  1. Antiwear additive for jet fuels t1602

    T1602噴氣燃料抗磨添加劑
  2. Abstract : sulfurized oxymolybdenum dialkyldithiophosphate ( moddp ) is a lubricating oil additive which has good antiwear and friction reducing properites

    文摘:二硫代磷酸硫化氧鉬是一種具有優良抗磨減摩性能及節能效果的潤滑油添加劑。
  3. Antiwear ( aw ) agent additive that is active in preventing damage caused by occurrence of solid phase welding between sling surfaces without local surface melting

    抗磨（ aw ）添加劑相互滑動的表面因發生相互摩擦會造成損壞。抗磨添加劑就是能有效防止這類磨損，同時又不會發生滑動的表面熔化的添加劑
  4. With the reference of many relevant materials, the author prepared a fined molybdenum disulfide powder with a average size of 800nm by ball milling, and a nano - copper with average size of 30nm in micromulsion solution method, and synthesized surface - modified titanium dioxide nanoparticles with average size of 40nm in organic media via sol - gel method. the tribological performances of three particles were studied by universal test as well, with the result of fined molybdenum disulfide powder with good reducing wear and antiwear performance at low load, nano - copper with good reducing wear and antiwear performance at high load, surface - modified titanium dioxide nanoparticles maintaining stable reducing wear and antiwear performance from low load to high load due to its characteristics of organic and inorganic nanocomposite. the results indicate that the nanocomposite is the most perspective oil additive. the reducing wear and antiwear mechanism of nano oil additive was studied with in - situ tribochemical principle. nano additives possess broadly developing prospect with its above - mentioned performance

    在參閱了大量文獻的基礎上，分別採用了球磨法、微乳液法、溶膠?凝膠法制備了超細二硫化鉬、納米銅粒子、表面修飾納米二氧化鈦，經原子力顯微鏡測試，獲得的超細二硫化鉬的粒度平均在800nm以內，納米銅粒子平均粒度約為30nm ，表面修飾納米二氧化鈦平均粒度約為40nm ，在萬能摩擦磨損試驗機上測試了三種粒子的摩擦學特性，結果表明：在合理的添加濃度范圍內，超細二硫化鉬在低載時具有優良的減摩抗磨性能，納米銅在高載時具有比較好的減摩抗磨性能，表面修飾二氧化鈦粒子因具有有機與無機復合物的特性，從低載到高載都保持穩定的減摩抗磨性能。
  5. An oil agent has a low load bearing capacity, extreme pressure andantiwear additives often contain the element of sulph, phosphorus, chlorine, which pollute surrouding enviorement, which have been restricted to use overseas. deweloping lubricating oil additive with good antiwear, high load - bearing capacity and self - repair of wear surface is one of the important questions in tribology

    油性劑的承載能力低，極壓抗磨劑多為含硫、磷、氯的有機物，污染環境，在國外已被限制使用。發展具有良好抗磨性能、高承載能力、對磨損表面具有一定修復功能的潤滑油添加劑是摩擦學領域的前沿課題之一。
  6. Antiwear ( aw ) agent additive that is active in preventing damage caused by occurrence of solid phase welding between sliding surfaces without local surface melting

    抗磨（ aw ）添加劑相互滑動的表面因發生相互摩擦會造成損壞。抗磨添加劑就是能有效防止這類磨損，同時又不會令發生滑動的表面熔化的添加劑。