致斷韌度 的英文怎麼說

中文拼音 [zhìduànrèndù]
致斷韌度 英文
breaking toughness
  • 致 : Ⅰ動詞1 （給與;向對方表示禮節、情意等） deliver; send; extend 2 （集中於某個方面） devote （one s ...
  • 斷 : Ⅰ動詞1 （分成段） break; snap 2 （斷絕;隔斷） break off; cut off; stop 3 （戒除） give up; abstai...
  • 韌 : 形容詞（不易折斷; 柔軟而結實） pliable but strong; tenacious; tough
  • 度 : 度動詞[書面語] （推測; 估計） surmise; estimate
  • 韌度 : tenacity; viscosity韌度指數 toughness index
  1. Research about ctod and its components 8 ", " shows that the direction angle of ctod vector is identical with the fracture angle of void - mode fracture, which is obtained through experiments, and it is also identical with the result got by peak value line of stress triaxiality. besides, 8 i " was compare with vgc as criterion for initiation of void - mode fracture

    對裂紋尖端張開位移ctod及其張開型分量~ 1和剪切型分量~ 11的分析表明，在試件發生韌窩型斷裂時，按照圓弧裂紋中ctod矢量的垂直方向預測的斷裂角與試驗測得的斷裂角符合較好，與三軸度脊線預計的結果也比較一致。
  2. The results shows that the failure parts has high silicon content and uneven hardness, the impact toughness and elongation is far below the specification of the material

    結果發現，失效件的硅含量偏高、硬度值很不均勻，沖擊韌度和伸長率遠低於材質要求，因而導致脆斷。
  3. The results showed that the fracture of the tooth - razor was brittle fracture, the material quality was normal, the main fracture reson was that the carbide in the microstructure of the tooth - razor was distributed as reticulation, the brittleness of the razor was increased and the toughness was decreased, so the tooth of the razor was broken by external force when it was working

    結果表明，該剃齒刀的斷齒屬于脆性斷裂，主要是顯微組織中的碳化物分佈不均勻（呈網狀分佈） ，使刀具的脆性增大而強度、韌性下降，導致刀具在使用過程中由於外力的作用發生斷齒。
  4. Plastic strain first starts from ambient of the porphyroblast, and then develops to rims of porphyroblast and gradually transfers to the centers of porphyroblasts. the brittle remains in the central parts of porphyroblasts come to be decreased through the plastic deformation development, which is accordance with the banding of intensity in many mylonitization zones on wild occurrences and observation in the fabrics of mylonitization rocks under microscope

    長石眼球構造的形成主要是由長石與石英的韌性差決定的，塑性變形首先從斑晶的周圍部分開始，逐漸向斑晶發展，脆性殘斑核不斷減小，這與剪切帶內糜棱巖化強度分帶相一致。