  1. Using diethanolamine as aminating agent and glacial acetic acid as neutralizing agent, aminated epoxy acrylic cationic resin was prepared. the effect of technology of aminated epoxy acrylic resin on properties of eletrodeposition was studied by conductivity meter and electrophoresis apparatus. it was shown that, conductivity firstly decreased, and then increased with aminating temperature increase. in contrast with putting polyacrylic resin into thin acetic acid solution, the more compact film could be achieved by neutralizing polyacylic resin with glacial acetic acid and then add it into water. when neutralizing temperature was enhanced, the speed of electrodepsidon was found to increase, and the film was also more compact. increasing the dn leads to enhanced conductivity and smaller particle size. when dn equaled to 80, the smoothest film could be achieved

    以二乙醇胺為胺化劑、冰醋酸為中和劑，合成了胺化環氧丙烯酸陽離子樹脂.採用電泳儀和電導率儀，研究了胺化環氧丙烯酸樹脂合成工藝對陰極電泳塗料電沉積性的影響.結果表明，隨著胺化溫度的增加，電泳液電導率先下降後上升.將冰醋酸加入樹脂中中和，後用水稀釋，比樹脂在醋酸稀溶液中中和，電沉積性能更好.電沉積速率隨著中和溫度的上升而增加，電沉積膜緻密性相應增加.中和度（ dn ）愈高，電泳液電導率愈大，粒徑越小，而塗膜外觀在中和度為80時達到最佳
  2. The hydrothermal activities which were complicated and acted a positive effect in the formation of the zhulazaga gold deposit resulted in hydrothermal alterations of multiepisode, including pyroxeneization, actinolitization, epidotization, ice - feldsparization, silicification, chloritization and carbonatization etc. the research on inclusions in quartz of the ore indicates that the hydrothermal fluid varying greatly in temperature with an average of 286 shows characteristics of high temperature

    3 、朱拉扎嘎金礦的形成中熱液活動起到了積極的作用，熱液活動不僅復雜而且具多期性，有透輝石化、陽起石化、綠簾石化、綠泥石化、硅化、冰長石化、碳酸鹽化等。礦石中石英包裹體的研究表明，含礦熱液的溫度變化范圍較寬廣，平均在286 ，顯示中偏高溫特徵。
  3. In the third chapter, the influence of current density, solution concentration, erosion time and aging in ambient air on the pl spectra of ps suggests that peak would blue shift with current density increasing, and with erosion time and aging time prolonging ; with the increasing of solution concentration, peaks would red shift when solution concentration less than 1 : 1 but blue shift when solution concentration greater than 1 : 1. above phenomena can be explained by quantum confinement and light center model, but do not deny the action of si - h bonding and defect on the surface in the process of photoluminescence. at present, radiation mechanism is still one of the primary problems in the study of ps

    在第z三章中；通過對比，分析了電流密度、陽極化時間、溶液濃度以及自i然氧化時間對多孔硅光致發光光譜的影響，認為在一定的范圍內，多i孔硅的發光峰位會隨電流密度的增大而藍移，要獲得較強的發光，需z要選擇合適的電流密度；隨著腐蝕時間的延長，多孔硅的發光峰位會i發生藍移；當f酸的濃度較小q ： 1 ）時，峰位隨濃度的增大表現為向i低能移動；而當f酸的濃度較大河山時，峰位隨濃度的增大則表現z為移向高能；多孔硅在空氣中自然氧化；其發光峰位發生藍移，而強i度隨放置時間的延長而降低。
  4. It is proved that the new technology is feasible, but 4 important problems must be solved by test, viz, behavior of iron ion in anode ; influence of iron in electrolyte on current efficiency, cathode quality, and the allowable concentration of iron ion ; the optimal concentration of sulphuric acid in electrolyte ; the optimal method of removing iron ion in electrolyte

    但是要進行工業生產，必須經過試驗研究，解決好4個問題，即陽極中鐵的行為；電解液中的鐵離子對電流效率的影響和陰極析出質量的影響，鐵離子的最高允許濃度是多少；電解液中硫酸的最佳濃度是多少；電解廢液中的鐵離子採用什麼方法進行凈化最經濟。
  5. The main results and conclusions acquired from the dissertation are as follows : ( 1 ) aam templates with nano - pore arrays were fabricated in different anodic oxidative conditions by anodic oxidation of aluminum foils, so the pores in aam templates might have different diameters, different densities, different depths and different aspect ratios

    主要研究程果和結論如下： （ 1 ）在硫酸、草酸和磷酸電解液中，在不同的陽極氧化條件下制備出具有不同大小、密度、深度和縱橫比的納米孔陣列aam模板。
  6. Aao films were anodic oxidized using oxalic acid under different voltage from 30v to 60v. under 40v, the diameter range of aao is 80nm ~ 100nm and narrowly distributed. the thickness of aao film is about 2. 0 # m and the aspect ratio is beyond 15

    在不同電壓下（ 30v 60v ） ，採用草酸溶液體系用陽極氧化法制備了多孔氧化鋁模板，氧化鋁模板的孔徑在80nm 100nm之間，分佈均勻，模板厚度在1 . 5 2 . 0 m之間，長徑比在15以上。