矯頑性 的英文怎麼說
中文拼音 [jiǎowánxìng]
矯頑性
英文
coercivity-
Which have the following advantages : high coercive force, high electric resistance, long - time stability, and economical price
它們具有：高矯頑力、高阻抗、長效穩定性和經濟的價格。Vibrating samples magnetometer ( vsm ) testing implied that yig were of ferrimagnetism, and cerium substitution had effects on saturation magnetization ( ms ), residual magnetization ( mr ) and coercive force ( hc )
Vsm測試結果表明yig屬于亞鐵磁性物質， ce離子的摻雜對飽和磁化強度（ ms ） 、剩餘磁化強度（ mr ） 、矯頑力（ hc ）都有一定的影響。Fe - ni alloy fiber were first prepared in a mixed solution of ferrous and nickelous salts, using kbh4 as a reducing agent. conditions, such as quantity of naoh, concentration of salts, and species of surfactants, of preparation of fe - ni alloy were studied. the result show that fe - ni alloy were soft magnetic materials and they exhibited superparamagnetization at room temperature that have been widely used in industry
本文用液相還原法首次制備出纖維狀的fe - ni合金、球形的fe - co 、 co - ni合金、 fe - co - ni合金粉體材料，並對其性能進行了分析和測試，結果表明：這些合金粒徑小，比飽和磁化強度較大，矯頑力為零，呈現超順磁性，是非晶態的軟磁材料。Magnetic materials - method of measurement of the coercivity of magnetic materials in an open circuit
磁性材料.開路中磁性材料矯頑力的測量方法The effects of the different kinds of rare earths and the doping amount of them on magnetic properties of bafe, 2o19 ultrafine powders ( including the specific saturation magnetization, the specific remanent magnetization and coercive force ) were firstly discussed systematically
首次查明了鋇鐵氧體粉末的磁性能（包括比飽和磁化強度、比剩餘磁化強度和內稟矯頑力）隨稀土元素種類及其摻雜量的變化規律。Having investigated composites of ep coating ultramicro iron using atpu as surface agent, results showed that with increasing amount of atpu, density, complex permittivity ( ) and complex permeability ( ) of composites decreased, and retentivity and coercivity increased
用atpu作表面活性劑制備核殼結構復合粒子時，隨著復合時atpu用量的增加，復合粒子的密度、復介電常數（ ）和復磁導率（ ）逐漸減小，剩磁與矯頑力逐漸增大。The result shows that with the addition of rare earth elements, ultrasonic irradiation and magnetic field, the chemical component, surface configuration, microstructure and properties of electroless co - ni - b and co - fe - b alloy changes remarkably. such kind of change can be described as the followings. firstly the depositing speed of electroless alloy bath is raised while the polarizability and cathodic overpotential are reduced ; secondly the surface quality of the alloy coating and adhesion of the coating and matrix are improved ; thirdly in the coatings the content of the elements in the transient group increases, but the content of cobalt decreased ; fourthly the amorphous structure is transformed to microcrystal structure and polycrystal structure ; fifthly the microhardness and wear resistance of the coating are enhanced ; sixthly coercitive force is reduced, and magnetoconductivity of the coating is increased ; lastly the magnetic intensity of the coating increases with the addition of energy and light rare earth elements such as ce, la and decreases with the addition of heavy rare earth elements such as y. on the other side, when the alloy coatings passes through the heat treatment under the temperature of 250 or 500, their properties will change
結果顯示化學沉積co - ni - b 、 co - fe - b工藝在稀土元素（ ce 、 la 、 y 、 dy ） 、能量（超聲波、磁場）介入后，沉積過程、合金成分、鍍層形貌結構和性能都有顯著變化，表現在：鍍液的陰極極化過電位和極化度降低，沉積速度提高；鍍層的結合力、表面質量改善；鍍層中過渡族元素的含量增加，輕元素硼的含量降低，同時證實了稀土元素與過渡族元素共沉積的可能性；鍍層的顯微結構由非晶態向微晶和多晶態轉變；鍍層的顯微硬度與耐磨性提高，力學性能優化；鍍層的矯頑力降低；磁導率提高；鍍層的磁化強度在能量（超聲波、磁場）和輕稀土元素ce 、 la介入后提高，重稀土元素y介入后降低。Based on recent published research, explanation about the experimental results was also given. remanent polarization and coercive field decreased with the increasing of la content. the crystal structure transformed from tetragonal to cubic when la concentration increased to 28mol %
在薄膜的鐵電性質方面，隨著摻鑭含量的升高，剩餘極化和矯頑場逐漸降低；當鑭含量達到28mol時薄膜的結構從四方相轉變到立方相。1. this product is a new kind machinery induction - type electrical energy appliance. it adopts high coercive force aluminium nickl cobat material to make the special structure magnetic - hanged magnetic - propelled bearing. when it is electrified to operate, interrepulsion is produced between the bearing and the anxle so that it is electrified to operate. interrepulsion is produced between the bearing and the anxle so that it is suspend station. the friction loss is very small. it not only reduces energy exhaustion by a wide mardin, but also prolongs lifetime to 20 years and above
1 dd951型長壽命單相電度表是金雀儀表有限公司新開發的高可靠性民用電度表，本產品系一代機械感應式電能計量器具。採用高矯頑磁力鋁鎳鈷材料制面的特殊結構磁懸磁推軸承，能電動物時軸承與軸之間產生相互斥力合其和處于懸浮狀，運轉磨擦損耗極小，不但便能耗在幅下降，而且壽命可能性延長到二十年以上。Scientists have been devoting to enhance the density of magnetic recording media for years. magnetic materials are expected to be with high coercivity and high saturation magnetization
提高磁記錄介質的密度是人們多年所追求的目標，這要求磁性材料具有高矯頑力和相應的高飽和磁化強度。Baseing on the request of low coercivity and high squareness in application, we had confirmed the main formulation of the lizn ferrite ; during the study of the conventional ceramic process, with the main formula foundation, we mainly studied the influence of ti4 +, co3 + on lowering coercivity and bi2o3, v2o5 on lowering sinter temperature. the results showed bi2o3 good characteristic on lowering sinter temperature and the sample which mixed with 1 % bi2o3 could reduce 40 % coercivity through slowing heating rate and extending the holding time
在氧化物陶瓷工藝技術研究中，按實際應用中低矯頑力、高矩形比的要求，確定了lizn鐵氧體的主配方，在主配方基礎上進行了ti4 + 、 co3 +等離子對降低矯頑力的研究以及添加bi2o3 、 v2o5助熔劑對降低燒結溫度的研究，發現bi2o3具有優良的降低燒結溫度的特性，在添加bi2o3樣品燒結過程中，降低升溫速率，延長保溫時間可以降低40 %左右的矯頑力。The coercivity of ferrite containing cobalt is bigger than that of ferrite containing nickel because of special physical properties of cobalt
而因鈷離子的特殊物理性質，鈷鐵氧體的矯頑力比鎳鐵氧體的要大。The metastable austenitic phase of s s fiber at the interface of the fiber / cu composite would turn back to equilibrium with the interfacial energy and inter stain inducing, when the cu films were separated from s s fiber. so the magnetism value of the s s fiber declined. the information of grain - orientation at the interface of the fiber / cu composite can serve as a mechanism responsible for its declining coercivity, and a part of cu elements diffused into s s fibers
不銹鋼纖維銅復合體去除銅層后，原有的界面能及應力下降，使得原纖維界面處弱磁性的部分亞穩奧氏體，恢復到平衡態，它們對樣品s測試結果不再有貢獻；不銹鋼纖維銅復合體中，處于界面處的纖維晶粒具有很強的軸向取向排列，當晶粒取向性減弱，磁疇轉動的阻力增加，磁體的矯頑力上升。The results indicate that the best annealing temperature is 1100 for 2h. a conclusion has been drawn that when the mol percent of iron is 60 %, the productions of powders and cycle samples have the best magnetic properties
通過對shs粉末樣品和磁環的磁性能測試發現：當反應產物中fe的摩爾分數為0 . 6時，粉末樣品粒徑大小均勻，產物具有較高的比飽和磁化強度和低的矯頑力。X - ray diffraction results revealed that the structure of as - deposited smco film was amorphous and crystallization happened after the films annealed at 500 in vacuum. the magnetic tests of smco thin films showed that its coercivity reduced with the increase of film ' s thickness while the ratio of mr / ms was opposite. the films " coercivity and mr / ms declined after it annealed at 500 because the machanism of magnetization were changed from domain wall nailing into magnetic nuclear forming
研究結果表明，由於雜質fe的摻入降低了smco薄膜的磁性能；制備態smco薄膜為非晶態結構，矯頑力hc隨著薄膜厚度的增加而減小，剩磁比mr ms隨膜厚增加而增加；經過500真空退火熱處理后，薄膜出現smcos的結晶物，矯頑力hc降低， mr ms減小，磁化機制由疇壁釘扎類模型轉為形核類模型。Test method for magnetic properties of high - coercivity permanent magnet materials using hysteresigraphs
使用磁滯曲線繪制儀測試高矯頑磁力永磁材料磁性能的方法Identification cards - recording technique - part 2 : magnetic stripe - low coercivity
識別卡.記錄技術.第2部分:磁條.低矯頑磁性The magnetic properties result of the sample state that the ultimate 800 - treated mixed sample has the coercive of 4. 01oe and the core loss at w10 / 50 of 3. 28w / kg. the main reason may be there was large of oxide in the sample and the density was not high
樣品的磁性能的結果表明， 800混料樣品最終的矯頑力為4 . 01oe ，鐵損w10 50為3 . 28w kg 。所得到的最終樣品的磁性能較差，主要是因為樣品中存在較多的氧化物和樣品的緻密度不夠理想。The change of composing phases, the internal - stress and microstructure had insignificant effects on the magnetic properties for the s s fiber
纖維化過程引起材料內應力、微組織結構的改變，進而對纖維的磁導率、矯頑力、剩磁性能產生重要的影響。Methods of measurement of the coercivity of magnetic materials in an open magnetic circuit
在開磁路中測量磁性材料矯頑力的方法分享友人