  1. ( 3 ) the most principal factors that influence the supersonic atomization process include the flow ratio of the gas - liquid metal ( gmr ) value, the flow of atomizing of gas and the range of the inverse vortex taper. the more of the value of three factors, the more advantage they are for the atomization and the more fine the powders are. ( 4 ) the produced powders are the best in efficient atomization efficiency, particle diameter, particle shape and dispersion when the solder alloy is zhl63a, atomizing medium is n2, the protrusion h = 6. 0mm, atomizing gas pressure p = 100mpa, over - heat temperature t = 167 ( t = 350 )

    研究結果表明： （ 1 ）超音速霧化器的氣體流場在導液管下端形成一個倒渦流錐，在二維空間上呈軸對稱的雙峰分佈，負壓形成於這個倒渦流錐內； （ 2 ）修正後的霧化氣體速度公式可以滿足超音速霧化的要求； （ 3 ）影響超音速霧化工藝最根本的因素有氣液質量流率比（ gmr ）的大小、霧化氣體流量和倒渦流錐范圍，三個因素的值越大，對形成細粉越有利； （ 4 ）在焊錫合金為zhl63a ，霧化介質微n _ 2 ，導液管突出高度取h = 6 . 0mm ，霧化氣體壓力取p = 1 . 0mpa ，合金過熱度取t = 167 （ t = 350 ）時，所制得的粉末在有效霧化率、顆粒球形度、粒度及其離散度三個方面綜合性能最好。
  2. The conclusions are as follows : ( 1 ) high - pressure water - atomization can be used to produce a pre - alloyed steel powder with high apparent density, high green strength, size - stability after sintering and low hydrogen - loss content ; ( 2 ) the higher smelting temperature and / or water pressure, the finer particle size of steel powders ; ( 3 ) when the atomization angle holds in a reasonable value ' s range the obtained powder will have a better particle size distribution ; ( 4 ) an optimum atomization technological parameters : liquid steel flux, water pressure and water prick angle was obtained ( 5 ) reduction variables ( temperature, holding time, material - bed ' s thickness and reducing gas flux ) have a significant effect on the particle agglomeration and properties of final powder was given ( 6 ) different alloying methods were developed to modify properties of ferrous powder materials and hence to broaden its applications in ferrous powder metallurgy industry

    本文系統研究了水霧化預合金鋼粉生產工藝及合金化方法對鐵基粉末冶金材料性能影響，詳細研究了冶煉、霧化、還原工藝參數對預合金鋼粉化學成份和物理性能影響，並得出如下結論： （ 1 ）採用高壓水霧化技術可用於生產高密度、高強度、尺寸穩定性的低氫損含量的水霧化預合金鋼粉。 （ 2 ）冶煉溫度越高，高壓水壓力越大，所得生粉顆粒粒度越細。 （ 3 ）水錐角調整在一個適當角度范圍內可獲得粒度組成較好的生粉。
  3. Analyzing the finished sprinkler products in our country and overseas, testing all sorts of sprinkler parameters ( elevation of sprinkler, diameter of the nozzle, working pressure, the range of water, uniformity of spray irrigation, intensity of spray irriga tion, the degree of atomization ) so as to compare with the new style sprinkler install with pressure adjuster

    對國內和國外的一些中壓噴頭成品進行分析、研究、測試取得實際的各項參數（噴射仰角、噴嘴直徑，工作壓力、射程、噴灌均勻度、噴灌強度、霧化程度）以便和安裝「壓力調節器」后的噴頭進行比較2