易磁化軸 的英文怎麼說
中文拼音 [yìcíhuàzhóu]
易磁化軸
英文
axis of easy magnetization-
The results showed that the microstructure of as - deposited tbdyfe ii 1ms were amorphous and the crystal of tbfe2 were found in films after annealing at 500. annealing films in vaccum could improve the saturation magnetization ms and the susceptibility, decrease the coercivity and the saturaion field, and make the direction of the magnetic moments parallel to the film plane
結果表明,制備態薄膜為非晶態結構,經過500真空退火熱處理后,薄膜出現了tbfe _ 2的結晶物,薄膜的矯頑力和外場的飽和磁場大大降低,飽和磁化強度增強,初始磁化率提高,易磁化軸轉向膜面。The main reason are as following : on one hand, the nd - rich phases in the hydrogen desorpted powders is so brittle that they are easily milled too fine and some are run off seriously, and then inducing low density. on the other hand, the alignment of the magnets prepared by hydrogen desorption are much low. so the hydrogen desorption process should be modified, and the solution methods can be the substitution of traditional ingots with strip cast, the enhancement of the alignment magnetic field and the addition of nd - rich phase or ( and ) lubricant before the press
主要原因是hd磁粉中的富釹相較脆,在球磨時容易被磨成超細粉而造成過量流失和使磁體燒結不夠緻密;另外一個原因是hd法燒結磁體的易磁化軸的取向度較低,為了提高hd磁體的b _ r和( bh ) _ ( max )可對hd工藝進行改進,改進的方法可以是用鑄片代替鑄錠,提高成型磁場強度以及在磁粉成型前加富釹相和潤滑劑。If the magnetic anisotropy of the magnetostrictive layer is much larger than that of the soft layer, the magnetic hysteresis and magnetostriction of the ecmm magnetized along the easy axis of the magnetostrictive layer are different from those of hard axis of the magnetostrictive layer
當磁致伸縮層磁各向異性與軟磁層磁各向異性相差較大時,沿磁致伸縮層的易軸方向或難軸方向磁化,多層膜的磁學及力學性質差別較大。To measure the size of ba - ferrite fine magnetic particles, electromagnetic field was employed to drive the fine magnetic particles displace in order, then scanning electron microscope ( sem ) was used to observe and measure the size of ba - ferrite fine magnetic particles
為了迅速、準確地測定鋇鐵氧體磁粉顆粒的厚度、直徑和厚徑比的統計分佈,採用對磁顆粒施加外加電磁場的方法,使各個磁顆粒的易磁化軸方向趨於一致,並用掃描電子顯微鏡觀察鋇鐵氧體磁粉顆粒。分享友人