燒結 的英文怎麼說

中文拼音 [shāojiē]
燒結 英文
firing; fritting; cementation; clotting; agglomeration; agglutination; [冶金學] sintering; nodulize; sinter-roasting燒結廠 ore-sintering plant; 燒結成型 sinter molding; 燒結鍛造 sintering forging; 燒結法 sintering process; 燒結工序 sintering circuit; 燒結機 sintering machine; 燒結劑 agglutinant; 燒結料 sintering feed; 燒結裂紋 sintering crack; 燒結爐 fritting furnace; welding furnace; 燒結設備 agglomerating plant; 燒結鑄石 sintering glass-ceramics; 燒結磚 baked brick
  • 燒 : Ⅰ動詞1 （使東西著火） burn 2 （加熱或接觸某些化學藥品、放射性物質等使物體起變化） cook; bake; hea...
  • 結 : 結動詞（長出果實或種子） bear （fruit）; form （seed）
  1. Beryllium powders with the same particle size and various contents of beo were prepared by pre - sintering - acid washing processes initiatively and the influence of beo alone on o mys of beryllium was observed and some new results have been obtained - compared with the content of beo, the distribution of beo in beryllium has more critical influence on mys ; finely dispersed beo along the grain boundaries and in the matrix results in the dispersion strengthening of beryllium matrix and thereby the higher mys value ; on the contrary, the coarser beo particles clustering on the grain boundaries results in negative influence on o mys

    開創性地用預燒結? ?酸洗工藝制備了相同粒度、不同beo含量的鈹粉，從而開展了beo含量單獨對鈹材_ （ mys ）影響的研究，得出一些新的結果：與beo含量相比， beo在鈹中的分佈狀態對_ （ mys ）的影響更大。沿晶界、晶內彌散分佈的較細小beo對基體鈹有彌散強化作用，使_ （ mys ）即較高；如果beo較粗大地成簇狀聚集在晶界，反而對_ （ mys ）有不良的影響。
  2. The investigation of the effect of temperature field, stress field and the adscititious physical field on the sls can lead to the systematical analysis and elimination of the disfigurements existed in the metal parts prepared by sls

    通過研究激光燒結的溫度場、應力場以及研究外加物理場對激光燒結的影響，可以系統分析和解決激光燒結金屬零件存在的缺陷。
  3. The agglomeration and sintering of fine particles can necessitate a lowering in temperature of operation.

    由於微粒易於聚集和燒結，不得不降低操作溫度。
  4. For noncatalytic operations at high temperature the agglomeration and sintering of fine particles can necessitate a lowering in temperature of operation.

    對於一些高溫非催化操作，由於微粒易於聚集和燒結，不得不降低操作溫度。
  5. ( 2 ) the properties of the material with finer andalusite particle size are superior to those of coarse particle size at lower temperature, but properties of material of fine and coarse particle size have little difference at higher temperature. this illustrates that the andalusite particle size can lower the sintering temperature and that it brings forth not remarkable influence on the property of the material when the material is sintered completely

    （ 2 ）對于不同粒度的原料，在燒成溫度較低的情況下，粒度小的材料性能明顯高於粒度大的材料，但在燒成溫度較高的情況下，兩者差別不大，說明原料粒度減小能降低製品的燒結溫度，但在制品均完全燒結的情況下對材料性能影響不大。
  6. We also attainted mosi2 / sic composite by using melting mosi2 infiltrated sic body which shaped by sic powder. the result show that the diameters of sic particle and shaping methods have effect on the composite ' s microstructure and properties

    另外，嘗試了用mosi _ 2在2050下浸滲直接由sic粉體成型的坯體制備mosi _ 2 / sic復合材料。採用sic顆粒的級配有利於提高坯體密度，但是降低燒結體的緻密度。
  7. Burn - back resistance test

    抗燒結試驗
  8. Sintered bimetal material - determination of shear strength

    燒結雙金屬材料剪切強度的測定方法
  9. The material was sintered at 1050 for three hours to get the porous artificial bone, that its apparent porosity was54 %, its volume density was 1. 28 g / cm3, and its bending strength was 13. 25mpa. the results showed that the sintering temperature was reduced by adding bioglass

    本研究採用含生物玻璃前驅體粉末原料，添加檸檬酸造孔劑，模壓成型，在1050燒結保溫3小時，獲得了顯氣孔率為54 、體積密度為1 . 28s cm ~ 3 、抗彎強度為13 . 25mpa的多孔hap人工骨材料。
  10. Using in situ formation of ternary boride base cermets hard phases through chemical reactions and sinterbonding onto steel substrates though liquid sintering we successfully prepared a kind of ternary boride base cermet

    摘要通過化學反應將原料粉來生成三元硼化物硬質相併通過液相燒結燒與鋼很好的結合，用這種工藝成功地在鋼基體上塗覆了預壓制的三元硼化物基金屬陶瓷。
  11. Materials for sintered neodymium iron boron permanent magnets

    燒結釹鐵硼永磁材料
  12. The shaped briquet was sintered at 1600 for 2. 5 hours under normal pressure and at certain heating rate in si - mo electric furnace

    成型后的坯體置於硅鉬棒電爐中，在常壓、適當升溫速率下於1600保溫2 . 5小時燒結。
  13. To meet the processing requirements before sintering, the pressed briquet was pre - calcined at 1150 to make it possess adequate processing strength at first and then was shaped through precise turning on the numerical control lathe according to the design diagram of the femoral head prostheses of partial hip joint

    為滿足燒結前坯體加工的要求，壓制后的坯體在1150預燒，使其具備一定的加工強度，然後按照半髖關節股骨頭假體的形狀尺寸設計圖在數控車床上進行精密車削成型。
  14. In recent years at iron - making plant of pangang, the coke ratio of pig iron has reduced evidently by insisting on “ burden preparation ” course, improving quality of sinter, raising wind temperature, increasing rich oxygen quantity and injecting abundant pulverized coal into bf. the solid fuel consumption of sinter has been decreased greatly through insisting on using high - quality calces, practising high feed sintering, actualizing many techniques in solving key problems. at the same time, the energy source base management has been strengthened, and energy - saving work has made great progress, profits generated by energy - saving have exceeded a hundred million yuan

    近年煉鐵廠通過堅持「精料」方針，改善燒結礦質量，提高風溫，增大富氧，實施大噴煤，使入爐焦比有明顯下降；燒結堅持用好生石灰，推行厚料層燒結，實施多項技術攻關，固體燃耗大幅度下降；同時加強能源基礎管理，節能工作取得長足進步，節能創效益1億元以上。
  15. Ceramic elements are made by pressing and sintering finely powdered materials.

    陶瓷元件是將仔細研磨的材料經過加壓和燒結製成。
  16. The soft powder fired at high temperature until the ceramic particles melt and coalesce to form a glaze.

    松軟的粉末在高溫下燒結，陶土粒子即溶結成一層瓷釉。
  17. Widely employed in coal mine, downhole coal bunker, coal washery, cement factory, foundary, thermal power plant, sintering plant coal gas factory, fertilizer plant, chemicals plant, aluminium plant, alkali factory, steel works, coking plant, pharmaceutical factory, mine, dock, foodstuff, and feedings process works, concrete process, etc. with bunker, hopper, transmitting pipeline and drawshaft

    廣泛用於煤礦、及井下煤倉、洗煤廠、水泥廠、鑄造廠、火力發電廠、燒結廠、煤氣廠、化肥廠、化工廠、鋁廠、制堿廠、鋼鐵廠、焦化廠、制藥廠、礦山、碼頭、糧食、飼料加工廠、混凝土加工廠等擁有料倉、料斗、輸送管道和礦山溜井的廠礦企業。
  18. Lifepo4 was sintered by solid - state method, we found that the capacity of the sample which was synthesized by codeposition method exhibited high specific capacity ( 142 mah ? g - 1 ) and good cycling performance

    採用高溫固相法制備了lifepo4 ，發現共沉澱制備的前驅體燒結出的材料容量達到142mah ? g - 1 ，循環性能也很好。
  19. As a comparison, ba1. 03ce0. 8gd0. 2o3 - was synthesized by sol - gel method. among these samples, nonstoichiometric samples were synthesized for the first time. the research work involved : the crystal phase of the sinters were determined by xrd ; ionic conduction under different experimental atmospheres was measured by gas concentration cells ; performances of hydrogen - air fuel cells with the sinters as electrolytes and porous pt as electrodes were measured

    用粉末x射線衍射儀鑒定它們的結晶相；在（ 600 1000 ）范圍內，以燒結體作為電解質隔膜，多孔性pt黑為正、負電極， pt - rh合金網為集電極，分別組成氫濃差電池、氧濃差電池及氫?空氣燃料電池並測定了它們的性能，研究了不同氣氛下樣品的離子導電特性及影響燃料電池性能的因素。
  20. Mas precursor powders were uniaxially pressed at 100 mpa employing a lubricated steel cylindrical mold. after sintering at 1450 for 2 hours, single - phase cordierite ceramic is prepared, and its relative density is 95. 1 %

    Mas先驅體粉末在100mpa的軸向壓力下成型后，經1450無壓燒結2小時，得到單相堇青石陶瓷，其緻密度達95 . 1 。