塑性收縮開裂 的英文怎麼說

中文拼音 [sùxìngshōusuōkāiliè]
塑性收縮開裂 英文
plastic shrinkage cracking
  • 塑 : 動詞（塑造） model; mould
  • 性 : Ⅰ名詞1 （性格） nature; character; disposition 2 （性能; 性質） property; quality 3 （性別） sex ...
  • 收 : Ⅰ動詞1 （把攤開的或分散的事物聚集、合攏） put away; take in 2 （收取） collect 3 （收割） harvest...
  • 縮 : 縮構詞成分。
  • 裂 : 裂動詞[方言] （東西的兩部分向兩旁分開） open
  • 收縮 : 1 （由大變小; 由長變短） contract; shrink 2 （緊縮） concentrate one s forces; draw back 3 take u...
  1. We research the causes of concrete cracking, develop the high performance anti - cracking additive, optimize the concrete mix and construction techniques, increase the stability of concrete volume by shrinkage compensation, enhance splitting tensile strength, and can meet demand of high workability of fresh concrete. in the study, a thorough investigation of this problem is made from all points of view, with the aid of various modern measurement & testing technology and different theories & methods in surface physical chemistry, structural chemistry, solid - state chemistry, composite materials, fracture mechanics, etc. our research results have shown that the various shrinkage of concrete cause concrete cracking in building engineering, such as autogenous shrinkage, dry shrinkage, temperature shrinkage, plastic shrinkage, carbonized shrinkage, etc

    目前，解決混凝土開裂的方法是綜合的，我們調查研究了混凝土開裂的原因，開發研製了高性能抗裂外加劑，優化混凝土的設計和施工方法，並通過補償收縮達到混凝土體積穩定，提高抗裂強度，滿足混凝土拌和物高工作性能的要求。本研究採用多種測試技術，應用表面物理化學、結構化學、固體化學、復合材料學、斷裂力學等多學科的理論與方法，從不同的角度進行深入的研究和探討。通過調查研究建築工程中出現的混凝土開裂、滲漏問題，發現混凝土在非荷載作用下開裂主要是由混凝土的自收縮、乾燥收縮、溫度收縮、塑性收縮、碳化收縮等各種收縮變形引起的。
  2. Some manufacturers use fiber reinforcement to control plastic shrinkage and thermal cracking

    一些生產商使用纖維增強來控制塑性收縮和熱脹開裂。
  3. In the paper the effects of the made parameters, the main materials and environmental conditions on plastic shrinkage cracking were investigated. it can be concluded as following : 1 ) there was a critical w / c ratio of maximum plastic shrinkage cracking between lower and higher w / c ratio of concrete mixtures made with the same cement content per cubic meter, concretes with lower or higher w / c ratio being less prone to plastic shrinkage cracking and the w / c critical ratio critical of maximum plastic shrinkage cracking being about 0. 5

    本文研究了配製參數、主要原材料以及環境條件對新拌混凝土塑性收縮裂縫的影響，結果表明： 1 ）單方混凝土水泥用量一定時，較低水灰比和較高水灰比對應的混凝土拌合物不易開裂，而中間某一臨界水灰比對應的混凝土拌合物開裂較嚴重，這一臨界水灰比為0 . 5 ；單方混凝土水用量或水泥漿量一定時，混凝土拌合物的塑性開裂趨勢與上述情況相似，但臨界水灰比分別為0 . 45 - 0 . 4和0 . 4 。
  4. Therefore, the technology combining steel fiber with expensive agent is appropriate to the plastic shrinkage and cracking of concretes

    因此，採用膨脹劑與鋼纖維的復合技術是防止混凝土發生塑性收縮開裂的比較理想的技術措施。
  5. The judge criterion of plastic shrinkage cracking for cement based material was studied through the testing of plastic tensile strength and plastic shrinkage capillary stress of cement mortar and concrete

    摘要採用自行設計的塑性抗拉強度、塑性收縮開裂應力測定裝置測試了水泥砂漿、混凝土塑性抗拉強度和塑性收縮開裂應力。
  6. With a slab test of restricted shrinkage, the effect of polypropylene fiber, steel fiber and expansive agent on early - age plastic shrinkage and cracking of concretes with high content mineral admixtures is investigated

    摘要採用平板限制收縮試驗法，研究了聚丙烯纖維、鋼纖維與膨脹劑及其復合技術對大摻量礦物摻合料混凝土早期塑性收縮開裂的影響。
  7. The results shows that the combined use of fibers and expansions was superior to the use of fibers or expansion agents alone in reducing the amounts of plastic shrinkage cracks and diminishing the size of cracks, and it improved the resistance to plastic shrinkage crack extremely

    文章研究了聚丙烯纖維和膨脹劑復合對砂漿塑性收縮裂縫的影響，結果顯示，纖維與膨脹劑復合，在減少塑性收縮裂縫數量和細化裂縫兩個方面均優于纖維或膨脹劑的單獨作用，砂漿抵抗塑性收縮開裂能力顯著提高。
  8. 2 ) to a certainty of sand percentage, concretes with moderate critical sand percentage which changed in about 36 % - 43 % were more sensitive to plastic shrinkage cracking than concretes with lower or higher sand percentage. 3 ) concrete made with lower strength grading cement was more prone to plastic shrinkage cracking than that of concrete made with higher strength grading cement

    4 ）粉煤灰和硅灰對混凝土塑性收縮裂縫的影響與拌合物的實際水膠比有關，存在一個水膠比界限，在此界限之上，摻入粉煤灰或硅灰的混凝土較易開裂，在此界限之下，粉煤灰或硅灰高性能混凝土對塑性收縮裂縫具有抑制作用。