  1. The results of tem showed that the layers of omt had been separated partly into alone fragment by in - situ polymerization of pu ; the agglomerative nano - sio2 particles in pu composite had been dispersed, but the disperse status became worse as the increase of its content

    Tem結果顯示，通過pu的原位聚合，復合材料中omt的片層被部分分離成單獨的片層;納米510 :粒子被分散，但在復合材料中的分散狀況隨著其含量的增大而變差。
  2. In this thesis study, graphite nanosheets were effectively prepared from natural graphite flake. fabrication of graphite nanosheets with nylon 6 via an in - situ polymerization approach led to the nylon 6 / foliated graphite nanocomposites

    通過原位聚合復合技術，將石墨納米薄片分散於尼龍6基體中，構造了尼龍6納米石墨納米導電復合材料。
  3. This thesis was composed in three parts : ( 1 ) the performance of the catalysts for the oligomerization and polymerization of ethylene ; ( 2 ) the comonomer effect of the in - situ copolymerization of ethylene by the bis ( imino ) - pyridyl iron complexes and metallocenes ; ( 3 ) the in - situ copolymerization of ethylene by cobalt - based catalysts and metallocenes

    本論文共分為3部分：催化劑性能的評價，雙亞胺基吡啶鐵配合物與茂金屬復配催化乙烯原位共聚中的共單體效應以及雙亞胺基吡啶鈷配合物與茂金屬復配催化乙烯原位共聚。
  4. Two kinds of n - substituted pyrrole ( trimethyl - ( 2 - pyrrol - l - yl - ethyl ) - ammonium iodide and 2 - ( 2 - pyrrol - 1 - yl - ethoxy ) - ethane - sulfonate sodium ) were synt hesized ; poly ( trimethyl - ( 2 - pyrrol - l - yl - ethyl ) - ammonium iodide ) / v2os nanocomposites were synthesized by two methods ( monomer in - situ intercalate polymerization and polymer intercalation in solvent ). to fabricate vaos sol by melt quenching, oxygen top - blend technique was applied to improve oxygenic part - pressure, decrease the oxygenic anoxic and restrain the increase of v4 + ion when vos was melted. the xos xerogel prepared by the new technique had more complete structure than the vos xerogel which v20s powder was melted in the air

    針對以v _ 2o _ 5為原料、熔融淬冷法合成v _ 2o _ 5溶膠、制備v _ 2o _ 5干凝膠薄膜這一方法，提出了在v _ 2o _ 5熔融時運用氧氣頂吹工藝這一思路，目的是增加熔體表面的氧分壓，減少熔體的氧缺損，使v _ 2o _ 5干凝膠的v ~ （ 5 + ）離子含量更高、其結構更完整、性能更穩定。
  5. Preparation of rotenone microcapsules by in - situ polymerization

    原位聚合法制備魚藤酮微膠囊
  6. The work was composed in five parts : ( 1 ) epoxy resin / org - mmt / diethylenetriamine ( deta ), epoxy resin / org - mmt / imidazole ( mz ) and epoxy resin / org - mmt / tung oil anhydride ( toa ) nanocomposites were prepared by in situ intercalation polymerization

    所研究的內容及其結論主要包括以下五個部分： （ 1 ） xrd測試表明環氧樹脂進入了有機蒙脫土片層內，使蒙脫土層間距增大。
  7. In this paper, two kinds of polyazomethine / nylon - 6 ( pam / pa - 6 ) composites with different chemical structures were prepared by means of in - situ polymerization. pam1 and pam2 were prepared from the reaction of terephthalaldehyde with l, 6 - hexanediamine ( paml ), and terephthalaldehyde with 4, 4 ' - diamiediphenyl ( pam2 ). during the preparation, pam chain ends played a retard role in the polymerization of s - caprolactam obviously

    本文通過原位聚合法制備了兩種不同化學結構的聚甲亞胺尼龍6 （ pam pa6 ）分子復合材料， pam1為對苯二甲醛與1 ， 6 -己二胺反應制備的聚甲亞胺， pam2為對苯二甲醛與4 ， 4 』 -二氨基二苯醚合成的聚甲亞胺。
  8. The new methods of toughening epoxy resins, including those of doing thermoplastic resin, thermotropoic liquid crystalline polymer, core - shell latex polymer, forming interpenetrating networks polymer, in - situ polymerization, are introduced, with their mechanisms discussed herein as well

    介紹了環氧樹脂增韌改性的一些新方法，包括熱塑性樹脂增韌、互穿網路增韌、熱致性液晶增韌、原位聚合增韌、核殼結構聚合物增韌等，並對其中的增韌機理作了總結分析。
  9. In this paper, three different kinds of polyazomethines ( pam ) / nylon 6 in situ polymerization composites were prepared using the process of monomer casting. their structures, thermal properties and also mechanical properties were analyzed

    本文利用三種聚甲亞胺的單體與尼龍6單體通過原位聚合反應，制備了三種聚甲亞胺/尼龍6原位聚合復合材料，制備工藝採用澆鑄法。
  10. In the paper, we use coupler kh570 to modify nanoparticles, bond coupler onto nanoparticles, and obtain alkylated nanoparticles ; then with the help of coupler on the surface of alkylated nanoparticles, we graft pmma onto nanoparticles through in - situ polymerization of mma monomer, and gain composited nanoparticles encapsulated by polymer, thereby nanoparticles are encapsulation modified

    本論文採用偶聯劑kh570對納米粒子進行改性，使之鍵接于納米粒子表面后，獲得烷基化納米粒子；然後在烷基化納米粒子表面通過單體mma的原位聚合，接枝聚合物pmma ，實現聚合物包覆納米粒子獲得復合納米粒子，以達到納米粒子的聚合物包覆改性。
  11. The nanocomposites were prepared by monomer in - situ polymerization or polymer solution intercalation. the structures of nanocomposites were analyzed. the polymer intercalated in the layer

    在單體插層聚合中， n一乙基毗咯三甲基鐐不僅在層內聚合，還可在層外聚合， vzos層間擴大至13
  12. Thermosetting resin / org - mmt nanocomposite, including exopy resin / org - mmt and phenolic resin / org - mmt, were prepared by in situ intercalation polymerization, and the intercalation and exfloliation behaviour of them were characterized by x - ray diffraction ( xrd ), dynamic mechanical thermal analysis ( dmta ), and different scanning calorimetry ( dsc )

    採用原位插層聚合法通過澆模固化成型制備了熱固性樹脂蒙脫土納米復合材料，並用xrd ， dmta ， dsc等手段研究了熱固性樹脂與有機蒙脫土的插層與剝離行為，並對固化過程進行了理論預估。
  13. The composite films can be prepared by in - situ polymerization processes, spin - cast from doped polyaniline / polymer solution, or by casting from polyaniline / polymer solution or dispersion

    原位聚合法、摻雜聚苯胺旋轉塗膜法和機械共混澆鑄法均可制備透明導電復合膜。
  14. Using paracetamol as template molecule, molecularly imprinted polymer membranes with supporting membrane were synthesized through in situ polymerization by uv irradiation

    採用紫外光引發原位聚合的方法制備了具有支撐膜的撲熱息痛分子印跡聚合物膜。
  15. On the initiating systems for in situ graft polymerization of - caprolactone - grafted on the pva film

    膜上原位開環接枝聚合引發體系的研究
  16. Polydispersed a - fe nanoparticles have been obtained by using bi - amine terminated polyurethane flexible macromolecule as a surfactant, and on the basis of them, the epoxy - iron nanocomposite particles have been synthesized by in situ polymerization compositing technology. the real parts of both the permittivity and the permeability of the nanocomposite decrease firstly and then increse with increasing dose of surfactant. the composite particles have ideal comprehensive properties at the dosage of the sufactactant of 0. 5 g, and its frequency dispersion exceeds that of traditional micrometer carbonyl iron powders

    以雙端氨基柔性大分子為表面活性劑制備了多分散的- fe粒子，並在此基礎上以原位聚合復合法制備了環氧樹脂-鐵納米復合粒子，發現隨表面活性劑用量增加，復合粒子介電常數實部和磁導率先降低后增加，在表面活性劑用量為0 . 5g時復合粒子有較好的綜合性能，頻散特性優于傳統微米羰基鐵吸收劑。
  17. In this dissertation, two kinds of polyazomethines ( pam ) / nylon 6 in situ polymerization composites with different rigidity of pam are synthesized through anionic polymerization. the crystalline forms and melting behavior are characterized by waxd, ft - ir and dsc. the results show that a is still the main crystalline form of composites

    通過waxd 、 ft - ir及dsc ，對復合材料的晶態結構及熔融行為進行了初步表徵，結果表明復合材料的主體仍為晶型， pam的加入並沒有改變基體的基本晶型。
  18. In this paper, the kaolinite / polyacrylamide intercalation compound was prepared first by the displacement reaction of kaolinite / formamide intercalation precursor with acrylamide, and then the in - situ polymerization of acrylamide. the kaolinite structure and the intercalation mechanism were discussed by the techniques of powder x - ray diffraction analysis, * h mas nmr, raman, and ir spectra

    本文以甲酰胺為前驅劑、丙烯酰胺為取代劑，採用插層-取代-原位聚合的方法制備高嶺石有機插層復合物，用x射線衍射、 ~ 1hmasnmr 、 raman 、 ir等技術研究了插層復合物結構特徵和插層反應機理。
  19. In addition, in the condition of high content of ommt, poly ( methyl methacrylate ) / organophilic montmorillonite ( ommt / pmma ) prepared by in - situ polymerization was orderlessly intercalated nano - masterbatch, the space of the layers reached 3. 65nm. pp / mmt nanocomposites

    另外，還在ommt高含量（ 60wt ）條件下，通過單體插層原位聚合法制得了ommt pmma無序插層型納米母料，蒙脫土的層間距達到了3 . 65nm 。
  20. Conductive polymer composite film of polyaniline / poly ( vinyl alcohol ) ( pan / pva ) was synthesized with an in - situ polymerization. the conductivity of the composite film was determinated to be 4. 36 s - cm ' 1. thermal stabilities of this composite film and pure pan were investigated by baking polymers in air atmosphere at 200 * c

    通過現場聚合制備出聚苯胺與聚乙烯醇的復合膜，產物電導率達4 . 36s ? cm ~ （ - 1 ） ，掃描電鏡研究結果表明，隨聚合時間和靜置時間的延長，膜表面的聚苯胺層緻密、均勻。