vermicular graphite 中文意思是什麼
vermicular graphite
解釋
蠕蟲狀石墨- vermicular : adj. 1. 蠕蟲（狀）的；蠕動的。2. 蟲蛀形的，蟲跡形的。
- graphite : n 【化學】石墨，黑鉛，炭精；鉛筆粉。 colloidal graphite膠體石墨。 graphite electrode 【電學】石墨...
-
For the manifold of sedan engine, the hest thermal fatigue properties can be obtained by keeping the percent of vermicular graphite at about 50 %, therefore it shouldn ' t he considered that the lowest e. g. percent limit of 50 % specified in chinese vermicular iron standard is too lower, and it is also not proper to take the v. g. percent as the basis for judging the level of production technology
摘要對轎車發動機排氣歧管而言，蠕化率控制在50 %左右可以獲得最佳的抗熱疲勞性能，因此不能認為我國的蠕鐵標準中規定的蠕化率高於50 %的要求偏低了，也不能把蠕化率的高低作為衡量工藝水平的依據。 -
Dry sliding friction characteristics of vermicular graphite iron
高速干滑動下材料摩擦學性能的研究進展 -
The fracture toughness values of vermicular graphite cast iron specimen subjected to four different heat treatment methods were tested and compared
摘要比較四種熱處理方法下蠕墨鑄鐵試樣的斷裂韌度。 -
How to control and check percentage of vermicular graphite was described, and some suggestions to prevent vermicularizing effect degeneration were offered
介紹如何控制、檢測蠕化率，並對如何防止蠕化衰退提出建議。 -
The influences of furnace charges, chemical composition, quality of vermicularizing alloy, holding duration after vermicularizing treatment and tapping temperature on percentage of vermicular graphite were discussed
摘要討論爐料、化學成分、蠕化劑質量、處理后包內保留時間和溫度對蠕墨鑄鐵蠕化率的影響。 -
The metamorphous graphite in the section center of heavy section s. g. iron castings is superspheroidal graphite, and not the product of degeneration along the direction from shperoidal graphite to vermicular or flake graphite
大斷面鑄件中心的變態石墨是過球化石墨，而不是球狀石墨向蠕蟲狀石墨或片狀石墨方向衰退的產物。 -
The results indicate that the fracture toughness is influenced markedly by the different base structure of vermicular east iron and by the form of graphite ; unlike steel, the fracture toughness of vermicular cast iron increases with the yielding strength, while drops drastically with the increase of ratio of graphite grain length to thickness
試驗結果表明，蠕墨鑄鐵的斷裂韌度受不同基體組織的影響比較明顯；受不同石墨形態的影響顯著，與結構鋼不同，蠕墨鑄鐵的斷裂韌度隨材料的屈服強度增大而增大，隨石墨顆粒的長厚比增加會急劇下降。 -
Vermicular iron has graphite shape between flake graphite of gray iron and nodular graphite of nodular iron, tensile strength higher than that of gray iron by 70 %, and some lower than that of nodular iron, so is a sort of excellent material for structural parts
摘要蠕墨鑄鐵的石墨形狀介於灰鐵的片狀石墨與球鐵的球狀石墨之間，抗拉強度高於灰鑄鐵70 % ，略低於球墨鑄鐵，是結構件的優良材料。 -
It was showed that the basic varying law of graphite morphologies is as follows : with increasing of growing rate of graphite crystal along direction of [ 0001 ], the morphologies of graphite change from flack shape vermicular shape spheroidal shape explosive shape superspheroidal shape
研究得出，鑄鐵中石墨變態的基本規律是：隨著石墨晶體沿[ 0001 ]方向生長速度的增加，石墨由片狀石墨蠕蟲狀石墨球狀石墨開花狀石墨過球化石墨。
分享友人