石榴石膜-
Faraday rotation spectra was measured on samples with model cgx - 1 fr test apparatus by ourselves using the magneto - optical modulated double - frequency method. the development on magneto - optical material and devices, especially on rare - earth ion garnet, were reviewed. as a solution to the problem for temperature stabilized and wideband magneto - optical materials which could satisfy the development of magneto - optical devices for integration and miniaturization, a modified liquid phase epitaxy ( lpe ) technique was brought forward to grow thin film yb3fe5o12 onto substrate ybilg or thin film ybilg onto sustrate ybig
本論文工作包括對ybiig 、 ybig系列石榴石薄膜制備的實驗構想、相圖分析、制備工藝分析和配方設置，搭建了液相外延設備；比較系統地研究了ybiig 、 ybig系列石榴石薄膜的生長、測試，首次成功制備了ybig ybiig 、 ybiig ybig ggg系列復合膜，並採用xrd 、 sem 、 epma等方法對所得樣品進行了結構、組分和微區形貌分析，用紫外可見光光譜儀測試了其在可見近紅外波段光吸收。 -
So that film ybig / ggg was grown in proper temperature, then film ybilg was grown onto ybig / ggg. to improve the magneto - optical properties of films, film ybig was grown onto substrate ybilg which was sliced from garnet ybilg and polished. the tests of magneto - optical properties of the grown thin films showed that through combining two types of rare - earth ion garnet films with opposite signs of farady rotation temperature coefficients, high faraday temperature stability was reached due to temperature compensation effect, which indicated of great potential for application
反復實驗結果表明， ybiig薄膜的最佳外延溫度區間比ybig薄膜的低約10以上，因此，根據實驗結果選擇合適的溫度，我們先在ggg上外延生長ybig薄膜，然後在ybig上再外延ybiig薄膜，成功製成了ybiig ybig ggg復合膜結構；為了進一步提高性能，我們還將以前生長的ybiig單晶定向切割制為基底，在其上進行復合外延。
分享友人