The main reasons causing increased chilling tendency of nodular iron are as follows : using metal charge containing trace and alloy elements which can increase chilling tendency ; molten iron being holded at high temperature too long ; abnormal nodularizing and / or inoculation treatment, as well as abnormal composition control
摘要引起球鐵白口傾向大的主要原因是：爐料穩定性差、電爐保溫、球化處理及鐵液成分控制和孕育處理出現異常。 -
In charge of one of major subjects of the national eighth five - year plan, i. e. " study on shotcreting techniques of polyacrylate emulsion cement mortar for impermeability coating of pu ding rcc dam ", the achievement of which has been appraised by the ministry of electric power and evaluated as reaching national leading level. 2. in charge of the major subject aided by the committee of national natural science funds, " study on durability of high bolumes of fly ash concrete ", the first phase achievement of which has been commended by the committee. 3. in charge of one of major subjects of the national ninth five - year plan, i. e. " study on high performance concrete in marine engineering, design and construction ". 4. acting as one of editors - in - chief of " technical specification for abrasion and cavities resistance of concrete in hydraulic structures ", which is issued by the ministry of water resources. 5. by providing the repairing and strengthening schemes on seepage and cracks of the basement of nanjing lukou international airport, the air traffic opening of the airport was ensured as scheduled. 6. consulting services on techniques of high performance and abrasion - erosion resistance concrete for three - gorges project, anti - corrosion of reinforced concrete strutures for the ore port of shanghai baoshan iron and steel works, mass fly ash concrete for jiangyin yangtze river bridge and pumping concrete for nanjing yangtze river second bridge
主持國家「八五」攻關項目「普定碾壓混凝土壩上游面丙乳砂漿防滲層大面積施工工藝研究」 ，成果通過部級鑒定，評價屬國內領先水平； 2 .主持國家自然科學基金重大項目「高摻量粉煤灰混凝土的長期性能研究「 ，階段成果獲國家自然科學基金委通報表彰與獎勵； 3 .主持國家「九五」攻關項目「海工高性能混凝土成套技術研究」 ； 4 .水利部「水工混凝土抗沖磨防空蝕技術規范」的主編之一； 5 .為南京祿口國際機場地下室修漏與裂縫補提出技術方案被采納並實施，為機場如期通航作出貢獻； 6 .為三峽工程抗沖磨高性能混凝土技術、上海寶鋼礦石碼頭鋼筋混凝土防腐蝕技術、江陰長江大橋大體積粉煤灰混凝土技術、南京長江二橋泵送混凝土技術等提供咨詢建議。 -
In order to decrease chilling tendency, it is suggested to shorten holding time of molten iron at high temperature ; adopt nodularizing alloy with low rear earth content ; reduce trace elements and bismuth contents of the metal charge
為減小球鐵的白口傾向，建議：縮短高溫停留時間；採用低稀土球化劑；加強爐料控制，減少微量元素，避免鉍量過高。 -
The fitness of four negative electrode materials such as al, fe, zn, cd, and of six membranes materials : microfiber glass mat separator, polyethylene, polypropylene, polyvinyl chloride, vinylon, soapnated cellulose acetate, and of four current collects : carbon fiber ; nickel foam ; nickel foam sthongthened by iron wire net, punched silver grid in the super - iron alkaline batteries was comparatively studied. the influence of two storaged method ( with and without electrolyte ) and two impurities ( zno, fe ( oh ) 3 ) to the experiment cell ' s self - discharge nature was also comparatively studied. at last, the nature of discharge. structure and electrochemistry of experimental cell with k2feo4 as cathode active material prepared by three different methods : high temperature reaction, hypochlorite oxidizing and electrolysis, was comparative ly studied. we can conclude : i ) the open - circuit potential and the flat of work potential and the percent of capacity of k2feo4 till 1. 0v during the discharge at constant load of experimental cells decreased by the order of al / k2feo4, zn / k2feo4, cd / k2feo4, fe / k2feo4. as for the nature of charge - discharge cycle, cd / k2feo4 fe / k2feo4 zn / k2feo4. in water solute electrolyte, although al / k2feo4 can n ' t be used as storage battery, it have great potential as primary cell or storage cell from the aspect of its discharge capacity. discharge power
採用組裝實驗電池、 x -射線衍射（ xrd ）和循環伏安（ cv ）的方法，從實驗電池的放電特性、充放電循環特性、自放電特性，不同高鐵酸鹽的結構特性和電化學特性幾個方面，對4種金屬負極材料（ al 、 fe 、 zn 、 cd ） 、 6種隔膜材料（復合玻璃纖維、幅射接枝聚乙烯、改性聚丙烯、聚氯乙烯、維尼綸無紡布、皂化再生纖維素） 、 4種集流體材料（泡沫鎳、以鐵網為加強層的泡沫鎳、切拉銀網、炭纖維編織網）在堿性高鐵電池中的適用性進行了比較研究；對2種雜質組分（ zno 、 fe （ oh ） _ 3 ）和2類不同貯存方式（干、濕）對實驗電池自放電特性的影響進行了比較研究；對3種方法（高溫固相反應、次氯酸鹽氧化、直流電解）所制k _ 2feo _ 4的實驗電池的放電特性、結構特性和電化學性能進行了比較研究。 -
Due to their high oxidation, multiple electron transfer, and high intrinsic energy, we refer to the cells containing fe ( vi ) compounds as " super - iron " batteries with more energy capacity compared to conventional alkaline batteries. the three charge reduction of fe ( vi ) represents a high energy and capacity source of cathodes, and the products ( ferric oxide ) have been considered as an environmentally benign substance
如果fe （ ）化合物作為電池的陰極材料時，其氧化反應為3電子過程，且反應產物為fe _ 2o _ 3 （鐵銹） ，與一般傳統堿性電池相比，它是一種高能，而且放電產物對環境無污染的綠色電池，目前，它的研究已成為電池研究領域的一個熱點。