最大拉伸強力 的英文怎麼說
中文拼音 [zuìdàlāshēnqiánglì]
最大拉伸強力
英文
true tensile strength-
The results from x - ray diffraction demonstrated that pp / mmtome was a fully intercalated nanocomposite, pp / mmtom and pp / ommt were partly intercalated nanocomposites, but the intercalation effect of pp / mmtom nanocomposite was better ; the crystallization characteristics of pure pp and pp / mmt nanocomposites were investigated by dsc, waxd and pom. the result of these testing showed that mmt nano - layers acted as nucleating agents for the crystallization of pp, the addition of mmt had effect on the crystallization process, leading the increasing of crystallization temperature crystallization rate and crystallinity, but also the dimension of spherulite reduced. but the formation of pp crystal did n ' t change, the formation of pp crystal in three pp / mmt nanocomposites and pure pp were a - form on the whole ; influences of three sorts of mmt on mechanical properties of pp / mmt nanocomposites were studied, as a result, the addition of mmt comprehensively improved mechanical properties of pp : notched impact strength, tensile strength and flexural properties were all increasing, but the extent of increasing were n ' t large
通過xrd分析比較這三種pp mmt納米復合材料微觀結構得到, pp mmt _ ( ome )屬于完全插層, pp mmt _ ( om )與pp ommt的插層程度相近,但是pp mmt _ ( om )相對較好;通過對純pp和三種pp mmt納米復合材料的結晶性能研究發現,蒙脫土納米片層對pp結晶產生明顯的異相成核作用,結晶能力增強,使pp的結晶溫度和結晶速率提高,結晶度增加,球晶晶粒細化,但是沒有改變pp的結晶形態,三種pp mmt納米復合材料的結晶形態都屬于晶;通過對pp mmt納米復合材料的力學性能測試得知,蒙脫土的加入全面提高了pp的力學性能,缺口沖擊強度、拉伸強度和彎曲性能都有一定程度的提高,浙江{ _業大學碩十學位論文摘要但是提高幅度都不是很大,不過ommt 、 mmtom和mmtc ) me三種蒙脫土對pp力學性能有著不同的改性作用,其中pp / mmtom最好, pp月邊mto崛次之, pp / ommt最低,這種情況主要是由蒙脫土對pp結晶性能的影響和蒙脫土的納米改性作用造成的。Textiles. seam tensible properties of fabrics and made - up textile articles. part 2 : determination of maximum force to seam rupture using the grab method
紡織品.織物和成衣接縫拉伸特性.第2部分:用抓樣強力試驗方法對接縫裂開最大拉力的測定En iso 13934 - 2 textiles. tensile properties of fabrics. part 2 : determination of maximum force using the grab method
紡織品.織物拉伸特性.第2部分:用抓樣強力法對最大作用力的測定Abstract : this paper researches into the complex adhesive , which was mainly made by the soy protein isolate ( spi ) and polyvinyl alcohol or polyvinyl acetate. different composition of protein and polymers can perform different characters, together with other ingredients. the factors, which are related to the first adhesive strength and adhesive strength, are mainly studied and discussed. the first adhesive strength of the complex adhesive is related to the content of spi, and the adhesive strength is related to the content of the complex adhesive. on the basis of the researching, we can make the plant fibre box for food in the future
文摘:對大豆分離蛋白?聚乙烯醇、大豆分離蛋白?白乳膠復合膠粘劑進行了研究,採用不同混合比例及添加其他助劑,得到較好性能和可生物降解的復合膠粘劑,為製造一次性植物纖維快餐盒打下基礎.主要研究了影響這種復合膠粘劑粘接木塊的初粘力(剪切和拉伸強度)和粘接強度的因素,實驗表明: 9 . 2 %濃度的大豆分離蛋白的初粘力(剪切和拉伸強度)優於10 %濃度的聚乙烯醇膠和33 %濃度的白乳膠;大豆分離蛋白復合膠粘劑的初粘力主要與大豆分離蛋白含量有關,其最終粘接強度與膠液固含量正相關Tensile strength corresponds to the maximum tensile stress that may be sustained by a specimen
抗拉強度是指樣品可能承受的最大拉伸應力。The test result of the rene95 sample showed that the maximum ultimate tensile strength can be as high as 1400mpa and has reached 97. 9 % of that of the sample fabricated by powder metallurgy ( pm ). the plastic elongation of the test sample can even exceed that of pm. the ultimate tensile strength of the test sample grown from single crystal substrate has surpassed 6 % of that of grown from the stainless steel substrate, at the same time the plastic elongation surpassed 40 %
對成形試樣的力學性能測試結果表明,強度方面_ b最大為1400mpa ,已經達到了粉末冶金的97 . 9 ,塑性方面甚至超過了粉末冶金的水平;以單晶為基材的成形試樣其最大拉伸強度要比不銹鋼為基材的試樣高6 ,延伸率要高40 。When the a3 steel specimen was operated by tension - torsion - tension action, both the yield limit and strength limit had very large improved compared with that of monotonic tension. the improve scope of the yield limit could be 109. 36 %, the strength limit could be 56. 26 %. the yield limit value reached the max
A3鋼試件在拉伸-扭轉-拉伸作用下的力學性能與單一拉伸相比,試件的屈服極限和強度極限都有很大提高。屈服極限提高幅度最高可達109 . 36 ,強度極限提高幅度最高可達56 . 26 。分享友人