超導薄膜結 的英文怎麼說

中文拼音 [chāodǎobómójiē]
超導薄膜結 英文
superconducting thin-film junction
  • 超 : Ⅰ動詞1 （越過; 高出） exceed; surpass; overtake 2 （在某個范圍以外; 不受限制） transcend; go beyo...
  • 導 : 動詞1. （引導） lead; guide 2. （傳導） transmit; conduct 3. （開導） instruct; teach; give guidance to
  • 薄 : 名詞[方言] （浮萍） duckweed
  • 膜 : 名詞1. [生物學] （像薄皮的組織） membrane 2. （像膜的薄皮） film; thin coating
  • 結 : 結動詞（長出果實或種子） bear （fruit）; form （seed）
  • 薄膜 : thin film; film; diaphragm
  1. The properties of thin films have been investigated with modern analysis technique, such as afm ( atom force microscopy ), sem ( scanning electron microscope ), xrd ( x - ray diffraction ) and rocking curve ( - scan ). and the properties of ybco thin film and its substrate and deposition temperature have been analysed, comparing with lao substrate ' s crystallization quality, ybco thin film properties, such as morphology and degree of grain alignment, was concluded to correlate with the crystal orientation uniform of lao substrate as revealed by xrd

    本文結合afm 、 sem研究ybco薄膜的表面形貌， xrd 、 fwhm分析薄膜的結晶情況，並結合成膜溫度和基片的質量進行一系列結構與性能的對比研究，發現laalo3 （ lao ）基片的質量對ybco薄膜的結構完整性有很大影響，不僅影響了薄膜的c軸取向性，而且影響了ybco的超導性能。
  2. The purpose of this dissertation is to study the effect of substrate on the characteristics and microstructure of high temperature superconducting yba2cu3o7 - thin film, and well c - axis oriented epitaxial ybco thin films have been deposited on both laalo3 ( 100 ) and r - plane sapphire al2o3 ( 102 ) substrates by inverted cylindrical dc sputtering ( icds ) technique

    =本論文的目的是研究基片對薄膜結構和性能的影響關系，採用倒筒靶直流濺射技術在在laalo3 （ 100 ）和r -平面的藍寶石（ al2o3 （ 102 ） ）兩種基片上制備出c軸取向的外延高溫超導yba2cu3o7 -薄膜。
  3. The microwave delaylines using hts thin films have the advantages of small size and mass and low insertion lose. these characters are much better than the delaylines using surface acoustic wave, coaxial - line, magetostatic wave or conventional metal planar structures. these merits benefit a lot in largely reduction the mass and volume of communication systems

    利用高溫超導（ htsc ）薄膜材料研製的微波延遲線具有體積小、重量輕、插損小等優點，這是利用聲表面波、同軸線、靜磁波或常規金屬平面結構設計的延遲線所無法比擬的。這些優點對于減輕通信系統的重量和縮小體積都是非常有利的。
  4. There are better performances in the films prepared by ba2ca2cu3ox target than by ba2cacu2ox target. the single - phase tl2ba2cacu2o8 hts thin film was obtained with a tc0 of 107k at the optimal tl2o partial pressure and thallination temperature 750. on excursion from the optimal conditions, there exist some impurities in the resultant films resulting in a reduction in tc0 and surface quality with change in the microstructure morphology

    研究結果表明，採用成分為ba2ca2cu3ox的靶材制備的薄膜性能要優于成分為ba2cacu2ox的靶材；使用組成式為tl1 . 9ba2ca2cu3oy的鉈片做鉈源時，形成的tl2o分壓達到最佳值；在最佳tl2o分壓和最佳鉈化溫度750的條件下，制備出了純相完全c軸取向的tl2ba2cacu2o8高溫超導薄膜，其tc0高達107k ，膜面均勻平整光滑，呈圓片狀組織；偏離最佳制備工藝參數的條件下，制得的薄膜中都含有一定量的雜相，雜相的生成使得tc0值下降，薄膜表面質量下降，薄膜組織形貌發生變化。
  5. Abstract : based on the ahievement of epitaxial growth in several perovskite oxide films, we discuss the importance of substrate temperature ( ts ) and substrate material in the epitaxial growth of perovskite oxide thin films. influences of ts on growth orientation and epitaxial threshold temperature were observed. the results indicate that during the growth of the oxide films the phase formation and growth dynamics should be taken into consideration. the threshold temperature for epitaxial growth depends on the substrate materials. this demonstrates the influence of substrate material on the initial nucleation and epitaxial growth

    文摘:在成功地外延生長超導、鐵電、鐵磁等多種性質的鈣鈦礦結構氧化物薄膜的基礎上，討論影響氧化物薄膜外延生長的一些因素.考慮到相形成和薄膜生長動力學，在利用脈沖激光淀積法外延生長氧化物薄膜中襯底溫度是十分重要的工藝參數.襯底溫度對成相和生長薄膜的取向都有影響.考慮到薄膜是首先在襯底表面成核、成相併生長.因此襯底材料晶格的影響是不容忽視的.觀察到襯底材料對薄膜外延生長溫度的影響.在適當的工藝條件下，利用低溫三步法工藝制備得到有很強織構的外延薄膜.這突出表明界面層的相互作用對鈣鈦礦結構薄膜的取向有著相當大的影響
  6. It indicats that the growth temperature, annealing temperature and time greatly affects the quality of mgb

    超導薄膜表面形貌晶體結構超導電性的影響。
  7. At present, superconductor filter subsystems have been deployed abroad in the field of mobile communication and offered exceptional commercial performance. the design of hts filters is a comprehensive problem of network analysis. according to the condition of calculation and practical size of superconducting films, we configured compacted forward - coupled microstrip filter, with the aid of tumic and sonnet software

    高溫超導濾波器的設計是一個網路綜合的問題，根據我們目前的設計條件和超導薄膜的尺寸因素，我們選用了結構緊湊的前向耦合型電路設計，應用tumic和sonnet模擬軟體，設計了用於移動通訊頻段的高溫超導濾波器，並對幾個重要參數進行了實驗測試和分析。
  8. The results indicates that superconducting mgb2 thin films can be prepared by hfcvd in a single - step with the maximum critical transition temperature tc of 36k ; the best critical transition temperature tc of thin films grown by hpcvd in a single - step is 34k. the optimal zero resistance temperature tco of thin films fabricated ex situ is 37 k by post - annealing of precursor b film at 800 for 1 h under high mg vapor pressure

    實驗結果表明，用hfcvd法在400原位制備了臨界溫度為36k的mgb2超導薄膜；用hpcvd法在700原位制備了臨界溫度為34k的mgb2超導薄膜；將300制備的前驅物b膜在mg蒸氣中800保溫1h非原位退火，制備了臨界溫度為37k的mgb2超導薄膜。