The samples were welded at 800, 900. d _ ( cu ) and dni at contacting line increased with increase of welding temperature. and atom diffusion at contacting line welded by bpec heating was much quicker than by radiation heating
其它條件相同時，改變裝模方式以獲得不同的加熱條件和電場條件，結果表明，無模套時接觸面處cu和ni的擴散系數比有模套時大。 -
In this paper, three unique models were designed to research atom diffusion at interface, contacting line and joining point under bpec heating and compare with it under radiation heating in order to find out if bpec speed atom diffusion. the first model was aimed to research atom diffusion at interface under bpec heating. experiment condition of bpec diffusion welding sheet cu and ni : direct diffusion welding, at a pressure of l0mpa, welded at 750 ~ 900, with heat rate of 200 ~ 400 / min for 10mm, on / off of 6 / l ~ 48 / 8, with die or not, vacuum of 6pa
本文設計出三種樣品預構件，研究脈沖大電流加熱條件下片狀材料、線狀材料和球形顆粒之間的原子擴散過程，弄清脈沖大電流加熱條件下原子擴散與一般燒結和焊接過程中原子擴散的區別，以證實特殊的電場和磁場是否對原子的擴散有推動作用，揭示脈沖大電流加熱條件下原子的擴散過程，探索脈沖大電流熱加工技術快速高效的原因。 -
The third model was designed to investigate atom diffusion at contacting point. fe was sintered at 500, 550 > 600, 650 > 700 under bpec and radiation heating. the test results of image processing indicated that the average pore size took on wavelike with temperature under bpec heating
脈沖大電流加熱條件下，其它條件相同時，分別在800 、 900的溫度武漢理土大學碩士學位論文下擴散連接cu絲和ni絲，結果表明接觸線處cu和ni的擴散系數隨溫度的升高而增大。