calcined kaolin 中文意思是什麼

calcined kaolin 解釋
煅燒高嶺土
  1. Surface modification of calcined coal - series kaolin

    煅燒高嶺土表面改性
  2. Method for measurement of brightness of calcined kaolin in coal measures

    煤系高嶺巖土煅燒土白度測定方法
  3. Suface modification and application effect of calcined kaolin in coal series

    煤系煅燒高嶺土的表面改性和應用效果及應注意的問題
  4. The analysis results of reaction between calcined kaolin and saturation ca ( oh ) 2 solution and xrd results of reaction products of calcined kaolin and cement indicated that calcined kaolin has a high volcanic ash active

    通過對煅燒高嶺土與飽和石灰水的反應及煅燒高嶺土與水泥混合后的xrd分析，確認煅燒高嶺土具有較好的火山灰活性。
  5. The addition of calcined kaolin to cement increased the chemical shrinkage of cement stone, but it had no distinct impact on the self - shrinkage of cement stone

    煅燒高嶺土摻入水泥中，增加了水泥石的化學收縮，對水泥石的自收縮的影響並不明顯。
  6. Determination of the sediment volume of kaolin and calcined kaolin in coal measures

    煤系高嶺巖土及其煅燒土沉降體積測定方法
  7. Research on surface modification of calcined sedimentary kaolin and its application

    沉積型煅燒高嶺土表面改性與應用研究
  8. Surface modification of calcined sedimentary deposit kaolin and its application

    沉積型煅燒高嶺土表面改性與應用試驗研究
  9. Surface modification of yichang calcined sedimentary deposit kaolin and its application

    宜昌沉積型煅燒高嶺土表面改性與應用研究
  10. Considering energy conservation and effects of calcined kaolin on the strength of cement, it was optimum method to produce calcined kaolin by calcining it at 980 c for 0. 5h and then cooling it suddenly

    結合煅燒高嶺土對水泥強度的影響，考慮到節約能源，以採用980恆溫0 . 5h然後快速冷卻的方法作為最佳煅燒溫度與時間。
  11. Quality comparison among calcined coal - series kaolin products under different productive processes and their influences on properties of paper coating

    煤系煅燒高嶺土不同生產工藝產品質量的比較及對紙張塗層性能的影響
  12. The relation between addition content of calcined kaolin, aluminium powders and aluminum sulfate in concrete and compressive strength, slump constant, 30min slump and permeability altitude were studied, and according to the experiment results, the component percent contents of crack - resistant and water - repellent admixture in cement were determined as following : calcined kaolin 6 %, aluminum sulfate 4 % and aluminium powders 0. 005 %

    通過對煅燒高嶺土、鋁粉、硫酸鋁在混凝土中摻量對其抗壓強度、初始武漢理工大學碩士學位論文坍落度、 3omin坍落度保留值及透水高度的影響，確定了配製抗裂防水外加劑的各組成成分以其占水泥質量的百分比分別為:鍛燒高嶺土6 % ，硫酸鋁4 % ，鋁粉為0 . 005 % 。
  13. The calcined kaolin, aluminium powders and aluminum sulfate were used as components of water - repellent agent, which effects on cement hydration and concrete impermeability were discussed in this paper

    本文以煅燒高嶺土、鋁粉、硫酸鋁作為防水劑的組份，研究了它們對水泥水化及混凝土的抗滲性的影響。
  14. The research results revealed that activated alumina content of calcined kaolin of kaolin had a strong correlation with the calcined temperatures and time. the activated alumina content of calcined kaolin increased with the calcined temperatures increasing from 750 c to 950 c, and increased with the calcined time prolonging at 750 c, 800 c, 850 c, 900 c and 950 c. however, the elevated speed of the activated alumina content decreased at 950 c for 4h

    研究發現，高嶺土的煅燒溫度及煅燒時間對煅燒高嶺土中的活性氧化鋁的含量具有較大的影響：高嶺土在750 、 800 、 850 、 900 、 950溫度下煅燒，其活性氧化鋁含量隨溫度和時間的增加而增加，但在950 、 4h時后活性氧化鋁的增加速度降低。
  15. Determination of the function in suspension of kaolin and calcined kaolin in coal measures

    煤系高嶺巖土及其煅燒懸浮性能測定方法
  16. However, the addition of calcined kaolin to cement caused setting time of cement to prolong and water requirement of cement to reduce

    但其與水泥混合后稍微增大水泥的用水量、縮短凝結時間。
  17. The experiment was done that the cured cement stone with addition of calcined kaolin were dipped into nacl solution of 2. 5wt %, and the experiment results showed that addition of calcined kaolin made cement stone pore fine and cement mortar displayed high property of impermeability

    煅燒高嶺土的摻入可以使水泥石中的孔細化，通過對煅燒高嶺土摻入水泥中標養后在2 . 5氯化鈉溶液中浸泡試驗發現，煅燒后的高嶺土摻入水泥砂漿使其具有極好的抗滲透性。