance, carbonation and steel bar - protection were tested. the bonding characters between anchoring material matrix and post - embedding steel bar, the matrix and the concrete structures were studied
在植筋錨固長度足夠的條件下，混凝土與錨固砂漿的界面粘結強度大小直接決定了植筋錨固的控制荷載，粘結界面成為受力的薄弱環節。 -
Study on new type cement base anchoring material
新型水泥基錨固材料研究 -
This paper used the reactive powder concrete ( rpc ) as the inorganic anchoring material, and studied this material ’ s compositions and the materials mechanics properties ( mainly includes compressive strength, shearing strength, elasticity coefficient and poisson ' s ratio ), and also studied the contraction, durability ( including the rpc permeability, chemistry corrosiveness and anti - frozen performance ) and the heat - resistance of rpc
本文採用活性粉末混凝土（ rpc ）為無機錨固材料，並對該材料的配合比，材料力學性能（主要包括抗壓強度，抗剪強度，彈性模量和泊松比）進行研究，還分析了rpc的收縮性、耐久性能（包括rpc的滲透性、化學侵蝕性和抗凍性能）和耐高溫性能。