The tea waste powder with different sizes as an additive was used to urea - formaldehyde ( uf ) resin, and the effects of the tea waste powder sizes and amount on the free formaldehyde content of uf resin, the formaldehyde emission, and hood strength of uf resin hooded plywood were studied in this paper
摘要將不同顆粒度的茶葉廢料粉添加到脲醛樹脂膠中,研究了茶葉廢料的顆粒度、加入量等對脲醛樹脂膠黏劑的游離甲醛含量、黏接膠合板的甲醛釋放量及膠合強度的影響。The experimental results indicated that the tea waste powder as an additive to uf resin could reduce its free formaldehyde content and reduce the formaldehyde emission of uf resin bonded plywood ; the tea waste powder with much less size was easily mixed with uf resin and acted much more effective ; the tea waste as an additive to uf resin in a proper amount did nut decrease the bond strength of plywood
實驗結果表明,茶葉廢料作為填料添加到脲醛樹脂膠黏劑中,能夠降低其游離甲醛含量以及其黏接膠合板的甲醛釋放量;茶葉廢料顆粒度越小,與脲醛樹脂混合性越好,消除甲醛效果越顯著;茶葉廢料的適量加入不會降低膠合板膠合強度。The results indicate that the sort of walling material is the most important factor in bond capacity of mortar, the mixed quantity of polymer and mortar strength follows, and there is a remarkable increase in mortar bond strength when the mixed quantity of pvb and mc is 20 % ~ 30 % and 0. 05 % ~ 0. 1 % respectively
結果表明:塊體類別是最主要的影響因素,其次是聚合物摻量和砂漿強度;當聚乙烯醇縮丁醛和甲基纖維素的摻量分別為水泥質量的20 % ~ 30 %和0 . 05 % ~ 0 . 1 %時,可較大幅度提高砂漿的黏結強度。Aircraft industry. synthetic cloths for the fabric of airplane structures. peeling strength of the bonding of taping fabric
航空工業.飛機結構用合成纖維布.經紗上漿織物黏結的剝離強度Cover layer and stiffener have similar properties, both possess high flexibility, good weather - ability, flame retardation, anti - ion - migration and heat resistance