The dispersity and stability of the graphite aqueous suspensions was investigated with centrifugation, the violet visible spectrophotometer, the laser particle size analyzer and scanning electron microscopy ( sem ). the following aspects of the production technique were carefully studied : 1. the effects of surfactants, poly ( vinyl alcohol ) ( pva ), poly ( vinyl pyrrolidone ) ( pvp ), sodium alginate ( sa - na ) and poly ( sodium acrylate ) ( pa - na ) on the suspension stability of graphite were investigated
本研究的主要內容有以下三個方面: 1 、研究了陰離子表面活性劑、非離子表面活性劑、聚乙烯醇( pva ) 、聚乙烯基吡咯烷酮( pvp ) 、海藻酸鈉( sa - na ) 、聚丙烯酸鈉( pa - na )對石墨在水中分散性和穩定性的影響; 2 、研究了分散方法、分散介質、 ph值及羧甲基纖維素鈉( cmc )含量對石墨在水中分散性和穩定性的影響; 3 、研究了聚乙烯醇( pva ) 、聚乙烯基吡咯烷酮( pvp ) 、海藻酸鈉( sa - na ) 、聚丙烯酸鈉( pa - na )四種助分散劑與羧甲基纖維素鈉( cmc )復配對石墨在水中分散性和穩定性的影響。The studies expressed that the tensile - strength declined with the growth of dose rate after the radiation treatment, and at the same time, the gel content had extreme value with the change of the dose rate. the surface of uhmwpe fibers showed some irregular micro - pits and dents after radiation treatment, narnely rough degree increasing. their number and deepness increased with increase of dose. and this phenomenon is the most obvious when the dose rate was 8. 5kgy / s and the dose was 400kgy. at the same time some containing oxygen groups, including hydroxyl group, carbonyl group and carboxyl group, were introduced into the fiber surface which was exposed to the air
研究表明, uhmwpe纖維經電子束輻照處理后,纖維的拉伸斷裂強度隨劑量率的增加呈下降趨勢,凝膠含量隨著劑量率的變化存在極值。纖維表面出現了不規則的微裂紋和凹痕,隨著劑量的增大,電子束對纖維表面的刻蝕程度增加,在本研究中以劑量為400kgy劑量率為8 . 5kgy s時刻蝕效應最為明顯。同時,在空氣中進行輻照時,纖維表面被引入了一些含氧基團,包括羥基、羰基和羧基。
分享友人