The quality of furan sand castings is usually better than clay sand castings, however, some defects are also very easy take place with furan sand castings such as blow hole, metal penetration, veining, cracking, slag inclusion, hardness too low, surface recarburation, surface sulphuration, nodularity degeneration etc, which were usually caused by improper raw materials selection, improper method design, incorrect moulding or / and core - making
摘要呋喃樹脂砂鑄件質量一般比黏土砂鑄件好,但如果原材料選擇、工藝設計、造型和制芯操作不當,也會產生氣孔、粘砂、脈紋、裂紋,夾渣、硬度不足、滲碳、滲硫和球化不良等鑄造缺陷。A way to avoiding crack or reducing crack width of concrete or reducing distortion of member is using prestressed concrete. the writer tried to make full use of the merit of the prestressed concrete and designed prestressed concrete mandril to control crack of structure. the prestressed concrete mandril, which was firstly applied high pressure on a small concrete bar, and then was made in concrete, so it would act as reinforced bar and resist load. in this thesis the writer designed 24 mmnbers and had experimental study of them, reached the conclusion that the effect of resisting crack of the prestressed concrete mandril was good when the load was not large, it can enhance the capacity of resisting crack and reduce the crack distance and crack width, but when the loads was large, the effect of resisting crack was not good, when we used the prestressed concrete mandril and reinforced bar together in member, the effect of resisting crack was very good. the writer analysed the adherence mechanism and wreck mechanism of the prestressed concrete mandril in anxial tension members, and according to the character of the prestressed concrete mandril, the writer constructed the bond model of it. then the writer introduced the analysis theory of crack including the bond - slip theory, the non - slip theory, the synthesis theory and mathematics stat method. the different theory had different theory base, they considered that the primary affection of crack width was different. in this test, the crack distance and crack width of members which placed reinforced bar were match to the compute value of the code gb 50010 - 2002 very well. to the members which
本文共進行了24根試件的試驗研究,得出了預應力混凝土芯棒能較大地提高構件抗裂承載力,在荷載小於預應力混凝土芯棒的開裂荷載時有較好的抗裂效果,能較大地減小裂縫間距和裂縫寬度,但是當荷載較大預應力混凝土芯棒開裂時預應力混凝土芯棒的抗裂效果不是很好,若將普通鋼筋和預應力混凝土芯棒一起使用時則有很好的抗裂效果。本文分析了預應力混凝土芯棒在軸拉試件中的粘結機理和破壞機理,根據預應力混凝土芯棒本身的特點,提出了預應力混凝土芯棒與后澆混凝土之間的粘結模型。然後本文詳細介紹了經典的裂縫分析理論粘結滑移理論、無滑移理論、綜合理論和數理統計方法,各理論有著各自不同的理論基礎,認為影響裂縫寬度的主要影響因素也各不相同。The casting workshops of using clay sand include the parts of moulding, core making, sand processing, cleaning
完整的粘土砂生產車間包括有造型、型芯、砂處理、熔化、清理等幾個工部。
分享友人