  1. The investigation of a lot of parameters about treated sandstone, brick materials and earthen materials with fluorited polymers has been carried out, such as the formation of polymer, the penetration depth, porosity, capillary absorption and penetration coefficient, water uptake, compressive strength, drilling resistance, absorption isotherms of water vapor, water vapor diffusion, color changes as well as resistance to desegregation of water, frizzing - throwing cycles, worming - cooling cycles, and so on. in addition, the influence of salt crystallization, acid and base, and uv aging have also been assessed in order to better understand the protection effects and utilization possibility of two fluorinated polymers, mainly according to astm standard and the combination of international methods together with general technological

    分別以國家級文物保護單位的土質、砂巖和磚材文物樣品為對象，依據astm標準及國際通用文物保護研究方法與評估準則相結合，通過膠化物形成周期、滲透深度、孔隙度、毛細吸水和滲透系數、持水量、抗壓強度、抗鉆強度、吸附水蒸氣的能力、透氣性、外觀顏色等系列參數的測定，及凍融、冷熱循環、酸堿腐蝕后抗壓強度的衰減、可溶鹽對保護效果的影響、酸堿及光照對表面保護效果的影響，對兩種含氟聚合物及其與有機硅的共混物在文物加固保護和表面防護中的可行性和保護效果給予了系統研究。
  2. Based on testing results and soil theory, the modified mechanism of the nanometer silica fume in the clay is proposed : water molecule adsorption action, cementation action and filling action. combining the sem tests, the microstructure features of the cemented soil of nanometer silica fume are concluded

    設計了三組室內試驗，分別探討了納米硅粉對粘性土物理力學性能的影響；結合試驗結果和土質學基本理論，提出從水分子吸附作用、膠結作用、填充作用三個方面探討納米硅粉與粘性土之間的作用機理。
  3. The results of the uni - factor experiments and perpendicular experiments show their best mechanic synthesizing craft as followed : nvp ( 10 % wt ), kh570 ( 20 % wt ), hema ( 70 % wt ), initiator ( 0. 2 % wt ), crosslinker ( 20 % wt ), reacting 20 hours under 80 c. the factors which influenced organic silicon modified pvp hydrogel soft contact lens material ' s swelling capabilities were researched, which included temperature, monomer content, ion concentration etc. the experiments showed the equation swelling content ewc improved with the increase of nw, droped with the increase of kh570 and ion concentration, improved then droped with the raise of temperature, and hydrogels got the least ewc at 45 c. experiment carried on todiscuss water dehydration mechanism of organic silicon modified pvp hydrogel soft contact lens materials, which showed dehydration process could be divided into evaporating stage and diffusing stage

    正交實驗結果表明， nvp ? hema ? kh570共聚物的機械性能最佳時，其合成工藝條件為： nvp用量10 （質量百分含量，下同） ， kh570用量20 ， hema用量70 ，引發劑aibn用量0 . 2 ，交聯劑nmba用量0 . 2 ，反應溫度為80 ，反應時間16h 。討論了單體配比、溶脹溫度、離子濃度等因素對有機硅改性pvp水凝膠軟接觸透鏡材料溶脹性能的影響。實驗得出：水凝膠材料的平衡溶脹度ewc隨單體nvp含量的增加而增大， ewc隨kh570用量的增加而減小，隨離子濃度的增大而略微降低，隨溶脹溫度的升高先稍微下降後有所提高， 45時平衡含水量最低。
  4. Citric acid, taking the place of hno3, solutes the substance which does not solute in solution, and it acts as the ligand of metallic ionic and the hydrolysis catalyst of si ( oc2h5 ) 4, which reduces the pollution caused by no2 which forms at the decompose process of the hot treatment. by changing the means of calcine of the drier gel, choosing the suitable temperature to burn the gel, the high temperature calcine time is shorted, which solves the question of the long period calcine. so the preparation process of the matrix and composite was finished by using more lower temperature than the traditional solid state reaction and more shorter time than the traditional sol - gel process

    結果使基質和復合物的制備在比傳統的固相反應法低得多的溫度下和比常規的溶膠凝膠法短得多的時間里完成；五、對基質及復合物的干凝膠、粉體和燒結體進行了ir 、 dta 、 xrd 、 seni及交流阻抗譜表徵，研究結果表明：在溶膠向凝膠的轉化過程中同時存在著正硅酸乙酯自身的聚合作用和檸檬酸鹽絡合物之間的聚合作用：干凝膠向產物粉體的轉化在400600c之間進行；基質li 。
  5. For dagang oilfield, cements mainly is calcite, other and fills are mud, silicate, pyrite and organic matter, at least there are two or three stages. ( 4 ). after studying of cement stratagraphy, cementation - dissolution diagenesis is divided into four zones : phreatic, vadose, deep mixing and deep convection zones

    從大港探區的實例出發，認為充填物類型除方解石外，泥質充填也較普遍，同時還有硅質、黃鐵礦、有機質等多種充填類型，充填期次至少2一3期; （ 4 ）膠結物地層學研究，將膠結溶蝕成巖作用劃分出四個帶:滲流帶、潛流帶、深部混合帶和深部對流帶。