  1. The welding performance of homemade wear - resistant cast steel has been studied base on the weldability tests, the repair welding procedures of wean - resistant cast steel ( abrasion - plates ) have been made up, the results show that satisfying repair welding quality can be attained with such welding conditions as the low hydrogenous alkalescent welding rod, preheating and slow cooling, strictly maintaining the interbedded temperature of 250 ~ 300 and controlling welding technique

    通過對其焊接性能的試驗研究，制定了該類鑄鋼件（磨耗板）的補焊工藝：低氫型堿性焊條，預熱與緩冷相結合的工藝措施，嚴格控制層間溫度（ 250 ~ 300 ）及焊接工藝規范，可獲得滿意的修復質量。
  2. Before repairing, basing on the actual working condition, concerning the weldability, stress and deformation issues, the scheme of the cold welding technology whose essential being gtaw, low temperature preheating, postweld hammer the welded seam was established

    修理前，圍繞兼顧解決焊接性、應力和變形問題，結合實際施工條件制定了以手工鎢極氬弧焊、鎳基焊絲、焊前低溫預熱、焊后錘擊焊縫為要素的冷堆焊工藝。
  3. Mag welding solid wires for low temperature service steel

    低溫鋼用mag焊接焊絲
  4. Mag welding for 12ni14 low temperature steel heat exchanger

    14低溫鋼換熱器的混合氣體保護焊
  5. Thermosetting powder coating of low - temperature curing type is a newly - developed powder coating which is used on the things that are not suitable for high - temperture baking. this type of powder coating opens up wider application by lowering curing temperature to 108 - 130. it can be used for surface coatings on such things as flaw detectors, auto water tanks, springs, electrical appliances with coils, instruments, equipment with tin welding seams. it can also be used on the products made of aluminum and magnesium materials, glass, plastics and wood etc

    低溫固化型粉末塗料是針對那些不宜高溫烘烤的產品，而最新研製的新品種，它不僅具備一般粉末塗料的特徵，而且可以把固化溫度降低到108 - 130 ，從而拓寬了粉末塗料的應用領域；適用於擦傷機械、汽車水箱、發動機、彈簧、線圈電器、儀器儀表、錫焊條接縫設備、鉛鎂材質、玻璃、塑料、木材等製品的表面塗裝。
  6. Flux cored wires for gas shielded and self - shielded metal arc welding of mild steel, high strength steel and low temperature service steel

    低碳鋼高強度鋼和低溫鋼用氣保護和自保護金屬電弧焊用管狀焊絲
  7. The maximal power outputs of 37. 0 mw / cm2 and 30. 0 mw / cm2 for the p - and n - type laminated materials respectively at the temperature difference 490 have been experimentally obtained, which are about 2. 5 and 3. 0 times those of - fesi2. chemical analyses show that the interface failure between the bridge alloy and the semiconductor bi2te3 results mainly from the eutectic mixtures with low melting point and brittle compounds formed during welding and long time annealing at 190. it is found that the electrical properties of a laminated structure are mainly controlled by the wettability of the bridge alloy on the semiconductor surface

    發現： 1 ）疊層材料具有明顯優于均質材料的熱電性能，在490溫差下， p -型和n -型疊層材料的最大輸出功率分別達到37 . 0和30 . 0 （ mw / cm ~ 2 ） ，是同類型均質- fesi _ 2的2 . 5和3倍； 2 ）在焊接過程和190長時間退火處理過程中，焊接過渡層合金和基體半導體（特別是bi _ 2te _ 3 ）之間存在明顯的元素相互擴散，從而在過渡層中形成一些低熔點共晶體和脆性化合物，這是導致疊層材料破壞的主要原因； 3 ）焊接過渡層合金與半導體基體之間的潤濕性是影響界面層電性能的主要因素。
  8. The effects of the tested condition, e. g. environment humidity, drying temperature, dew point of shielding gas, etc, on diffusible hydrogen content of the domestic electrodes for welding mild and low alloy steels is analyzed and compared with that of the foreign electrodes

    摘要採用水銀法研究了環境濕度、烘乾溫度、保護氣體露點等測試條件對焊縫擴散氫含量的影響，分析了我國碳鋼及低合金鋼焊條中的擴散氫含量，並且與國外焊條的擴散氫含量進行了對比。
  9. The fracture energy of cu / - aiodiffusion - welded joints was greatly increased by the introduction of the thin film nb interlayer whereas diffusion welding can be performed at a relatively low temperature ( 900 ). the increase in fracture energy of the joints with nb film interlayer was attributed to the strong abhesion of nb to - aio combined with larger plastic deformation in the metal side during fracture tem observations showed large amounts of dislocations existing at the interfacial regions

    本文主要內容就是概括地介紹了國內外關于擴散連接接頭行為數值模擬的發展現狀；主要包括界面孔洞消失過程、接頭元素擴散與反應層的形成、接頭變形與應力行為的數值模擬，以使人們能夠定性或半定量的分析擴散連接因素對接頭性能的影響。
  10. The effective methods to avoid the cracking include lowering strictly the content of impurity and adopting low temperature welding process

    有效的改進措施是嚴格控制雜質含量、將高溫焊接工藝改為低溫焊接工藝。
  11. Ludong turbocharger ceramic is seeped into the surface of metal under low temperature in this way the capacities of anti - welding wear, duration reliability and oil consumption are highly improved

    低溫真空狀態下，陶瓷材料與金屬基體互相打散使金屬表面硬度和韌性同時提高。