熱油淬火 的英文怎麼說
中文拼音 [rèyóucuìhuǒ]
熱油淬火
英文
hot oil quenching-
Induction heated oil tempered spring wire is a kind of new technical material which has been developed since 1980s. it can be heated by means of eddy induced into itself through electromagnetic coil and this method is mainly used in surface quenching. with correct designing and reasonable current frequency, induction coil and heat treatment process selected, as well as plc controlling applied, the wire can be uniform heated along cross - sectional and longitudinal direction and can be quenched and tempered continuously
應加熱油淬火-回火彈簧鋼絲,是二十世紀八十年代發展起來的新技術材料,在國外稱為itw induction heat oil tempered spring wire 。是通過線圈電磁感應鋼絲本身產生的渦流進行加熱,通常主要用於表面淬火。經正確設計,選擇電流頻率,合理的感應線圈及熱處理工藝,並實施plc控制,可使鋼絲整個截面及長度上得到均勻加熱,進行連續整體淬火和回火。Process features characteristic of induction heat oil tempered spring wire
感應加熱油淬火-回火線材特點Hot - rolled wire rod for quenched and tempered springs
油淬火-回火彈簧鋼絲用熱軋盤條Product description : this series product has entire auto - lubrication systems and the ordinary two big kinds supplies to select, this machine major parts cancels the needle, cam and the ball bearing all uses the high quality import components, also selects the high quality steel products quenching heat treatment to the main stress components, the essential components uses special phosphorus processing, the foreign dew components all adopts special - purpose seal - up device and drains the oil the measure, therefore, entire causes machine throughout to locate the lubrication is reliable, the revolution is steady, under the high speed low chirp condition works
本系列產品具有全自動潤滑型及普通型兩大類以供選用,本機主要零件勾針,凸輪及滾珠均採用優質進口零件,對主要受力零件亦選用優質鋼材淬火熱處理,關鍵零件則採用專門磷化處理,對外露零件均採取專用密封裝置及排油措施,因此,使整機始終處于潤滑可靠,運轉平穩,高速低噪的條件下工作。Pit remediation & slop oil, industrial water, cutting & cooling oils, hexavalent chromium, acid & alkali with heavy metal content, steel mill & electro filter dust, spent catalysts, tempering salts, solvents recovery and recycling, sludge treatment and minimization, fuel - blending, thermal desorption and transfer centres
廢漿池和廢油、工業污水、巖屑和冷卻油、六價鉻、含重金屬成分的酸堿、鋼廠和電過濾器粉塵、反應過后的催化劑、淬火鹽、溶劑還原和回收、油泥處理和最小化、燃料混合、熱吸附和轉運中心。The changing carbon potential carburization - hot oil matrempering technology of helical bevel gear for automobile driven axle is introduced in this article. the board test and production application show that the technology not only quenchs directly gear after carbrization, but also decreases the heat treatment deformation and raises the contact fatigue life of gear
介紹了汽車驅動橋螺旋錐齒輪的變碳勢滲碳一熱油分級淬火工藝,臺架試驗及生產應用表明,該工藝與專用滲碳淬火掛具相結合,不僅可實現齒輪滲碳后直接淬火,而且熱處理變形小,齒輪接觸疲勞壽命也有所提高。Sino - foreign joint venture nanjing dongwu metal material co., ltd. is a hi - tech enterprise which specially produces and sells induction heat oil tempered spring wire and die pusher rod
中外合資南京東吳金屬製品有限公司是一家專門生產經營感應加熱油淬火-回火彈簧鋼絲冷鐓鋼絲軸承鋼絲異形鋼絲退火磨光定尺線材冷拉鋼絲和模具推桿線材的高新技術企業。Founded in september 1997, the company occupies an area of 35000 square meters and has 50 staffs, including 3 engineers, 2 vice senior engineers and 4 engineers. with the help of some domestic specialists who engaged in the research on induction heated quenching - tempering treatment in weapon and space industries. we developed the first induction heat oil tempered elastic wire production line in china by ourselves. this production line was put use in august 1998, and was enlisted in the spak programme in 2000 serial number : 369, programme code : 00b101d691004
創建於1997年9月,佔地35000平方米,員工50名,其中研究員級高工3名,高工2名,工程師4名。依靠國內一批在軍工企業長期從事感應加熱調質處理研究的專家,自行研製成功國內第一條彈性線材感應加熱油淬火-回火生產線,並於1998年投產。Its upside is heating chamber. its underside is chamber putting work - pieces in or out and oil tank
雙室立式結構,上部為加熱室下部為進出料室及淬火油槽。Due to the rapid heating rate, the time for wire stayed in high temperature zone is very short and no enough time for grain grows largely, hence the structure size of continuously induction heated wire is smaller than that of conventional heated wire and grain size is 2 to 4 level higher. due to the fine grain size, the induction heat oil tempered spring wire can acquire more reasonable comprehensive mechanical properties under same strength
可見,由於加熱快,在高溫停留時間短,組織晶粒來不及長大,因此,連續感應加熱鋼絲的組織晶粒尺寸比一般加熱小,晶粒度高2 - 4級。由於組織晶粒尺寸細小,因此,感應加熱油淬火-回火鋼絲,在同樣強度下,具有更高的綜合b力學性能。Induction heat oil tempered wire and rod can be directly used in the manufacture of spring and pusher and the quenching - tempering process thereafter can be omitted, thus the quality problems such as deformation of workpiece, decarburization, un - stability and un - qualification of mechanical property can be avoided and the quality stability and reliability of product can be improved
感應加熱油淬火-回火鋼絲及線材,能直接用於繞簧和製造推桿,可省去一般材料繞簧和推桿加工成形后的淬火-回火工序,避免了由此帶來的工件變形脫碳及力學性能不穩定甚至不合要求等質量問題,提高了產品的質量穩定性和可靠性。To put work - pieces in or out by hanging, the furnace especially suit heat treatment of work - pieces in the form of long pole and disk
加熱室上端裝有工件夾緊裝置,採用工件吊掛方式可根據用戶需要,採用淬火油槽固定式或移動式結構。分享友人