  1. The effects of gypsum on fluidity of cement mortar and setting time of cement paste are not significant when it used as retarder of cement. whereas, when 0. 3 % ca - lignosulphonate or ca - solassate added in cement used anhydrite gypsum as retarder, loss of fluidity of cement mortar is rapid, quick setting is occurred

    但是，在硬石膏調凝水泥中摻加0 . 3的木鈣和糖鈣緩凝減水劑卻能使水泥砂漿流動度經時損失加快，凈漿表現出促凝現象，發生外加劑與水泥的不相容問題。
  2. Abstract : based on composite testing of naphthalene superplasticizer and different retarders as well as retarding water reducer, in which the overall amount of admixture is certain, this paper analyzes the influence of these multicomponent admixtures on flowability of neat cement 、 retarding action and development of strength of colloidal mortar. the result shows that compatibilities of different components are different, and composition effects are also different

    文摘:在總摻量一定的情況下，就萘磺酸鹽高效減水劑與不同緩凝組分、緩凝型減水劑等復合后對水泥凈漿流動度、緩凝作用、膠砂強度發展等性能的影響作用進行了試驗分析，結果表明各不同組份復合的相容性不同，復合效應也存在差別。
  3. Based on above, the characteristics of hydration hardening process and microstructure of hsc as well as the interfacial layer between cement paste and coarse aggregate are investigated under low water cement ratio, high content superplasticiser and with one kind or more than one kind of mineral materials condition, the reaction mechanisms of different mineral materials are also discussed

    研究了不同水膠比、復合緩凝成分高效減水劑及礦物摻合料的摻加方式、摻量對高強混凝土水泥漿體水化放熱過程和水泥漿體的水化熱、水化放熱速率以及最高溫升的影響規律。探明了高強混凝土中水泥漿體的水化硬化過程、礦物摻合料之間的相互作用機理。
  4. The result of macro - quality experiments show : mineral admixtures markedly slow the hydrating velocity of cement slurry, decrease and delay the hydrating max - temperature, in which steel slag is more effective ; expansive agents compensate concrete shrinkage, enhance the concrete dense degree, strengthen the interfacial layer between fiber and cement matrix and improve the physical mechanics qualities of acic ; minimal admixtures markedly improve the concrete workability property, increase the concrete later intensity & density and the capability of anti - chemical attack and anti - permeability ; hybrid fiber reinforces the toughness of obviously acic by the means of anti - cracking effect of fiber with different sizes and different properties in the corresponding construction levels

    實驗結果顯示：鋼渣摻合料能顯著減緩水泥漿體水化速率，降低砂漿的水化溫升並延遲最高溫升時間；補償混凝土收縮，提高混凝土密實度，加強纖維與水泥石的界面粘結，增強混凝土力學性能，但不能明顯改善混凝土韌性。混雜纖維通過纖維的不同尺度與不同性質在相應的結構層次上產生阻裂效應，增韌鋼渣防滲抗裂混凝土；增加混凝土的破壞極限能，極大提高混凝土抗彎曲能力和韌性指數，改善混凝土脆性。
  5. The effects of five common set - retarders on setting time of cement paste and concrete and strength of concrete are studied. to cement paste, amount of set - retarders added in cement has a critical value

    論文分別研究了木鈣、糖鈣、酒石酸、焦磷酸鈉和蔗糖共五種常用緩凝劑對水泥凈漿凝結時間、混凝土凝結時間及強度的影響。