To meet the processing requirements before sintering, the pressed briquet was pre - calcined at 1150 to make it possess adequate processing strength at first and then was shaped through precise turning on the numerical control lathe according to the design diagram of the femoral head prostheses of partial hip joint
為滿足燒結前坯體加工的要求，壓制后的坯體在1150預燒，使其具備一定的加工強度，然後按照半髖關節股骨頭假體的形狀尺寸設計圖在數控車床上進行精密車削成型。 -
On the base of the analysis on the advanced technology of hard ferrite in foreign country, the main procedures of preparing hard ferrite pre - sintering material are determined as follows : first, the ferrite oxides coming from the main cold rolling line and strontium carbonate are conveyed to storage tank by gas power and weighed automatically according to the demands of constituent composition. and then they are mixed and grinded by using method of wet treatment. finally the mixtures is transported to the devices of storage by transporting pump
在分析國外先進的永磁鐵氧體生產工藝的基礎上，確定了生產高檔永磁鐵氧體預燒料的主要過程：首先，利用攀鋼冷軋鐵紅為主要原料，將氧化鐵紅及碳酸鍶採用氣力輸送至貯料料倉，經自動稱量裝置，按工藝配方稱量後分別由氧化鐵紅及碳酸鍶發送罐氣力輸送進入預混攪拌筒加水攪拌，然後再送入混磨機濕法混磨；最後，混合物經輸送泵輸送至料漿存儲裝置，經定量進料泵定量輸送至回轉窯進行濕法預燒，預燒料經緩冷至室溫后，再球磨。 -
Through this article work, the perfect rutile has been got with flame fusion method in developed domestic sjz sintering machine for the first time in china. based on it, the study of the electrical property of irradiationed rutile by high dose neutron has been also made. the achievements are concluded in the following : ( 1 ) through the development of technology of tio
對粉體的制備工藝本論文也做了詳盡的描述和研究，對粉體前驅體ats的晶相、合成和焙燒過程進行了xrd 、 sem 、 tg等全面的分析，對粉體的晶相結構、形貌以及性能的表徵都做了研究。 -
Under the background of correlative research project, the method of selective laser sintering has been used in the researching work. polymer - coated high - temperature alloy powder have been first developed successfully in our nation. the laser sintering and post - treatment process of high - temperature alloy parts have been systematically studied, which lay the foundation for its engineering application
在國內首先研製成功了覆膜高溫合金粉末及其制備工藝，並對其激光燒結成型和后處理工藝進行了系統的實驗研究，為該項技術的工程化應用打下了基礎。 -
The experimental data has been used to validate pdm and low temperature sintering mechanics. the advantage and disadvantage of pdm have been discussed also. for the first time, the pdm is used to study the low temperature sintering mechanics of uo _ 2, and the research results indicate : 1
3 、基於燒結頸長大速率與緻密化動力學方程得出，影響二氧化鈾低溫燒結的因素有原始粉末粒徑、粉末堆積方式、坯塊原始密度、燒結溫度、燒結時間、燒結氣氛等;粉末壓坯一定時，燒結溫度、燒結時間和燒結氣氛就成為控制低溫燒結的關鍵因素。 -
Beginning with the analysis of the effects, which are brought by the application of only one kind of pore - former and some other operating factors ( such as sintering temperature, warmth retaining time and so on ), on the properties of the beads, e. g., porosity, strength, size distribution of the beads and pores size, etc., these effects are discussed in detail and the relationship between the factors is studied thoroughly. the use of mpf ( multi - pore - former ) is introduced for the first time, which is of the most importance and significance in this paper
研究從造孔劑選用和燒結過程對顆粒的孔隙率、機械強度、孔徑分佈及粒度分佈的影響入手，找出了造孔劑的種類及含量、燒結溫度以及保溫時間等因素對最終所得產品顆粒的性能影響及它們之間的相互關系，並首次提出將造孔劑復配使用來對填充法加以改進，無需擴孔處理，即能直接制備宏孔徑、高強度、小粒度、比表面大的多孔玻璃載體顆粒。 -
As shown by the measurements, the electrical resistivity of sintered psc has a tendency of first decreasing and then increasing as the sintering temperature and / or sintering time increase. also it decreases with the increased pressure on the pressed powder compact
對樣品的電阻率進行了測量，總體呈現出隨燒結時間和燒結溫度的增加而先降低后增加的趨勢，並隨壓坯的成型壓力的增加而降低。 -
In this dissertation, eu2o3 - sc2o3, y2o3 - sc2o3 co - doped tungsten powders and impregnated cathodes related to these powders have been prepared by pressing, sintering and impregnating for the first time
本論文首次制備了復合稀土eu2o3 - sc2o3 、 y2o3 - sc2o3摻雜的鎢粉，通過粉末壓制、燒結和基體浸鹽的工藝制備了相應的復合稀土/氧化鈧-鎢基擴散陰極。 -
A study on the synthesis, structure and performance of linio2 - based compounds as cathode materials for lithium ion batteries was carried out systemically and in detail in this dissertation. as the first step of this study, a sol - gel method using citric acid as a chelating agent was developed. the reaction conditions in sol - gel process, pre - calcination process and calcination process, especially sintering temperature and sintering time in calcinations process, were analyzed and optimized carefully
本文採用多種結構分析、表面分析、熱分析和電化學研究方法和實驗手段，從合成方法、結構特徵、電化學性能、熱穩定性和貯存性能等多方面對鋰鎳氧系列電極材料進行了系統深入的研究，制備出性能良好的鋰鎳氧系列電極材料，解釋了鈦的摻雜對電極材料的作用機理，揭示了鋰鎳氧系列電極材料的貯存失效機理，並借鑒和發展了rietveld結構精修方法和tpd - ms技術在鋰離子電池電極材料研究中的應用。 -
But its sintering temperature is so high that it cannot be sintered under 1000 with low melting point electrode materials like ag, cu etc. presently investigations about this material are mainly via glass - ceramic technique to decrease the sintering temperature and the dielectric loss is high. for the first time, this investigation manufacture a casio 3 system low dielectric and high frequency microwave dielectric ceramic via tape casting with basic material altered and additives doped
本文以casio _ 3體系為研究對象，首先對casio _ 3體系進行改性，並首次採用li _ 2o和bi _ 2o _ 3作為燒結助劑，降低體系燒結溫度，在此基礎上，採用catio _ 3調節陶瓷的頻率溫度系數，制備出微波介電性能優良的具有工業應用價值的casio _ 3系ltcc低介高頻微波介質陶瓷。 -
The samples which are obtained by sintering at 500 for 2 hours and then at 750 for 8 - 16 hours, have good electrochemical performances. the first charge / discharge capacity reaches 120 mah. g - 1 ; the capacity lost is about 15 % after 50 cycles
先在500焙燒2小時，然後在750下焙燒8 - 16小時左右所得樣品具有很好的電化學性能，首次充放電容量達120mah . g ~ （ - 1 ） ，循環充放電50次后容量損失在15左右。