  1. The degrees of crystallinity of pure ptfe under the different conditions of water cooling, air cooling and furnace - varying cooling were made comparison by xrd. the thermal stability of pure ptfe and solid lubricant was analyzed by dsc - tg ; the composition and valence state of elements in the surface of carbon fiber, solid lubricant before and after friction test and lubricant transfer film were characterized by xps ; the frictional property of solid lubricant was tested by pin and disk test rig. the frictional wear property of solid lubricant between embedded bearing sleeve and steel axle friction pair ring was tested by special simulate test machine, the hardness of solid lubricant was tested by pm ; the compression strength of solid lubricant was tested by material test machine

    用sem表徵原料微觀結構、摩擦表面及潤滑轉移膜表面形貌：用xrd進行原料物相分析，及比較水冷卻、空氣冷卻、隨爐冷卻三種工藝條件下的純聚四氟乙烯樹脂的結晶度；用dsc - tg分析純聚四氟乙烯樹脂及固體潤滑劑的熱穩定性；用xps表徵碳纖維表面、固體潤滑劑摩擦前後表面、潤滑轉移膜表面的元素組成、價態變化；用銷盤式摩擦磨損試驗機對固體潤滑劑進行摩擦性能測試；採用專用的臺架模擬試驗機對固體潤滑劑鑲嵌軸承套與鋼軸摩擦副間的摩擦磨損性能進行測定；用萊次偏光顯微鏡（ pm ）測試固體潤滑劑的硬度；用材料試驗機測試固體潤滑劑的抗壓強度等。
  2. ( 2 ) it is found that distilled water as lubricant can markedly reduce the accumulation of friction heat and temperature rise on the frictional surfaces of polymer. so the heat fatigue and adhesive wear decrease. moreover, a lubricating film forms on the interface between the counterpart and polymer when distilled water acts as polar lubricant

    （ 2 ）潤滑劑水的存在，可大幅度降低聚合物磨損表面的摩擦熱積累及溫升，從而減少了基體的熱疲勞磨損和粘著磨損，同時，水作為一種極性潤滑劑，在摩擦界面上能形成一層潤滑膜，對摩擦表面起了一定的隔離作用。
  3. When mixed with the lubricating oil, the nanometer particles can improve lubricating oil ' s abilities of extreme pressure, anti - wear and reduce frictional resistance

    將納米粒子加入到潤滑油中，可以提高其極壓性能和抗磨性能，減少摩擦阻力，延長機器零部件的使用壽命。
  4. The wear mechanism of tungsten carbide particle reinforced steel matrix composites was studied according to the frictional and wear characteristics and the scanning electron microscopy photographs of worn surfaces after wear testing. the effect of heat treatment and tungsten carbide content on wear resistance was investigated as well

    結合磨損特性曲線和不同磨損時間的摩擦面sem照片，分析了wc鋼復合材料的磨損機理，並討論了不同熱處理工藝和wc顆粒含量對wc鋼復合材料磨損性能的影響。
  5. Powder - metallurgy copper two - metals friction material has a steel body and wear - resistant copper - alloy thin coating. its frictional factor is lower, it has good wearing resistance, csolidl self - lubrication and anti - bite

    銅基粉末冶金雙金屬減摩材料是以鋼為基體，薄層銅合金為耐磨層，它具有較低的摩擦系數，耐磨性好，具有固體自潤滑成份，有良好的抗咬合性。
  6. The tlow distance and gelating time of the nanocomposites were shorter than that of the pure pf, which meet the standard of the pf used in frictional materials. compared to the pure pf, the silica7pf nanocomposites exhibited excellent heat stability only in nitrogen atmosphere, however, so do vermiculite / pf nanocomposites in both nitrogen and air atmospheres. compared to the brake pad based pf resin, the wear rate of the present one based with silica / pf nanocomposite decreased obviously, especially in high temperature

    用烷基銨ctab和kh - 560對蛭石進行有機化處理，通過原位聚合法制備了酚醛樹脂接枝改性sio _ 2納米復合材料、酚醛樹脂kh - 560改性sio _ 2納米復合材料、酚醛樹脂ctab改性蛭石納米復合材料、酚醛樹脂/ kh . 560改性蛭石納米復合材料，採用ftir 、 xrd 、 afm和tg分析與流動距離、凝膠化時間的測試，研究了所制備的酚醛樹酯納米復合材料的結構、固化行為和熱穩定性能，並研究了以酚醛樹酯納米復合材料為基體的剎車片摩擦磨損性能。
  7. Xrd, scanning electron microscopy ( sem ), frictional wear test, and vickers hardness measurement were used to characterize the specimens

    產物進行x射線衍射分析，掃描電子顯微鏡分析，摩擦磨損試驗和維氏硬度測量。
  8. Powder - metallurgy copper friction materal has enough and steady frictional factor. it can perfectly coexist with coordination material. it has good anti - bite, thermal conduction, wear - proof and corrosion - proof

    銅基粉末冶金摩擦材料，具有足夠和穩定的摩擦系數，能與對偶材料很好的共存，具有良好的抗咬合性和導熱性，耐磨、耐腐蝕。
  9. It is believed that the formation of a1n is not only helpful for improving the properties of samples, but also helpful for bonding. bn and al. sem photos show the river pattern which is bond with tough fracture, bn particles and cnts are also observed. hardness measurement, frictional wear test results reveal that the contents of bn and cnts have apparent influence on the properties of specimens

    單獨添加bn和cnts時，樣品的硬度和耐磨、減摩性能都有不同程度的提高；同時添加bn和cnts浙江大學碩士學位論文時，兩者之間表現出明顯的相互作用:樣品的性能可能高於bn和cnts影響的簡單加合，也可能低於對比樣品（無bn和cnts ）的性能。
  10. The composition and structure of the films synthesized by mw - ecrpemsd technology were examined by electron probe, edx, afm, xrd, sem, moreover the corrosion resistance of films were detected by anodic polarization. furthermore, the wear resistance of films was tested by frictional wear. the relationship between properties of films and mw - ecrpemsd technology was summarized

    對微波- ecr等離子體增強非平衡磁控濺射沉積工藝制備的薄膜，採用電子探針、 edx 、 aex 、 xrd 、 sem進行成分及微觀結構分析；利用陽極極化測試了薄膜的耐蝕性能；通過摩擦磨損實驗測試了薄膜的耐磨性能；總結了薄膜的特性與制備工藝的關系。