淬火破裂 的英文怎麼說

中文拼音 [cuìhuǒpòliè]
淬火破裂 英文
hardening failures
  • 淬 : 動詞（淬火） temper by dipping in water, oil, etc. ; quench
  • 火 : fire
  • 破 : Ⅰ動詞1 （完整的東西受到損傷） be broken; be damaged 2 （使損壞） break; break down; damage 3 （使...
  • 裂 : 裂動詞[方言] （東西的兩部分向兩旁分開） open
  • 破裂 : break; fracture; burst; split; rupture; crack
  1. Smooth tempered glass is manufactured by heating up float glass to swiftly and uniformly, with this special heat treatment and quenching process which increases glass strength up to four to five times vs, annealed glass, in case stresses beyond its capacity, smooth tempered glass simply disintegrates into innumerable small pieces, significantly reducing the risk of serious injury

    鋼化玻璃是將浮法玻璃經過物理性淬火處理，使其表面形成均勻的壓應力，而內部則形成張應力，從而有效的提高了玻璃的抗彎和抗沖擊性能，強度達到了普通玻璃的3 - 4倍，當其破碎時則分裂成均勻純角不易傷人的小顆粒，使其成為一種現代生活中理想的安全玻璃。
  2. Analysis which was based on the fracture mode of mould in wire - cutting processing, and the results show that the partial - quenched of mould, the non - uniformity of blank temperature and the carbide segregation inside the material are the main reasons of deformation and cracking

    摘要通過分析在線切割加工中模具的破壞形式表明：模具不完全淬火、坯料溫度的不均勻分佈、材料內部的碳化物偏析是模具變形與開裂的主要原因。
  3. The network carbide and acicular martensites that existed in the microstructure of the root grooves of the spline due to improper carburating and quenching process of the shafts, led to the initiation and propagation of the intergranular microcracks and were the main reason that caused the early fracture of the shafts

    由於滲碳淬火工藝不當，在二軸花鍵槽根部的組織中產生了網狀破化物和粗大的針狀馬氏體，在外力作用下形成沿晶顯微裂紋並擴展，是導致二軸疲勞斷裂的主要原因。